牌号简介 About |
---|
DOWLEX™ 2388聚乙烯树脂是一种乙烯/辛烯-1共聚物,由陶氏化学公司专有溶液法生产。具有独特的分子结构,侧链分布可控,具有优异的抗应力开裂性能和优异的长期静液强度。应用:热水和冷水系统用管道,例如:热水/冷水配水散热器连接加热/冷却应用单层和多层管道工业应用。主要特点:适用于高温下无交联、气味突出、性能优良的加工性。加工建议:DOWLEX™ 2388聚乙烯树脂在传统的聚乙烯加工设备上易于加工。加工的典型挤压温度范围为190至230°C。有关更多信息,请参阅我们的挤压指南。符合:欧盟第10/2011号美国食品药品监督管理局21 CFR 177.1520有关完整详细信息,请参考法规。 DOWLEX 2388 Polyethylene Resin is an ethylene/octene-1 copolymer produced in the proprietary solution process of The Dow Chemical Company. It has a unique molecular structure with a controlled side chain distribution, which provides excellent stress crack resistance properties combined with outstanding Long Term Hydrostatic Strength. Applications: Pipes for hot and cold water systems, e.g.: Hot / cold drinking water distribution Radiator connections Heating / cooling applications Mono- and multi-layer pipe Industrial applications. Main Characteristics: Suitable for elevated temperatures without crosslinking Outstanding taste and odor performance Excellent processability. Processing Recommendations: DOWLEX 2388 Polyethylene Resin is easy to process on traditional PE processing equipment. Typical extrusion temperatures for processing range from 190 to 230 °C. For further information see our Extrusion Guideline. Complies with: EU, No 10/2011 U.S. FDA 21 CFR 177.1520 Consult the regulations for complete details. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.941 | g/cm³ | ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
ISO 1133 | ||
190℃,2.16kg 190℃,2.16kg |
0.55 | g/10min | ISO 1133 |
190℃,5.0kg 190℃,5.0kg |
1.9 | g/10min | ISO 1133 |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
23 | kJ/m² | ISO 180 |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
维卡软化温度 Vicat Softening Temp |
125 | ℃ | ISO 306 |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD:20~70℃ MD:20~70℃ |
1/℃ | DIN 53752 | |
导热系数 Thermal conductivity coefficient |
|||
60℃ 60℃ |
W/m/K | DIN 52612 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 D,2.00 mm,模压成型 Shaw D, 2.00 mm, molded |
ISO 868 | ||
拉伸模量 Tensile modulus |
|||
2 mm,模压成型 2 mm, molded into shape |
MPa | ISO 527-2 | |
拉伸强度 tensile strength |
ISO 527-2/50 | ||
屈服,2 mm,模压成型 Yield, 2 mm, molded |
MPa | ISO 527-2/50 | |
断裂,2 mm,模压成型 Fracture, 2 mm, molded |
MPa | ISO 527-2/50 | |
拉伸应变 Tensile strain |
ISO 527-2/50 | ||
屈服,2 mm,模压成型 Yield, 2 mm, molded |
% | ISO 527-2/50 | |
断裂,2 mm,模压成型 Fracture, 2 mm, molded |
% | ISO 527-2/50 | |
弯曲模量 Bending modulus |
|||
2 mm,模压成型 2 mm, molded into shape |
MPa | ISO 178 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
美的、格力智能装备业务均表现亮眼
2017-09-07 近日,家电行业巨头美的、格力双双发布半年报。数据显示,二者上半年营收均实现大幅度增长。不同以往的是,虽然此次营收增长仍以家电行业为主,但是两家企业新兴的机器人、自动化及智能装备业务出现大幅增长,表现亮眼。 美的机器人业务营收同比增长35% 2017年 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |