牌号简介 About |
---|
聚偏氟乙烯315080003是偏氟乙烯(VF2)与三氟氯乙烯(CTFE)的柔性共聚物,具有很低的收缩率和优异的抗冲击性能。PVDF 315080003还具有很低的脆性温度,具有优异的低温性能。与所有的聚偏氟乙烯等级一样,聚偏氟乙烯315080003也具有很好的耐化学性和耐温性。特徵偏氟乙烯(VF2)和三氟氯乙烯(CTFE)的共聚物超柔韧极低收缩率宽工作温度范围可使用各种热塑性转化技术加工优异的低火焰和低烟性能 3M™ Dyneon™ PVDF 31508/0003 is a flexible copolymer of VF2 and CTFE, exhibiting very low shrinkage and excellent impact resistance. PVDF 31508/0003 also has a very low brittleness temperature, for excellent low temperature performance. This material is ideal for insulation and buffering materials for wire and cable applications and for tubing. PVDF 31508/0003 has excellent flame and smoke performance, with an LOI of 65. PVDF 31508/0003 is designed for high speed extrusion, and can be processed using a variety of conventional thermoplastic conversion techniques. As with all PVDF grades, PVDF 31508/0003 also possesses very good chemical and temperature resistance. Features and Benefits Copolymer of VF 2 and CTFE Ultra-flexible Very low shrinkage rates Wide operating temperature window Processable using a variety of thermoplastic conversion techniques Excellent low flame and low smoke performance |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.76 | g/cm³ | ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
ASTM D1238 | ||
230℃,2.16kg 230℃,2.16kg |
5.0 | g/10min | ASTM D1238 |
230℃,5.0kg 230℃,5.0kg |
15 | g/10min | ASTM D1238 |
吸水率 Water absorption rate |
|||
23℃,24hr 23℃,24hr |
< 0.040 | % | ISO 62 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength 2 |
|||
断裂,23℃ Fracture, 23 ℃ 2 |
22.0 | MPa | ASTM D638 |
拉伸应变 Tensile strain 2 |
|||
断裂,23℃ Fracture, 23 ℃ 2 |
% | ASTM D638 | |
弯曲模量 Bending modulus 3 |
|||
23℃ 23℃ 3 |
MPa | ASTM D790 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
脆化温度 Embrittlement temperature |
℃ | ASTM D746 | |
熔融峰值温度 Melting peak temperature |
℃ | ASTM D3418 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
表面电阻率 Surface resistivity |
ohms | DIN 53483 | |
体积电阻率 Volume resistivity |
ohms·cm | DIN 53483 | |
介电常数 Dielectric constant |
|||
1 MHz 1 MHz |
ASTM D150 | ||
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
UL 94 | ||
极限氧指数 Extreme oxygen index |
|||
3.0 mm 3.0 mm |
% | ASTM D2863 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 2.0 in/min |
3 0.079 in/min |
【新闻资讯】查看全部
巴斯夫生物法丙烯酰胺消费安装在南京落成
2017-11-30 日前,巴斯夫在中国南京化学工业园区的一套业内领先的生物法丙烯酰胺生产装置落成投产。该装置每年可生产超过 5 万吨丙烯酰胺。 丙烯酰胺用于生产水溶性絮凝剂,让污水处理、造纸、以及矿物加工和原油采收率的提升更加高效、更节省资源。 2014 年起,巴斯夫就开始在美国弗吉尼亚州萨福克生产生物法丙烯酰胺;2016 年,一套新的生物法丙烯酰胺装置在英国布拉德福德投入运营。南京项目顺利投产后,巴斯夫已在全球主要市场拥有三套业内最先进的生产装置。 巴斯夫表示 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |
电邮一份说明书
PDF文档名:搜料网-3M™ Dyneon™ Fluoroplastic PVDF 315080003证书
发送至:(多个地址,中间以逗号隔开)
发送一份副本给我:您还没有填写邮箱!(点击完善资料)