牌号简介 About |
---|
Tenac™ GN705是一种聚甲醛(POM)均聚物产品,含有的填充物为玻璃纤维增强材料。 它,在北美洲、非洲和中东、欧洲或亚太地区有供货。 Tenac™ GN705的应用领域包括工程/工业配件 和 房屋。 特性包括: 阻燃/额定火焰 低粘度 高刚度 高强度 均聚物 Tenac™ GN705 is an Acetal (POM) Homopolymer product filled with glass fiber. It is available in Africa & Middle East, Asia Pacific, Europe, or North America. Applications of Tenac™ GN705 include engineering/industrial parts and housings. Characteristics include: Flame Rated High Stiffness High Strength Homopolymer Low Viscosity |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density Density |
|||
|
1.56 | g/cm³ | ASTM D792 |
|
1.59 | g/cm³ | ISO 1183 |
熔体质量流动速率 Melt Flow Rate Melt Flow Rate |
|||
190℃,2.16 kg 190℃,2.16 kg |
10 | g/10min | ISO 1133 |
成型收缩率 Molding Shrinkage Molding shrinkage |
|||
flow flow |
0.4-0.6 | % | 内部方法 |
across flow across flow |
1.0-1.3 | % | 内部方法 |
吸水率 Water Absorption Water Absorption |
|||
24 h,23℃,50 % r.h. 24 h,23℃,50 % r.h. |
% | ASTM D570 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile Modulus Tensile Modulus |
MPa | ISO 527 | |
拉伸应力 Tensile Stress Tensile Stress |
|||
断裂 brk Broken BRK |
MPa | ISO 527 | |
断裂 brk Broken BRK |
MPa | ASTM D638 | |
断裂伸长率 Elongation at Break Elongation at Break |
|||
断裂 brk Broken BRK |
% | ASTM D638 | |
断裂 brk Broken BRK |
% | ISO 527-1,2 | |
弯曲模量 Flexural Modulus Flexural Modulus |
|||
|
MPa | ASTM D790 | |
|
MPa | ISO 178 | |
弯曲强度 Flexural Strength Flexural Strength |
MPa | ASTM D790 | |
泰伯耐磨性 Taber Abrasion Taber Abrasion |
mg | ASTM D1044 | |
洛氏硬度 Rockwell Hardness Rockwell hardness |
|||
M-Scale M-Scale |
M Scale | ASTM D-785 | |
R-Scale R-Scale |
R Scale | ASTM D-785 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy notched Impact strength Charpy Notched Impact Strength |
kJ/m² | ISO 179 | |
悬臂梁缺口冲击强度 Izod Notched Impact strength Izod Notched Impact strength |
J/m | ASTM D256 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 HDT Hot deformation temperature HDT |
|||
0.45 MPa 0.45 MPa |
℃ | ASTM D648 | |
0.45 MPa 0.45 MPa |
℃ | ISO 75-1/-2 | |
1.8 MPa 1.8 MPa |
℃ | ASTM D648 | |
1.8 MPa 1.8 MPa |
℃ | ISO 75-1/-2 | |
线性热膨胀系数 Coeff.of linear therm expansion Coeff. of linear thermal expansion |
|||
Flow Flow |
cm/cm/℃ | ASTM D696 | |
Flow Flow |
cm/cm/℃ | ISO 11359-2 | |
Transverse Transverse |
cm/cm/℃ | ASTM D696 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame Class Rating Flame Class Rating |
|||
0.75 mm 0.75 mm |
UL 94 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
鲁姆斯工艺聚丙烯聚合反应器实现国产化
2021-07-30 搜料网资讯: 7月20日,记者从兰州市科协获悉,日前由天华化工机械及自动化研究设计院有限公司设计制造的年产30万吨聚丙烯聚合反应器交付使用,这标志着全国首台/套鲁姆斯工艺聚 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |