聚丙烯自熄化合物,按UL-94规范分类,文件E178416,V-0至1.5mm。无PBDE和PBB的卤素含量符合RoHS。R在高温下的比热稳定性。高流动性,良好的尺寸稳定性,硬度和冲击强度之间的良好折衷,注塑成型的特殊等级,可根据样品选择天然色和有色。 Polypropylene self-extinguishing compound, classifiable according to the norms of UL-94, file E178416, V-0 up to 1.5mm. halogen content, free from PBDE and PBB, conforms to RoHS. Specific thermal stabilization ofr use at high application temperature. High flowability, excellent dimensional stability, good compromise between stiffness and impact strength, specifc grade for injection molding, available in natural and colored as per sample. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.35 | g/cm³ | ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
|||
230℃,2.16kg 230℃,2.16kg |
13 | g/10min | ISO 1133 |
收缩率 Shrinkage rate |
ISO 294-4 | ||
TD TD |
1.0 | % | ISO 294-4 |
MD MD |
1.0 | % | ISO 294-4 |
灰份含量 Ash Content |
20 | % | ISO 3451 |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
|||
23℃ 23℃ |
kJ/m² | ISO 179/1eU | |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
ISO 180/1A | ||
-20℃ -20℃ |
kJ/m² | ISO 180-1A | |
23℃ 23℃ |
kJ/m² | ISO 180-1A | |
老化性能 Aging performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
加速烘箱老化 Accelerate oven aging |
|||
150℃ 150℃ |
day | ISO 4577 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
维卡软化温度 Vicat Softening Temp |
|||
B50 B50 |
℃ | ISO 306 | |
球压测试 Ball pressure test |
|||
125℃ 125℃ |
IEC 335 | ||
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
UL 94 | ||
1.50 mm 1.50 mm 4 |
UL 94 | ||
3.00 mm 3.00 mm |
UL 94 | ||
灼热丝起燃温度 Igniting temperature of the hot wire |
℃ | IEC 60695-2-13 | |
极限氧指数 Extreme oxygen index 5 |
% | ISO 4589-2 | |
Glow Wire Test Glow Wire Test |
IEC 60695-2-12 | ||
针焰测试 Needle flame test 6 |
|||
2.00 mm 2.00 mm 6 |
IEC 60695-2-2 | ||
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 D,15 秒 Shore D, 15 seconds |
ISO 868 | ||
拉伸强度 tensile strength |
ISO 527-2/20 | ||
屈服,23℃ Yield, 23 ℃ |
MPa | ISO 527-2/20 | |
断裂,23℃ Fracture, 23 ℃ |
MPa | ISO 527-2/20 | |
拉伸应变 Tensile strain |
ISO 527-2/20 | ||
屈服,23℃ Yield, 23 ℃ |
% | ISO 527-2/20 | |
断裂,23℃ Fracture, 23 ℃ |
% | ISO 527-2/20 | |
弯曲模量 Bending modulus 3 |
|||
23℃ 23℃ 3 |
MPa | ISO 178 | |
弯曲强度 bending strength |
|||
23℃ 23℃ |
MPa | ISO 178 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 0.079 in/min |
3 up to 1.5mm |
4 23°C |
5 Method A-B |
【新闻资讯】查看全部
生态文明贵阳国际论坛“陆地微塑料研讨会”
2018-07-31 近年来,全球对海洋环境和海岸微塑料污染带来的生态效应、渔业影响和健康风险日益关注。在7月初举行的生态文明贵阳国际论坛“海洋微塑料研讨会”高峰会上,世界各国再次聚焦海洋微塑料问题。这也是该论坛举办十年来首次将“微塑料防治”作为主题,呼吁人们关注微塑料污染,保护海洋生态环境。 塑料垃圾是海洋不能承受之重。据统计,全球每年约有1000万―2000万吨的塑料垃圾进入海洋,随时间的流逝破碎成不计其数的塑料微粒进入水体中,能够存在数百年时间。作为环境中的一类新型污染物,微塑料将对海洋生 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |