牌号简介 About |
---|
Ultramid® B3EG6 BK00564是一种30%玻璃纤维增强,色素黑色注塑成型PA6级。典型应用包括工业品和电气绝缘部件。 Ultramid B3EG6 BK00564 is a 30% glass fiber reinforced, pigmented black injection molding PA6 grade. Applications Typical applications include industrial articles and electrical insulating parts. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.36 | g/cm³ | ISO 1183 |
吸水率 Water Absorption |
|||
23℃,24hr 23℃,24hr |
6.00 | % | ISO 62 |
23℃,50% RH 23℃,50% RH |
2.10 | % | ISO 62 |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 HDT |
|||
0.45 MPa,未退火 0.45 MPa, unannealed |
220 | ℃ | ISO 75-2/Bf |
1.8 MPa,退火 1.8 MPa, annealed |
210 | ℃ | ISO 75-2/Af |
熔融温度 Melting temperature |
℃ | ISO 11357-3 | |
维卡软化温度 Vicat Softening Temperature |
|||
电气性能 ELECTRICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
体积电阻 Volume Resistivity |
Ω.cm | IEC 60093 | |
介电常数 Dielectric constant |
|||
23℃ 23℃ |
1 MHz | IEC 60250 | |
耗散因数 Dissipation factor |
|||
23℃ 23℃ |
100 Hz | IEC 60250 | |
23℃ 23℃ |
1 MHz | IEC 60250 | |
相比漏电起痕指数 Comparative Tracking Index |
V | IEC 60112 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame Class Rating |
|||
1.50mm 1.50mm |
UL-94 | ||
2.00mm 2.00mm |
UL-94 | ||
3.00mm 3.00mm |
UL-94 | ||
灼热丝起燃温度 Glow Wire Ignitability Temperature(GWIT) |
|||
1 mm 1 mm |
℃ | IEC 60695-2-12 | |
2 mm 2 mm |
℃ | IEC 60695-2-12 | |
3 mm 3 mm |
℃ | IEC 60695-2-12 | |
灼热丝相对温度 Relative temperature of heating wire |
|||
1.00mm 1.00mm |
℃ | IEC 60695-2-13 | |
2.00mm 2.00mm |
℃ | IEC 60695-2-13 | |
3.00mm 3.00mm |
℃ | IEC 60695-2-13 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
|||
23℃ 23℃ |
kJ/m² | ISO 179/1eA | |
悬臂梁缺口冲击强度 Izod Notched Impact strength |
|||
23℃ 23℃ |
kJ/m² | ISO 180-1A | |
-30℃ -30℃ |
kJ/m² | ISO 180-1A | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
球压硬度 ball-indentation hardness |
MPa | ISO 2039-1 | |
拉伸强度 tensile strength |
|||
23℃ 23℃ |
MPa | ISO 527-2 | |
拉伸应变 Tensile strain |
|||
断裂,23℃ Fracture, 23 ℃ |
% | ISO 527-2 | |
拉伸模量 Tensile modulus |
|||
23℃ 23℃ |
MPa | ISO 527-2 | |
弯曲模量 Flexural Modulus |
|||
23℃ 23℃ |
MPa | ISO 178 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
欧洲钛白粉价格稳中走软在于欧洲供应形势改善
2018-07-20 随着欧洲钛白粉市场供应状况改善,三季度合约价格出现走软迹象。本周结算价格显示,来自油漆、塑料和纸张层压板行业钛白粉合约价稳中有降,降幅为30~70欧元/吨。 买家和经销商们表示,欧洲钛白粉价格稳中走软在于欧洲供应形势改善,尤其是近几个月来自中国的进口量增加,人们对7月钛白粉现货价格基本看跌。不过,虽然钛白粉价格有所下跌,但整体仍处于较高水平,买家尝试通过使用替代材料或通过减少钛白粉用量来节省成本。 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |