牌号简介 About |
---|
Lupoy NF 1009F08R,环保型UL94 V0/2.0 mm,专为挤出和注塑产品设计。它结合了优良的物理性能平衡的耐热性,透明度和冲击强度,并显示出优良的加工特性。 LUPOY NF 1009F08R, eco-friendly UL94 V0/2.0 mm, is designed for extrusion and injection molding products. It combines an excellent physical property balance of heat resistance, transparency and impact strength and exhibits excellent processing characteristics. |
产品描述 Product Description
厂家:韩国LG化学 LG Chemical
类别:PC Polycarbonate
用途:通讯器材;电气/电子应用领域;照明装置;外壳;
加工条件:挤出 Extrusion
性能特点: 无卤; 防火阻燃等级V-0; 含脱模剂; 耐高温; 防火阻燃等级V-2; 低磷含量; 透光性好; 冲击性能好; 易加工; Excellent Processability,Good Clarity,High impact resistance,Halogen free,Good stripping performance,High Heat Resistance,Low to no phosphorus content,V-2,V-0
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.20 | g/cm³ | ASTM D792 |
熔体质量流动速率 Melt Flow Rate |
|||
300℃,1.20kg 300℃,1.20kg |
8.0 | g/10min | ASTM D1238 |
收缩率 Shrinkage rate |
|||
MD MD |
0.50 to 0.70 | % | ASTM D955 |
吸水率 Water absorption rate |
|||
平衡,23℃,50% RH Equilibrium, 23 ℃, 50% RH |
0.32 | % | ASTM D570 |
23℃,24hr 23℃,24hr |
0.15 | % | ASTM D570 |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
23℃,3.2mm 23℃,3.2mm 4 |
J/m | ASTM D256 | |
23℃ 23℃ |
ASTM D256 | ||
装有测量仪表的落镖冲击 Dart impact equipped with measuring instruments 5 |
|||
23℃,3.20 mm,Total Energy 23℃,3.20 mm,Total Energy 5 |
J | ASTM D3763 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火,4.0 mm 1.8 MPa, unannealed, 4.0 mm |
℃ | ASTM D648 | |
0.45 MPa,未退火,4.0 mm 0.45 MPa, unannealed, 4.0 mm |
℃ | ASTM D648 | |
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 6 | |
球压温度 Ball pressure temperature |
℃ | IEC 60598-1 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD:-40~82℃ MD:-40~82℃ |
1/℃ | ASTM D696 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
体积电阻率 Volume resistivity |
|||
23℃ 23℃ |
ohms·cm | ASTM D257 | |
介电强度 Dielectric strength |
kV/mm | ASTM D149 | |
介电常数 Dielectric constant |
|||
60 Hz 60 Hz |
ASTM D150 | ||
耗散因数 Dissipation factor |
|||
60 Hz 60 Hz |
ASTM D150 | ||
相比漏电起痕指数 Compared to the leakage tracing index |
|||
2.00 mm 2.00 mm |
V | IEC 60112 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
UL 94 | ||
1.50 mm 1.50 mm |
UL 94 | ||
2.00 mm 2.00 mm |
UL 94 | ||
3.00 mm 3.00 mm |
UL 94 | ||
灼热丝起燃温度 Igniting temperature of the hot wire 7 |
|||
2 mm 2 mm 7 |
℃ | IEC 60695-2-13 | |
极限氧指数 Extreme oxygen index |
% | ASTM D2863 | |
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
折射率 Refractive index |
ASTM D542 | ||
透光率 Transmittance |
% | ASTM D1003 | |
雾度 Haze |
% | ASTM D1003 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
MPa | ASTM D638 | |
拉伸强度 tensile strength 2 |
|||
断裂 fracture |
MPa | ASTM D638 | |
屈服,23℃ Yield, 23 ℃ 2 |
MPa | ASTM D638 | |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ASTM D638 | |
屈服 yield |
% | ASTM D638 | |
弯曲模量 Bending modulus |
MPa | ASTM D790 | |
弯曲强度 bending strength |
MPa | ASTM D790 | |
耐磨耗性 Wear resistance 3 |
|||
Change in Haze Change in Haze 3 |
% | ASTM D1004 | |
洛氏硬度 Rockwell hardness |
ASTM D785 | ||
M 级 M-level |
ASTM D785 | ||
R 级 R-level |
ASTM D785 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 2.0 in/min |
3 1000g, 500 cycles, CS-10F Wheel |
4 9.8 mil 缺口深度 |
5 11.1 ft/sec |
6 速率 A (50°C/h), 载荷2 (50N) |
7 5 sec |
【新闻资讯】查看全部
获新专利,硅宝科技新专利守护锂电安全
2023-01-12 扫描上图二维码,可以免费下载 搜料 APP 日前,成都硅宝科技股份有限公司的一种有机硅阻燃添加剂及阻燃型锂离子电池电解液获得国家发明专利授权。该专利产品可以有效提高电池的 |
获新专利,硅宝科技新专利守护锂电安全
日前,成都硅宝科技股份有限公司的“一种有机硅阻燃添加剂及阻燃型锂离子电池电解液”获得国家发明专利授权。该专利产品可以有效提高电池的循环稳定性,从而提高锂电池的安全水平。
锂离子电池易燃易爆,需要在电解液中添加阻燃添加剂。目前,使用最广泛的阻燃添加剂是磷阻燃剂。然而,磷阻燃剂的阻燃效率低,如果添加量大,电解质的导电性会降低。此外,传统的磷阻燃剂与锂离子电池负极的兼容性较差,这会影响电池的电化学性能,降低电池的循环寿命。
硅宝科技的这一专利产品克服了直接使用传统磷系阻燃剂的缺点,采用热稳定性好、阻燃效率高、相容性好的有机硅化合物作为阻燃添加剂,少量添加也能达到理想的阻燃效果。此外,这种有机硅阻燃剂与锂离子电池电解质具有很好的相容性。在提高电解液的阻燃性时,不能影响电池的电化学性能,提高电池的循环稳定性。
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |
价格走势图
开始时间:
结束时间:
材料厂家:
【牌号齐全,内容全面】
全网共2500+项牌号+上游原料单体+原油价格,最长可追溯近20年价格行情
【精准,及时,权威!】
专业团队挖掘行情信息,第一时间发布行情
抱歉!该牌号暂无认证数据。
免责声明:参考价格是搜料网根据网络大数据拟合分析的结果,仅供参考。实际成交价取决但不限于以下因素:下单时间,付款方式,交货方式,数量,税费,色号,产地,项目信息。
抱歉!暂无数据。
抱歉!暂无数据。