牌号简介 About |
---|
Bayflex XGT-80是一种用于反应注射成型(RIM)工艺的弹性聚氨酯系统。该体系分为两种液体组分:A组分为改性二苯基甲烷二异氰酸酯(MDI),B组分为聚醚多元醇体系。注:多元醇组分相在静置时分离,使用前必须通过机械方式彻底混合。BayFLUX XGT-80的延长凝胶时间给设备设计者创造了可以在现有的注塑机上成型的大型复杂零件的灵活性。该树脂具有优良的表面质量和高抗冲击性,可用于农业设备、重型卡车、特种运输和海洋应用。 Bayflex XGT-80 is an elastomeric polyurethane system used in the reaction injection molding (RIM) process. The system is supplied as two liquid components: Component A is a modified diphenylmethane diisocyanate (MDI), and Component B is a polyether polyol system. Note: The polyol component phase-separates upon standing and must be thoroughly mixed via mechanical means prior to use. The extended gel time of Bayflex XGT-80 gives equipment designers the flexibility to create large, complex parts that can be molded on existing injection machinery. The resin's excellent surface quality and high impact resistance make it a candidate for agricultural equipment, heavy-duty trucks, specialty transportation, and marine applications. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.15 | g/cm³ | ASTM D792 , ASTM D1622 |
收缩率 Shrinkage rate |
|||
MD:3.2 mm MD:3.2 mm |
0.55 到 0.65 | % | 内部方法 |
弹性体 elastic body |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
撕裂强度 tear strength 2 |
|||
3.18 mm 3.18 mm 2 |
114 | kN/m | ASTM D624 |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
3.2mm 3.2mm |
270 | J/m | ASTM D256 |
装有测量仪表的落镖冲击 Dart impact equipped with measuring instruments 3 |
ASTM D3763 | ||
-30℃,3.18 mm -30℃,3.18 mm |
2.71 | J | ASTM D3763 |
23℃,3.18 mm 23℃,3.18 mm |
J | ASTM D3763 | |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
Heat Sag(4 in Overhang,121℃,3.18 mm) Heat Sag(4 in Overhang,121℃,3.18 mm) 6 |
mm | ASTM D3769 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 D,3.18 mm Shaw D, 3.18 mm |
ASTM D2240 | ||
拉伸强度 tensile strength |
|||
断裂,3.18 mm Fracture, 3.18 mm |
MPa | ASTM D638 | |
拉伸应变 Tensile strain |
|||
断裂,3.18 mm Fracture, 3.18 mm |
% | ASTM D638 | |
弯曲模量 Bending modulus |
ASTM D790 | ||
-30℃,3.18 mm -30℃,3.18 mm |
MPa | ASTM D790 | |
23℃,3.18 mm 23℃,3.18 mm |
MPa | ASTM D790 | |
70℃,3.18 mm 70℃,3.18 mm |
MPa | ASTM D790 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD:3.2 mm MD:3.2 mm |
1/℃ | ASTM D696 | |
热固组件 Thermosetting components 4 |
|||
部件 A Component A |
|||
部件 B Component B |
|||
贮藏期限 Storage period 5 |
|||
32℃ 32℃ 5 |
wk | ||
脱模时间 stripping time |
min |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 C 模具 |
3 7,33 ft/sec |
4 1.05 Index |
5 0.125 in |
6 1 hr |
【新闻资讯】查看全部
106亿塑料大单支出囊中!重庆在下哪盘棋?
2016-11-02 10月31日,第二届中国国际工程塑料产业创新峰会暨中国西部(重庆)塑料生态产业园投资峰会在重庆开幕,会议以“创新.智造.产业互联”为主题。此次峰会上,共签约37个塑料项目、2个创新平台,协议引资106.8亿元人民币。 会议期间举行了中国西部(重庆)塑料生态产业园院士专家工作站、重庆市塑料检测中心揭牌仪式。重庆市政府副秘书长罗德表示,塑料作为新材料技术革命的重要领域,是重庆创新发展战略性新兴产业的重要支撑和组成部分。 中国西部(重庆)塑料生态产业园位于重庆市梁 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |