牌号简介 About |
---|
PRE-ELEC® PE 1202是一种基于PE-HD的导电热塑性化合物。导电性是通过使用特殊的导电炭黑来实现的。除了低电阻率。Pre-elec PE 1291具有良好的机械性能平衡,易于挤出。PRE-ELEC® PE 1202也可以用15-25%的未净化或回收的PE-HD稀释。应始终测试实际数量,因为它还取决于处理参数。典型应用包括成本效益吹塑瓶,容器和罐。 PRE-ELEC® PE 1202 is a conductive thermoplastic compound based on PE-HD. The electrical conductivity is achieved by using special conductive carbon black. In addition to a low electrical resistivity. PRE-ELEC® PE 1291 has an excellent balance of mechanical properties and is easy to extrude. PRE-ELEC® PE 1202 may also be diluted with 15-25% virgin or recycled PE-HD. The actual amount should always be tested as it also depends on the processing parameters. Typical applications include cost-effective blow moulded bottles, containers and canisters. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.08 | g/cm³ | ASTM D792 |
密度 Density |
1.09 | g/cm³ | ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,21.6kg 190℃,21.6kg |
2.0 | g/10min | ISO 1133 |
收缩率 Shrinkage rate |
|||
MD MD |
1.5 to 2.5 | % | ISO 294-4 |
MD MD |
1.5 to 2.5 | % | ASTM D955 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
ISO 868 | ||
邵氏 A Shaw's A |
ISO 868 | ||
邵氏 D Shaw's D |
ISO 868 | ||
拉伸强度 tensile strength |
MPa | ASTM D638 | |
屈服 yield |
MPa | ISO 527-2 | |
屈服 yield |
MPa | ASTM D638 | |
4 mm 4 mm |
MPa | ISO 527-2 | |
拉伸应变 Tensile strain |
|||
断裂,4 mm Fracture, 4 mm |
% | ISO 527-2 | |
屈服 yield |
% | ISO 527-2 | |
弯曲模量 Bending modulus |
|||
4 mm 4 mm |
MPa | ISO 178 | |
4 mm 4 mm |
MPa | ASTM D790 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength 2 |
|||
-20℃ -20℃ |
kJ/m² | ASTM D256 | |
-20℃ -20℃ |
kJ/m² | ISO 179 | |
23℃ 23℃ |
kJ/m² | ISO 179 | |
23℃ 23℃ |
kJ/m² | ASTM D256 | |
简支梁无缺口冲击强度 Charpy Unnotch Impact strength 2 |
|||
-20℃ -20℃ |
ASTM D256 | ||
-20℃ -20℃ |
ISO 179 | ||
23℃ 23℃ |
ISO 179 | ||
23℃ 23℃ |
ASTM D256 | ||
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch 2 |
ISO 180 | ||
Area Area |
ASTM D256 | ||
-20℃,4.00 mm -20℃,4.00 mm |
kJ/m² | ASTM D256 | |
23℃,4.00 mm 23℃,4.00 mm |
kJ/m² | ASTM D256 | |
-20℃ -20℃ |
kJ/m² | ISO 180 | |
23℃ 23℃ |
kJ/m² | ISO 180 | |
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam |
ASTM D256 | ||
-20℃,4 mm -20℃,4 mm |
ASTM D256 | ||
23℃,4 mm 23℃,4 mm |
ASTM D256 | ||
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam 2 |
ISO 180 | ||
-20℃ -20℃ |
ISO 180 | ||
23℃ 23℃ |
ISO 180 | ||
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/Af | |
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ASTM D648-A | |
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ISO 75-2/Bf | |
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ASTM D648-B | |
维卡软化温度 Vicat Softening Temp |
|||
-- -- |
℃ | ASTM D1525 3 | |
-- -- |
℃ | ASTM D1525 4 | |
维卡软化温度 Vicat Softening Temp |
|||
A50 A50 |
℃ | ISO 306/A50 | |
B50 B50 |
℃ | ISO 306 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
表面电阻率 Surface resistivity |
ohms | IEC 61340-2-3 | |
体积电阻率 Volume resistivity |
ohms·cm | 内部方法 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 4 mm thickness |
3 标准 B (120°C/h), 载荷2 (50N) |
4 速率 A (50°C/h), 载荷2 (50N) |
【新闻资讯】查看全部
沙特基础获准收购科莱恩24.99%的股份
2018-09-12 科莱恩(Clariant)是全球特种化学品行业的领军企业。该公司宣布,沙特基础工业公司(SABIC)已获得竞争监管机构的最终批准,获准收购科莱恩24.99%的股份。因此,在接下来的几天内将无条件完成收购,此次收购使沙特基础工业公司成为科莱恩最大的战略锚定股东,也是Sud-Chemie集团除了前股东之外的第二大战略锚定股东。 沙特基础工业公司是全球第三大多元化化工企业,也是科莱恩公司在催化剂合资企业科学化设计方面的长期合作伙伴。该公司于2018年1月就收购科莱恩股份达成了一项 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |