| 牌号简介 About |
|---|
| CALIBRE™ 3503是一种聚碳酸酯树脂，具有优异的抗冲击性、热变形性和光学透明性的平衡性，在注塑应用中具有出色的加工能力。CALIBRE™ 3503包含脱模剂和紫外线稳定剂。政府和行业标准：保险商实验室公司（UL）应用：照明电气存储 CALIBRE™ 3503 is a polycarbonate resin offering an excellent balance of impact resistance, heat distortion resistance and optical clarity with outstanding process ability for injection molding applications. CALIBRE 3503 contains mould release and UV stabilizer. Govt. and Industry Standards: Underwriters Laboratory Inc. (UL) Applications: Lighting Electrical Storage |
产品描述 Product Description
用途：电气/电子应用领域;照明应用;
加工条件：注射成型 Injection Molding
性能特点： 防火阻燃等级V-2; 透光性好; 冲击性能好; 耐候抗UV; Weather resistance is good,Good Clarity,High impact resistance,V-2
紫外线：UV Stabilized
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
1.20 | g/cm³ | ASTM D792 |
|
密度 Density |
1.20 | g/cm³ | ISO 1183/B |
|
熔体质量流动速率 Melt Flow Rate |
|||
|
300℃，1.20kg 300℃，1.20kg |
35 | g/10min | ISO 1133 |
|
300℃，1.20kg 300℃，1.20kg |
35 | g/10min | ASTM D1238 |
|
收缩率 Shrinkage rate |
|||
|
MD MD |
0.50 | % | ASTM D955 |
|
MD MD |
% | ISO 294-4 | |
|
吸水率 Water absorption rate |
|||
|
平衡，23℃，50% RH Equilibrium, 23 ℃, 50% RH |
% | ISO 62 | |
|
平衡，23℃，50% RH Equilibrium, 23 ℃, 50% RH |
% | ASTM D570 | |
|
23℃，24hr 23℃，24hr |
% | ASTM D570 | |
|
23℃，24hr 23℃，24hr |
% | ISO 62 | |
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
拉伸模量 Tensile modulus 2 |
MPa | ASTM D638 | |
|
拉伸模量 Tensile modulus |
MPa | ISO 527-2/50 | |
|
拉伸强度 tensile strength |
|||
|
断裂 fracture |
MPa | ISO 527-2/50 | |
|
断裂 fracture 2 |
MPa | ASTM D638 | |
|
屈服 yield 2 |
MPa | ASTM D638 | |
|
屈服 yield |
MPa | ISO 527-2/50 | |
|
拉伸应变 Tensile strain |
|||
|
断裂 fracture |
% | ISO 527-2/50 | |
|
断裂 fracture 2 |
% | ASTM D638 | |
|
屈服 yield 2 |
% | ASTM D638 | |
|
屈服 yield |
% | ISO 527-2/50 | |
|
弯曲模量 Bending modulus 3 |
MPa | ASTM D790 | |
|
弯曲模量 Bending modulus 4 |
MPa | ISO 178 | |
|
弯曲强度 bending strength 3 |
MPa | ASTM D790 | |
|
弯曲强度 bending strength 4 |
MPa | ISO 178 | |
|
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
简支梁缺口冲击强度 Charpy Notched Impact Strength |
|||
|
23℃ 23℃ |
kJ/m² | ISO 179/1eA | |
|
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
|
23℃ 23℃ |
kJ/m² | ISO 180-A | |
|
23℃ 23℃ |
J/m | ASTM D256 | |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
热变形温度 Hot deformation temperature |
|||
|
1.8 MPa，退火 1.8 MPa, annealed |
℃ | ASTM D648 | |
|
1.8 MPa，退火 1.8 MPa, annealed |
℃ | ISO 75-2/A | |
|
0.45 MPa，退火 0.45 MPa, annealed |
℃ | ASTM D648 | |
|
0.45 MPa，退火 0.45 MPa, annealed |
℃ | ISO 75-2/B | |
|
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 5 | |
|
B50 B50 |
℃ | ISO 306 | |
|
球压温度 Ball pressure temperature |
℃ | IEC 60335-1 | |
|
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
|
MD MD |
1/℃ | ISO 11359-2 | |
|
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
体积电阻率 Volume resistivity |
ohms·cm | IEC 60093 | |
|
介电强度 Dielectric strength |
kV/mm | ASTM D149 | |
|
介电强度 Dielectric strength |
kV/mm | IEC 60243-1 | |
|
介电常数 Dielectric constant |
ASTM D150 | ||
|
60 Hz 60 Hz |
ASTM D150 | ||
|
1 MHz 1 MHz |
ASTM D150 | ||
|
耗散因数 Dissipation factor |
ASTM D150 | ||
|
50 Hz 50 Hz |
ASTM D150 | ||
|
1 MHz 1 MHz |
ASTM D150 | ||
|
相比漏电起痕指数 Compared to the leakage tracing index |
|||
|
2.00 mm，解决方案 A 2.00 mm, solution A |
V | IEC 60112 | |
|
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
阻燃等级 Flame retardant level 6 |
UL 94 | ||
|
1.00 mm 1.00 mm |
UL 94 | ||
|
1.50 mm 1.50 mm |
UL 94 | ||
|
3.00 mm 3.00 mm |
UL 94 | ||
|
灼热丝可燃性指数 Glowing wire flammability index 6 |
IEC 60695-2-12 | ||
|
1.0 mm 1.0 mm |
℃ | IEC 60695-2-12 | |
|
2.0 mm 2.0 mm |
℃ | IEC 60695-2-12 | |
|
3.0 mm 3.0 mm |
℃ | IEC 60695-2-12 | |
|
灼热丝起燃温度 Igniting temperature of the hot wire 6 |
IEC 60695-2-13 | ||
|
1 mm 1 mm |
℃ | IEC 60695-2-13 | |
|
2 mm 2 mm |
℃ | IEC 60695-2-13 | |
|
3 mm 3 mm |
℃ | IEC 60695-2-13 | |
|
极限氧指数 Extreme oxygen index 6 |
% | ISO 4589-2 | |
|
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
折射率 Refractive index |
ASTM D542 | ||
|
折射率 Refractive index |
ISO 489 | ||
|
透光率 Transmittance |
% | ASTM D1003 | |
|
雾度 Haze |
% | ASTM D1003 | |
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
| 2 2.0 in/min |
| 3 方法 I (三点负荷), 0.079 in/min |
| 4 0.079 in/min |
| 5 速率 A (50°C/h), 载荷2 (50N) |
| 6 This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
|
【新闻资讯】查看全部
拜耳提高收购孟山都报价至650亿美元
2016-07-15 德国拜耳公司(Bayer，BAYRY)宣布，向孟山都公司(Monsanto ，MON)发出修改后的收购提议。之前拜耳公司希望达成这笔巨额交易的尝试被孟山都拒绝。 据15日报道，拜耳在声明中称，对孟山都的收购报价已提高至每股125美元，总值650亿美元。之前报价为每股122美元，总价值620亿美元。拜耳对孟山都的这份新报价为纯现金收购，拜耳称所需资金已就位。 拜耳公司还提出，如果交易受阻于反垄断理由，将支付15亿美元的分手费。 孟山都随后证实已 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |