牌号简介 About |
---|
Westlake EF706AA是一种低密度聚乙烯树脂,建议用于吹塑或铸膜应用,其中硬度和机械加工性很重要。应用/使用铸膜 Westlake EF706AA is a LDPE resin suggested for blown or cast film applications where stiffness and machinability are important. Application/Uses Cast Film |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.923 | g/cm³ | ASTM D1505 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
2.3 | g/10min | ASTM D1238 |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
薄膜厚度 film thickness |
|||
测试 test |
51 | µm | |
割线模量 Secant modulus |
ASTM D882 | ||
1% 正割,MD:51 µm,吹塑薄膜 1% secant, MD: 51 µ m, blow molded film |
165 | MPa | ASTM D882 |
1% 正割,TD:51 µm,吹塑薄膜 1% secant, TD: 51 µ m, blow molded film |
207 | MPa | ASTM D882 |
拉伸强度 tensile strength |
ASTM D882 | ||
MD,断裂,51 µm,吹塑薄膜 MD, fracture, 51 µ m, blow molded film |
MPa | ASTM D882 | |
TD,断裂,51 µm,吹塑薄膜 TD, fracture, 51 µ m, blow molded film |
MPa | ASTM D882 | |
拉伸应变 Tensile strain |
ASTM D882 | ||
MD,断裂,51 µm,吹塑薄膜 MD, fracture, 51 µ m, blow molded film |
% | ASTM D882 | |
TD,断裂,51 µm,吹塑薄膜 TD, fracture, 51 µ m, blow molded film |
% | ASTM D882 | |
落锤冲击 Drop hammer impact |
|||
51 µm,吹塑薄膜 51 µ m, blow molded film |
g | ASTM D1709 |
备注 | |||
---|---|---|---|
暂无数据 |
【新闻资讯】查看全部
投资260亿元,大连长兴岛恒力聚酯科技产业园开工
2022-02-09 大连市政府网发布消息,2月8日,大连长兴岛恒力聚酯科技产业园开工暨重大项目签约仪式举行。 恒力聚酯科技产业园项目将分三期建设,将重点打造可降解材料、功能性聚酯材料、高 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |