牌号简介 About |
---|
Lexan Exl132t树脂Lexan Exl132t聚碳酸酯(PC)硅氧烷共聚物树脂是一种具有额外释放性能的紫外线稳定透明注塑(IM)级树脂。与标准PC树脂相比,该树脂具有良好的低温(20 C)延展性、高流动性和良好的加工性,有机会缩短IM循环时间。LEXAN™ EXL1132T resin是一种通用产品,可提供透明和不透明的颜色,可能是广泛应用的最佳候选。 LEXAN EXL1132T polycarbonate (PC) siloxane copolymer resin is a UV stabilized transparent injection molding (IM) grade with extra release properties. This resin offers good low temperature (-20 C) ductility in combination with high flow characteristics and excellent processability with opportunities for shorter IM cycle times compared to standard PC resins. LEXAN EXL1132T resin is a general purpose product available in transparent and opaque colors and may be an excellent candidate for a broad range of applications. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.19 | g/cm³ | ASTM D792 |
密度 Density |
1.19 | g/cm³ | ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
|||
300℃,1.20kg 300℃,1.20kg |
20 | g/10min | ASTM D1238 |
熔体体积流动速率 Melt Volume Rate |
|||
300℃,1.2 kg 300℃,1.2 kg |
19.0 | cm³/10min | ISO 1133 |
收缩率 Shrinkage rate |
|||
TD:3.2 mm TD:3.2 mm |
0.40 to 0.80 | % | 内部方法 |
MD:3.2 mm MD:3.2 mm |
% | 内部方法 | |
吸水率 Water absorption rate |
|||
饱和,23℃ Saturation, 23 ℃ |
% | ISO 62 | |
平衡,23℃,50% RH Equilibrium, 23 ℃, 50% RH |
% | ISO 62 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength 7 |
ISO 179/1eA | ||
-30℃ -30℃ |
kJ/m² | ISO 179/1eA | |
23℃ 23℃ |
kJ/m² | ISO 179/1eA | |
简支梁无缺口冲击强度 Charpy Unnotch Impact strength 7 |
ISO 179/1eU | ||
-30℃ -30℃ |
ISO 179/1eU | ||
23℃ 23℃ |
ISO 179/1eU | ||
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
ASTM D256 | ||
-30℃ -30℃ |
J/m | ASTM D256 | |
23℃ 23℃ |
J/m | ASTM D256 | |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch 8 |
ISO 180/1A | ||
-30℃ -30℃ |
kJ/m² | ISO 180-1A | |
23℃ 23℃ |
kJ/m² | ISO 180-1A | |
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam 8 |
ISO 180/1U | ||
-30℃ -30℃ |
ISO 180/1U | ||
23℃ 23℃ |
ISO 180/1U | ||
装有测量仪表的落镖冲击 Dart impact equipped with measuring instruments |
|||
23℃,Total Energy 23℃,Total Energy |
J | ASTM D3763 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火,64 mm跨距 1.8 MPa, unannealed, 64 mm span 9 |
℃ | ISO 75-2/Af | |
1.8 MPa,未退火,3.2 mm 1.8 MPa, unannealed, 3.2 mm |
℃ | ASTM D648 | |
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 10 | |
维卡软化温度 Vicat Softening Temp |
|||
B50 B50 |
℃ | ISO 306 | |
B120 B120 |
℃ | ISO 306/B120 | |
球压测试 Ball pressure test |
|||
125℃ 125℃ |
IEC 60695-10-2 | ||
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
TD:23~80℃ TD:23~80℃ |
1/℃ | ISO 11359-2 | |
TD:-40~95℃ TD:-40~95℃ |
1/℃ | ASTM E831 | |
MD:23~80℃ MD:23~80℃ |
1/℃ | ISO 11359-2 | |
MD:-40~95℃ MD:-40~95℃ |
1/℃ | ASTM E831 | |
相对温度指数 Relative temperature index |
|||
电气性能 Electrical performance |
℃ | UL 746 | |
强度机械性能 Strength mechanical performance |
℃ | UL 746 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
表面电阻率 Surface resistivity |
ohms | ASTM D257 | |
体积电阻率 Volume resistivity |
ohms·cm | ASTM D257 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
|||
1.50 mm 1.50 mm |
UL 94 | ||
灼热丝可燃性指数 Glowing wire flammability index |
|||
3.0 mm 3.0 mm |
℃ | IEC 60695-2-12 | |
灼热丝起燃温度 Igniting temperature of the hot wire |
IEC 60695-2-13 | ||
0.8 mm 0.8 mm |
℃ | IEC 60695-2-13 | |
3 mm 3 mm |
℃ | IEC 60695-2-13 | |
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
透光率 Transmittance |
|||
2540 µm 2540 µm |
% | ASTM D1003 | |
雾度 Haze |
|||
2540 µm 2540 µm |
% | ASTM D1003 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus 2 |
MPa | ASTM D638 | |
拉伸模量 Tensile modulus |
MPa | ISO 527-1-2 | |
拉伸强度 tensile strength 3 |
|||
断裂 fracture 3 |
MPa | ASTM D638 | |
断裂 fracture |
MPa | ISO 527-2/50 | |
屈服 yield |
MPa | ISO 527-2/50 | |
屈服 yield 3 |
MPa | ASTM D638 | |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ISO 527-2/50 | |
断裂 fracture 4 |
% | ASTM D638 | |
屈服 yield 3 |
% | ASTM D638 | |
屈服 yield |
% | ISO 527-2/50 | |
弯曲模量 Bending modulus 5 |
MPa | ISO 178 | |
50 mm跨距 50 mm span 4 |
MPa | ASTM D790 | |
弯曲强度 bending strength 5 , 6 |
MPa | ISO 178 | |
弯曲强度 bending strength 4 |
|||
屈服,50 mm跨度 Yield, 50 mm span 4 |
MPa | ASTM D790 | |
洛氏硬度 Rockwell hardness |
|||
L 级 Level L |
ISO 2039-2 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 2.0 in/min |
3 类型 1, 2.0 in/min |
4 0.051 in/min |
5 0.079 in/min |
6 Yield |
7 80*10*3 sp=62mm |
8 80*10*3 |
9 80*10*4 mm |
10 速率 A (50°C/h), 载荷2 (50N) |
【新闻资讯】查看全部
生物可降解复合材料:医学植入技术的严重停顿
2016-07-14 赢创工业集团正研发先进的可生物降解的高强度复合材料。 这些材料有望代替金属作为骨折内部固定的植入物。植入物对支撑骨骼的愈合起到至关重要的作用。目前使用的金属植入物或永久留在人体内,或需通过额外的手术取出。 |
生物可降解复合材料:医学植入技术的严重停顿 赢创工业生产集团公司正产品研发优秀的可生物溶解的高韧性高分子材料。 这种原材料有希望替代金属材料做为骨裂內部固定不动的植入物。植入物对支撑点骨骼的痊愈具有尤为重要的功效。现阶段应用的金属材料植入物或永久性留到人体内,或需根据附加的手术治疗取下。相比而言,赢创新式高分子材料做成的植入物在骨骼痊愈的全过程里能被人体消化吸收。 这种原材料由聚合物和骨骼中当然存有的化学物质构成。赢创的此项科学研究仍处在前期环节,但它针对病人的潜在性褔利已不言而喻。病人将不用开展附加的手术治疗取下植入物。独特的器材设计方案还有利于骨骼更迅速地再造。 此新项目已经坐落于英国阿拉巴马州谢菲尔德的医疗器械新项目屋进行。该新项目有着一支由20 多位权威专家构成的精英团队。她们的每日任务是开发设计新式医疗技术解决方法和原材料,尤其是植入物。新项目屋的责任人Andreas karau 博士研究生那样叙述她们的企业愿景:"长久来讲,大家关心的关键是生物研究。大家期待开发设计出生物可消化吸收植入物,以身心健康机构取代损伤机构。大家现阶段相关生物生物降解高分子材料的工作中正向着这一总体目标迈开了第一步。" 销售市场对高韧性生物可降解材料的要求是极大的。骨裂固定不动需要的植入物总数丰厚:比如,骨质疏松每一年会造成 约890 万例的骨裂病案。除此之外,3000 亿英镑的全世界医疗技术销售市场正以每一年约6%的速率稳步增长。 英国占全世界销售市场的较大 市场份额,约为40%。除此之外,美企是嵌入技术性的关键参加者,别的关键的医疗技术销售市场包含欧州和日本。 "赢创在聚乳酸基聚合物行业具备领导干部影响力,它是大家开发设计生物研究原材料和解决方法的关键基本。"Karau 表述道。这类聚合物可转化成二氧化碳和水,其溶解時间在于分子结构构成、链长和晶粒大小。该聚合物将存有几个星期到好多个月的時间,保证骨骼或其他组织有充足的時间再造。 医疗器械生产商应用赢创医药健康业务流程线市场销售的RESOMER®聚合物,生产制造生物可消化吸收的骨螺丝、骨针和中小型板,关键用以手术缝合膝关节或肩部的韧带撕裂,及其固定不动手指头或脸部较小的骨骼。 但Karau 也提及:"现阶段这类原材料的抗压强度还不够,没法用以固定不动大中型、载重性骨骼。"因而,医疗器械新项目屋的科学研究工作人员正试着在生物降解聚合物中添加无机物化学物质,比如碳酸钙的衍生物。这类加上化学物质不但能提升原材料的抗压强度,还能提升其生物相溶性。"伴随着聚合物慢慢溶解,在其中的钙和聚磷酸盐将被消化吸收入新产生的成骨细胞中。"Karau 讲到。 除此之外,科学研究工作人员的企业愿景更为宏大。依靠适当的原材料,她们有希望选用三维打印为病人量身定做植入物。谢菲尔德的赢创科学研究工作人员的总体目标之一便是使生物生物降解聚合物适用这一生产工艺流程。 Karau 填补道:"大家的长期性总体目标是开发设计可以移殖体细胞的聚合物支撑架,打造出真实实际意义上的生物植入物。"这类方法将完成软骨组织再造,或是以身心健康机构替代损伤的心血管机构等。但科学研究工作人员务必最先寻找提升这种原材料生物相溶性的方式。 谢菲尔德的专家归属于赢创发展战略自主创新单位Creavis,她们与来源于医药健康和新型功能材料业务流程线的聚合物权威专家们密不可分协作。该新项目屋的精英团队已经进行生物相溶性塑胶的有关科学研究,运用于赢创VESTAKEEP 嵌入商品系列产品。现阶段,赢创医疗技术产品组合策略包含RESOMER 和VESTAKEEP 嵌入原材料,及其用以成形软管和相近运用的VESTAMID Care 聚酰胺树脂。 来源于:塑料新闻我国 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |
抱歉!该牌号暂无认证数据。
价格走势图
抱歉!该牌号暂无认证数据。
- 笔记本键盘膜
- 2019-08-09 0
- LEXAN™ EXL1132T resin聚碳酸酯(PC)硅氧烷共聚物树脂是一种具有额外释放性能的紫外线稳定透明注塑(IM)级树脂。与标准PC树脂相比,该树脂具有良好的低温(20 C)延展性、高流动性和良好的加工性,有机会缩短IM循环时间。LEXAN™ EXL1132T resin是一种通用产品,可提供透明和不透明的颜色,可能是广泛应用的最佳候选。
- 阅读全文
笔记本键盘膜
2-提供高度稳定的机械,电气,光学和热学性能
3-具有高流动特性,易于释放和优异的加工性能
4-具有高抗冲击性,出色的尺寸稳定性
5-具有良好的透明度。
6-耐化学性好,耐油性优良
2-熔体质量流动速率(300℃,1.20kg) 20 g/10min
3-弯曲模量(50 mm跨距) 2250 MPa
4-简支梁缺口冲击强度(23℃) 65 kJ/m²
5-热变形温度(1.8 MPa,未退火,64 mm跨距) 117 ℃
抱歉!暂无数据。