牌号简介 About |
---|
亲和力*pl 1881g聚烯烃塑性体(pop)是通过InSite*技术生产的。它是专为各种苛刻的包装应用,包括高速填表密封产品。优异的最终热粘强度、低温密封性、通过污染进行密封的能力、出色的光学性能符合:美国FDA FCN 424加拿大HPFB无异议(有限制)欧盟,2011年10月,详细信息请参考法规。 AFFINITY* PL 1881G Polyolefin Plastomer (POP) is produced via INSITE* Technology. It is designed for a variety of demanding packaging applications, including high-speed form-fill-seal products. Excellent ultimate hot tack strength Low temperature sealability Ability to seal through contamination Outstanding optics Complies with: U.S. FDA FCN 424 Canadian HPFB No Objection (with limitations) EU, No 10/2011 Consult the regulations for complete details. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.904 | g/cm³ | ASTM D792 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
1.0 | g/10min | ASTM D1238 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
摩擦系数 friction coefficient |
|||
与自身 - 动态 With oneself - dynamic |
0.15 | ASTM D1894 | |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
薄膜厚度 film thickness |
|||
测试 test |
51 | µm | |
膜刺穿强度 Membrane puncture strength |
|||
51 µm 51 µm |
8.09 | J | 内部方法 |
膜刺穿力 Membrane puncture force |
|||
51 µm 51 µm |
N | 内部方法 | |
膜耐刺穿性 Membrane puncture resistance |
|||
51 µm 51 µm |
J/cm³ | 内部方法 | |
割线模量 Secant modulus |
ASTM D882 | ||
2% 正割,MD:51 µm 2% secant, MD: 51 µ m |
MPa | ASTM D882 | |
2% 正割,TD:51 µm 2% secant, TD: 51 µ m |
MPa | ASTM D882 | |
拉伸强度 tensile strength |
ASTM D882 | ||
MD,屈服,51 µm MD, yield, 51 µ m |
MPa | ASTM D882 | |
TD,屈服,51 µm TD, yield, 51 µ m |
MPa | ASTM D882 | |
MD,断裂,51 µm MD, fracture, 51 µ m |
MPa | ASTM D882 | |
TD,断裂,51 µm TD, fracture, 51 µ m |
MPa | ASTM D882 | |
拉伸应变 Tensile strain |
ASTM D882 | ||
MD,断裂,51 µm MD, fracture, 51 µ m |
% | ASTM D882 | |
TD,断裂,51 µm TD, fracture, 51 µ m |
% | ASTM D882 | |
落锤冲击 Drop hammer impact |
|||
51 µm 51 µm |
g | ASTM D1709-B | |
埃尔曼多夫抗撕强度 Elmandorf tear strength 2 |
ASTM D1922 | ||
MD:51 µm MD:51 µm |
g | ASTM D1922 | |
TD:51 µm TD:51 µm |
g | ASTM D1922 | |
始封温度 Initial sealing temperature 3 |
|||
51 µm 51 µm 3 |
℃ | 内部方法 | |
阻塞力 Blocking force |
g | ASTM D3354-89 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 | |
熔融温度 Melting temperature |
|||
DSC DSC |
℃ | 内部方法 | |
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
光泽度 gloss |
|||
20°,50.8 µm 20°,50.8 µm |
ASTM D2457 | ||
透明度 transparency |
|||
50.8 µm 50.8 µm |
ASTM D1746 | ||
雾度 Haze |
|||
50.8 µm 50.8 µm |
% | ASTM D1003 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 改性过的矩形测件。 |
3 实现 2 磅/英寸 (8.8 N/25.4 mm) 热封强度的温度。 热封强度,Topwave HT 测试仪 0.5 S 保压,40 psi 压力,拉动速度 10 英寸/分(250 mm/秒)。 |
【新闻资讯】查看全部
2021中国汽车零部件行业发展现状与市场规模分析
2021-05-24 搜料网资讯: 汽车零部件作为汽车工业的基础,是支撑汽车工业持续健康发展的必要因素。特别是当前汽车行业正在轰轰烈烈、如火如荼开展的自主开发与创新,更需要一个强大的零部 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |