Elastollan 1180A是专为挤压型材、片材和薄膜应用而设计的。Elastollan 1180A具有优异的耐磨性、韧性、透明度、低温柔韧性、水解稳定性和抗真菌性。它具有优良的阻尼特性和优异的抗撕裂扩展性能。Elastollan 1180A在0.83mm壁厚的垂直火焰试验中被评定为UL-94HB。Elastollan 1180A还符合FDA食品接触部分第21册第177.2600节的要求。Elastollan 1180A还拥有NSF标准61“水接触材料”认证。Elastollan 1180A以色块或颗粒形式提供。 Elastollan® 1180A is specifically formulated for extruded profile, sheet and film applications. Elastollan® 1180A exhibits excellent abrasion resistance, toughness, transparency, very good low temperature flexibility, hydrolytic stability and fungus resistance. It has excellent damping characteristics and outstanding resistance to tear propagation. Elastollan® 1180A is rated UL-94 HB in vertical flame test for wall thickness of 0.83 mm. Elastollan® 1180A also conforms to the FDA food contact section, book 21, section 177.2600. Elastollan® 1180A also has NSF Standard 61 "Water Contact Material" certification. Elastollan® 1180A is supplied uncolored in diced or pelletized form. |
产品描述 Product Description
厂家:德国巴斯夫 BASF
类别:TPU-醚 TPU-醚
颜色:清晰/透明
加工条件:注射成型 Injection Molding
性能特点: 防火阻燃等级HB; 耐低温柔性; 耐磨; 机械强度好-撕裂; 耐水解; 细菌阻隔; 食品接触; 韧性好; Good flexibility,Hydrolysis stability,Antimicrobial properties,Food contact compliance,Low temperature toughness,Good tear strength,Good wear resistance,HB
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.11 | g/cm³ | ASTM D792 |
熔体质量流动速率 Melt Flow Rate |
ASTM D1238 | ||
190℃,21.6kg 190℃,21.6kg |
20 to 50 | g/10min | ASTM D1238 |
190℃,8.70kg 190℃,8.70kg |
10 to 20 | g/10min | ASTM D1238 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 A Shaw's A |
80 | ASTM D2240 | |
拉伸模量 Tensile modulus |
|||
注塑成型 injection molding |
12.4 | MPa | ASTM D412 |
弯曲模量 Bending modulus |
|||
注塑成型 injection molding |
MPa | ASTM D790 | |
泰伯耐磨性 Taber abraser |
mg | ASTM D1044 | |
Abrasion(DIN) Abrasion(DIN) |
mm³ | DIN 53516 | |
弹性体 elastic body |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
MPa | ASTM D412 | |
300% 应变 300% strain |
MPa | ASTM D412 | |
100% 应变 100% strain |
MPa | ASTM D412 | |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ASTM D412 | |
撕裂强度 tear strength 2 |
kN/m | ASTM D624 | |
压缩形变 Compression deformation |
ASTM D395B | ||
23℃,22 hr 23℃,22 hr |
% | ASTM D395B | |
70℃,22 hr 70℃,22 hr |
% | ASTM D395B | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
玻璃化转变温度 Glass transition temperature |
℃ | 内部方法 | |
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 | |
软化温度 Softening temperature |
|||
DMA DMA |
℃ | Internal Method | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
0.80 mm 0.80 mm |
UL 94 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 C 模具 |
【新闻资讯】查看全部
宁夏成功破解锰渣处理世界性难题
2021-10-17 搜料网资讯: 日前,宁夏天元锰业集团50万吨/年锰渣脱硫烟气制硫酸项目点火成功。 这是国内首个锰渣脱硫烟气制硫酸项目,为锰渣处理这一世界性难题提供了新的破解路径。 该项目 |
宁夏成功破解锰渣处理世界性难题 搜料网资讯:日前,宁夏天元锰业集团50万吨/年锰渣脱硫烟气制硫酸项目点火成功。这是国内首个锰渣脱硫烟气制硫酸项目,为锰渣处理这一世界性难题提供了新的破解路径。
该项目按照循环经济的发展理念,利用回转窑煅烧废渣过程中产生的烟气生产硫酸和氨水,总投资11.56亿元,建成后可年处理锰渣220万吨,生产脱硫锰渣100万吨,年产硫酸80万吨、氨水约10万方。生产的脱硫锰渣即可制作成马路砖、墙体材料等水泥制品,也可作为商砼骨料,避免了废渣对环境造成污染的风险;100%回收锰渣中的硫酸、氨水,回用于电解锰生产系统,节省了生产经营成本,提高了企业市场竞争力。 此项新工艺、新技术首开行业先河,成功破解了废渣和含硫烟气的处理难题,使其变废为宝、综合利用,彻底改变了传统电解锰生产工艺路线,延伸了电解锰产业链,实现了资源循环利用。通过综合利用锰渣,既创建了全新的工艺模式,提高了企业效益,又减少了因传统堆存处置方式给环境带来的不利影响,在电解锰生产领域产生深远而重大的积极影响,为工业固废循环利用再创新途径。(李红生 王文丽) |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |
价格走势图
开始时间:
结束时间:
材料厂家:
【牌号齐全,内容全面】
全网共2500+项牌号+上游原料单体+原油价格,最长可追溯近20年价格行情
【精准,及时,权威!】
专业团队挖掘行情信息,第一时间发布行情
抱歉!该牌号暂无认证数据。
免责声明:参考价格是搜料网根据网络大数据拟合分析的结果,仅供参考。实际成交价取决但不限于以下因素:下单时间,付款方式,交货方式,数量,税费,色号,产地,项目信息。
抱歉!暂无数据。
抱歉!暂无数据。