牌号简介 About |
---|
HM-8355(BL4)是以1-丁烯为共聚单体的高密度聚乙烯,适用于大型容器。它是一种高摩尔质量,易于加工,高刚度强度,良好的抗应力开裂性和很好的成型表面光洁度等级的树脂。具有摩尔质量高、易加工、刚度强度高、抗应力开裂、成型表面光洁度好等特点。应用杰里可以通用级大容器(体积约。1-500点燃 HM-8355(BL4) is a high density polyethylenee with 1-Butene as co monomer with general purpose grade for large containers. It is a high molar mass, easily processable, high stiffness strength, good stress cracking resistance and very good molding surface finish grade resin. Features High molar mass, easily processable high stiffness strength, good stress Cracking resistance and very good molding surface finish. Applications Jerry can General purpose grade for large container (volume aprox. 1-500 lit) |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.951 | g/cm³ | ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
ISO 1133 | ||
190℃,21.6kg 190℃,21.6kg |
9.5 | g/10min | ISO 1133 |
190℃,5.0kg 190℃,5.0kg |
0.35 | g/10min | ISO 1133 |
Flow Rate Ratio(21.6/5) Flow Rate Ratio(21.6/5) |
27.0 | ||
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
|||
23℃,模压成型 23 ℃, molded |
10 | kJ/m² | ISO 179/1eA |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
Swelling Ratio Swelling Ratio |
% |
备注 | |||
---|---|---|---|
暂无数据 |
【新闻资讯】查看全部
神马股份拟3亿元设立全资子公司,建设年产5万吨己二腈项目
2020-11-15 搜料网资讯: 11月13日丨神马股份(600810.SH)公布,公司拟在河南省平顶山市尼龙新材料产业集聚区设立全资子公司河南神马祥龙化工有限责任公司(以工商登记机关核准名称为准),建设年 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |