牌号简介 About |
---|
NANCAR® 1204D是由100份NBR、60份PVC和120份DEHP组成的熔剂混合物。这种聚合物具有足够的稳定剂,可以在正常老化条件下使用,并且可以通过正常的混合程序进行加工。它具有很好的挤出加工性能,使产品表面光滑。NANCAR® 1204D在低硬度应用和耐磨、耐臭氧、耐油和耐燃油方面表现出色。建议用于低硬度的印版和卷筒。 NANCAR® 1204D is a fluxed blend of 100 parts NBR, 60 parts PVC and 120 parts DEHP. This polymer has sufficient stabilizer for normal aging conditions and can be processed with normal mixing procedures. It has good processability for extrusion, providing smooth surfaces on the resultant product. NANCAR® 1204D is excellent in low hardness application and resistance to abrasion, ozone, oil and fuel. It is suggested to be use in low hardness printing plates and rolls. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
门尼粘度 Mooney viscosity |
|||
ML 1+4,100℃ ML 1+4,100℃ |
29 | MU | ASTM D1646 |
丙烯腈含量(Bound) Acrylonitrile content (Bound) |
33.0 | % | 内部方法 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 A Shaw's A |
68 | ||
弹性体 elastic body |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
|||
屈服 yield |
14.3 | MPa | |
拉伸应变 Tensile strain |
|||
断裂 fracture |
460 | % | |
压缩形变 Compression deformation |
|||
100℃,70 hr 100℃,70 hr |
% | ||
老化性能 Aging performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
空气中拉伸强度的变化率 The rate of change in tensile strength in air |
|||
100℃,70 hr 100℃,70 hr |
% | ||
空气中极限伸长率的变化率 The rate of change in ultimate elongation in air |
|||
100℃,70 hr 100℃,70 hr |
% | ||
空气中硬度计硬度的变化率 The rate of change in hardness of a hardness tester in the air |
|||
100℃,70 hr 100℃,70 hr |
|||
拉伸强度的变化率 The rate of change in tensile strength |
|||
100℃,70 hr,在ASTM #1油中 100 ℃, 70 hr, in ASTM # 1 oil |
% | ||
100℃,70 hr,在IRM 903油中 100 ℃, 70 hr, in IRM 903 oil |
% | ||
极限伸长率的变化率 Change rate of ultimate elongation |
|||
100℃,70 hr,在ASTM #1油中 100 ℃, 70 hr, in ASTM # 1 oil |
% | ||
100℃,70 hr,在IRM 903油中 100 ℃, 70 hr, in IRM 903 oil |
% | ||
邵氏硬度的变化率 The rate of change in Shore hardness |
|||
支撐 A,100℃,70 hr,在ASTM #1油中 Support A, 100 ℃, 70 hr, in ASTM # 1 oil |
|||
支撐 A,100℃,70 hr,在IRM 903油中 Support A, 100 ℃, 70 hr, in IRM 903 oil |
|||
体积变化 Volume change |
|||
100℃,70 hr,ASTM 标准油(1号) 100 ℃, 70 hr, ASTM standard oil (No.1) |
% | ||
100℃,70 hr,在IRM 903油中 100 ℃, 70 hr, in IRM 903 oil |
% | ||
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热损耗 Heat loss |
% | ASTM D5688 | |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
耐臭氧性 Ozone resistance 2 |
|||
50 pphm X 40℃ X 20% 50 pphm X 40℃ X 20% 2 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 at 24 hrs, 48 hrs, 72 hrs, 96 hrs, 168 hrs |
【新闻资讯】查看全部
即刻生效!15省市启动停电计划,大厂生产中断!原料大涨8000元/吨!
2021-08-04 搜料网资讯: 电力负荷过高!15省启动停电计划! 高温天气持续,据国家电网数据显示,7月份全国的用电负荷及日均发电量都已突破去年夏季最高峰!2021年上半年工业用电量同比增长 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |