牌号简介 About |
---|
Promyde® B20 P是一种热稳定、成核和润滑的聚酰胺6。特点Promyde® B20 P是一种聚酰胺6热稳定,润滑和成核快速循环和技术注射成型。它的主要特点是易于流动,易于模具填充和非常快的冷却时间,同时保持良好的聚酰胺6机械性能。应用由于其易于流动的特点和非常快的冷却时间;Promyde® B20 P提供了显著的生产力提高。Promyde® B20 P模具填充速度比标准粘度的聚酰胺6快35%,再加上其优异的机械和热性能,使其适用于汽车、电气、电子、窗帘系统等部件的高速多腔注塑成型,也适用于SINGL生产的大型技术部件。E型腔模具。 Promyde® B20 P is a Polyamide 6 heat stabilised, nucleated and lubricated. CHARACTERISTICS Promyde B20 P is a polyamide 6 heat stabilized, lubricated and nucleated for fast cycle and technical injection moulding. Its main characteristics are easy flowing, easy mould filling and very fast cooling time whilst maintaining excellent polyamide 6 mechanical properties. APPLICATIONS Due to its easy flow characteristics and very fast cooling time; Promyde B20 P provides significant productivity improvement. Promyde B20 P mould filling is 35 % faster than standard viscosity polyamide 6; that combined with its excellent mechanical and thermal properties make it suitable for high speed multi cavity injection moulding for parts such as components used in automotive, electrical, electronics, curtain systems, and also for large technical parts produced in single cavity moulds. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.13 | g/cm³ | ISO 1183 |
粘数 viscosity number |
125 | cm³/g | ISO 307 |
吸水率 Water Absorption |
3 | % | ISO 62 |
吸湿性 Moisture Absorption |
9.5 | % | ISO 62 |
熔体体积流动速率 Melt Volume Rate |
|||
275℃,5kg 275℃,5kg |
226 | cm³/10min | ISO 1133 |
成型收缩率 Molding Shrinkage |
|||
纵向 longitudinal |
% | ISO 294-4 | |
横向 transversal |
% | ISO 294-4 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame Class Rating |
|||
1.5 mm 1.5 mm |
UL 94 | ||
灼热丝可燃性指数 Glow Wire Flammability Index(GWFI) |
|||
1.5 mm 1.5 mm |
℃ | IEC 60695-2-12 | |
灼热丝起燃温度 Glow Wire Ignitability Temperature(GWIT) |
|||
1.5 mm 1.5 mm |
℃ | IEC 60695-2-13 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile Modulus |
|||
干燥 dry |
MPa | ISO 527 | |
湿润 cond. |
MPa | ISO 527 | |
拉伸强度 Tensile Strength |
|||
干燥 dry |
MPa | ISO 527-2 | |
湿润 cond. |
MPa | ISO 527-2 | |
拉伸伸长率 Tensile Elongation |
|||
屈服,干燥 yld,dry |
% | ISO 527 | |
屈服,湿润 yld,cond. |
% | ISO 527 | |
断裂伸长率 Elongation at Break |
|||
干燥 dry |
% | ISO 527-1,2 | |
湿润 cond. |
% | ISO 527-1,2 | |
弯曲模量 Flexural Modulus |
|||
干燥 dry |
MPa | ISO 178 | |
湿润 cond. |
MPa | ISO 178 | |
弯曲强度 Flexural Strength |
|||
干燥 dry |
MPa | ISO 178 | |
湿润 cond. |
MPa | ISO 178 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁无缺口冲击强度 Charpy Unnotched Impact strength |
|||
23℃,干燥 23℃,dry |
kJ/m² | ISO 179/1eU | |
23℃,湿润 23℃,cond. |
kJ/m² | ISO 179/1eU | |
-30℃ -30℃ |
kJ/m² | ISO 179/1eU | |
简支梁缺口冲击强度 Charpy notched Impact strength |
|||
23℃,干燥 23℃,dry |
kJ/m² | ISO 179/1eA | |
23℃,湿润 23℃,cond. |
kJ/m² | ISO 179/1eA | |
-30℃ -30℃ |
kJ/m² | ISO 179/1eA | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
熔融温度 Melting temperature |
℃ | ISO 3146 | |
热变形温度 HDT |
|||
1.8 MPa 1.8 MPa |
℃ | ISO 75-1/-2 | |
0.45 MPa 0.45 MPa |
℃ | ISO 75-1/-2 | |
线性热膨胀系数 Coeff.of linear therm expansion |
|||
23-80℃ long. 23-80℃ long. |
×10-4/K | ISO 11359-2 | |
23-80ºC transv. 23-80ºC transv. |
×10-4/K | ISO 11359-2 | |
电气性能 ELECTRICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
介电常数 Dielectric Constant |
|||
干燥 dry |
IEC 60250 | ||
湿润 cond. |
IEC 60250 | ||
耗散因数 Dissipation Factor |
|||
干燥 dry |
IEC 60250 | ||
湿润 cond. |
IEC 60250 | ||
体积电阻率 Volume Resistivity |
|||
干燥 dry |
ohm·m | IEC 60093 | |
湿润 cond. |
ohm·m | IEC 60093 | |
表面电阻率 Surface Resistivity |
|||
干燥 dry |
ohm | IEC 60093 | |
湿润 cond. |
ohm | IEC 60093 | |
相比漏电起痕指数 Comparative Tracking Index |
IEC 60112 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 0.079 in/min |
3 10°C/min |
【新闻资讯】查看全部
“银十”新能源车销量同比翻倍
2020-11-10 搜料网资讯: 昨天,全国乘联会发布了10月乘用车市场销售数据。银十车市继续复苏,乘用车市场零售达到199.2万辆,同比去年10月增长8.0%,实现了连续4个月8%左右的近两年高位增速。值 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |