牌号简介 About |
---|
iRogran A92E 4860是一种高性能聚酯基热塑性聚氨酯,用于挤出和注塑成型应用。iRogran A92E 4860是亨斯迈技术挤压产品系列的一部分,提供了一种特殊设计的柔性材料,具有广泛的加工窗口,适用于制备螺旋管、气动管、皮带和技术模具。性能特点:高拉伸强度、优异的磨损性能、优异的耐水解性、良好的低温柔韧性。 IROGRAN A92E 4860 is a high performance polyester based thermoplastic polyurethane intended for extrusion and injection moulding applications. IROGRAN A92E 4860 is part of the HUNTSMAN technical extrusion product range and offers a specially designed, flexible material with a broad processing window particularly suitable for the preparation of spiral tubing, pneumatic tubing, belting and technical mouldings. PERFORMANCE FEATURES High tensile strength Excellent wear performance Excellent hydrolysis resistance Good low temperature flexibility |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density 2 |
1.20 | g/cm³ | ASTM D792 |
密度 Density 3 |
1.20 | g/cm³ | DIN 53479 |
熔体体积流动速率 Melt Volume Rate |
|||
210℃,10 kg 210℃,10 kg |
33.0 | cm³/10min | |
收缩率 Shrinkage rate |
|||
MD:注塑成型 MD: Injection molding |
0.90 | % | ASTM D955 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
DIN 53505 | ||
邵氏 A,注塑成型 Shaw A, injection molding |
91 | DIN 53505 | |
邵氏 D,注塑成型 Shaw's D, injection molding |
DIN 53505 | ||
邵氏硬度 Shore hardness |
ASTM D2240 | ||
邵氏 A,注塑成型 Shaw A, injection molding |
ASTM D2240 | ||
邵氏 D,注塑成型 Shaw's D, injection molding |
ASTM D2240 | ||
Abrasion Abrasion 2 |
mm³ | DIN 53516 | |
弹性体 elastic body |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength 2 |
|||
断裂 fracture 2 |
MPa | ASTM D412 | |
断裂 fracture 2 |
MPa | DIN 53504 | |
300% 应变 300% strain 2 |
MPa | DIN 53504 | |
300% 应变 300% strain 2 |
MPa | ASTM D412 | |
100% 应变 100% strain 2 |
MPa | ASTM D412 | |
100% 应变 100% strain 2 |
MPa | DIN 53504 | |
拉伸应变 Tensile strain 2 |
|||
断裂 fracture 2 |
% | ASTM D412 | |
断裂 fracture 2 |
% | DIN 53504 | |
撕裂强度 tear strength 2 |
kN/m | ASTM D624 | |
撕裂强度 tear strength 2 |
kN/m | ISO 34-1 | |
压缩形变 Compression deformation 2 |
ASTM D395 | ||
23℃,24 hr 23℃,24 hr |
% | ASTM D395 | |
70℃,24 hr 70℃,24 hr |
% | ASTM D395 | |
压缩形变 Compression deformation 2 |
ISO 815 | ||
23℃,24 hr 23℃,24 hr |
% | ISO 815 | |
70℃,24 hr 70℃,24 hr |
% | ISO 815 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
TMA TMA 3 |
Internal Method | ||
Low-High:635.0 µm Low-High:635.0 µm |
℃ | Internal Method | |
Peak:635.0 µm Peak:635.0 µm |
℃ | Internal Method |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 Injection Molded |
3 Extruded Film |
【新闻资讯】查看全部
0.5秒造一个口罩,为什么你如今还是买不到?
2020-02-12 新冠肺炎疫情 突然 爆发 不仅湖北各大医院寻求防护物资 全国多地也纷纷口罩库存告急 买不到口罩一时间成了热门话题 口罩,以前觉得可有可无 如今却成了炙手可热的硬通货 小小薄 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |