| 牌号简介 About |
|---|
| Y910A是一种用于拉伸纱线的高密度聚乙烯树脂。该等级设计用于在常规挤压拉伸设备中加工。 Description Y910A is a high-density polyethylene resins for stretched yarn applications. This grade is designed to be processed in conventional extrusion stretching equipment. Characteristics Y910A offers excellent processability and thermal stability during extrusion process. Good stretchability during hot press stretching allows high production speed with this grade. Stretched yarn products made from this grade offer high tensile strength and abrasion resistance. Applications Flat Yarn (T-DIE) Mono-filaments for fishing net and Ropes Flat yarn woven bag, Tarpaulin, Sacks Major Property Requirements Low gel/fish-eye material Good processability Good stretchability at the stretching stage Good mechanical strength and abrasion resistance High environmental stress crack resistance |
产品描述 Product Description
用途：网织品;绳索;袋子;渔业应用;单丝;单色高韧性线;
加工条件：挤出 Extrusion
性能特点： 拉伸性能好; 耐磨; 热稳定性好; 低速凝固晶点; 高密度; 抗应力开裂; 易加工; Excellent Processability,Low speed solidification point,Good Tensile Strength,Good wear resistance,High density,Heat Stabilized,High ESCR
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
0.956 | g/cm³ | ASTM D1505 |
|
熔体质量流动速率 Melt Flow Rate |
|||
|
190℃，2.16kg 190℃，2.16kg |
0.90 | g/10min | ASTM D1238 |
|
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
200 | J/m | ASTM D256 |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
维卡软化温度 Vicat Softening Temp |
125 | ℃ | ASTM D1525 2 |
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
洛氏硬度 Rockwell hardness |
|||
|
R 级 R-level |
50 | ASTM D785 | |
|
拉伸强度 tensile strength |
ASTM D638 | ||
|
屈服 yield |
MPa | ASTM D638 | |
|
断裂 fracture |
MPa | ASTM D638 | |
|
拉伸应变 Tensile strain |
|||
|
断裂 fracture |
% | ASTM D638 | |
|
弯曲模量 Bending modulus |
|||
|
23℃ 23℃ |
MPa | ASTM D747 | |
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
| 2 压 力1 (10N) |
|
【新闻资讯】查看全部
阿科玛向SKC株式会社无限公司授权多层构造薄膜技术
2018-05-25 多年来，阿科玛是多层结构PVDF薄膜相关专利技术的唯一拥有者，该多层结构的PVDF薄膜基于阿科玛的旗舰产品Kynar®PVDF树脂。经过一系列的测试评估，现阿科玛宣布SKC生产的薄膜产品(名为FW3B)与阿科玛的Kynar®302 PGM-TR薄膜性能相当，并已授权许可SKC生产该结构的薄膜产品并在光伏背板市场销售。 此外，阿科玛授权的光伏背板制造商将其高性能背板特别标注为KPK®结构。KPK®是阿科玛公司的注册商标，特指中间为PET阻隔层、两边为Kynar®302 PGM |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付