牌号简介 About |
---|
LNP Thermocomp 2F005是一种含25%玻璃纤维的含氟聚合物。也称为:lnp*Thermocomp*化合物fp-ef-1005产品重新订购名称:2f005 LNP THERMOCOMP 2F005 is a fluoropolymer compound based on ETFE containing 25% Glass Fiber. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.87 | g/cm³ | ASTM D792 |
收缩率 Shrinkage rate |
|||
TD:24 hrs TD:24 hrs |
2.0 to 4.0 | % | ASTM D955 |
MD:24 hrs MD:24 hrs |
1.0 to 3.0 | % | ASTM D955 |
吸水率 Water absorption rate |
|||
平衡,23℃,50% RH Equilibrium, 23 ℃, 50% RH |
0.020 | % | ISO 62 |
24hr,50% RH 24hr,50% RH |
0.010 | % | ASTM D570 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus 2 |
MPa | ASTM D638 | |
拉伸模量 Tensile modulus |
MPa | ISO 527-1-2 | |
拉伸强度 tensile strength 3 |
|||
断裂 fracture 3 |
MPa | ASTM D638 | |
断裂 fracture |
MPa | ISO 527-2/5 | |
屈服 yield |
MPa | ISO 527-2/5 | |
屈服 yield 3 |
MPa | ASTM D638 | |
拉伸应变 Tensile strain 3 |
|||
断裂 fracture |
% | ISO 527-2/5 | |
断裂 fracture 4 |
% | ASTM D638 | |
屈服 yield |
% | ISO 527-2/5 | |
屈服 yield 3 |
% | ASTM D638 | |
弯曲模量 Bending modulus 5 |
MPa | ISO 178 | |
50 mm跨距 50 mm span 4 |
MPa | ASTM D790 | |
弯曲强度 bending strength |
MPa | ISO 178 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
23℃ 23℃ |
J/m | ASTM D256 | |
23℃ 23℃ 6 |
kJ/m² | ISO 180-1A | |
23℃ 23℃ |
J/m | ASTM D4812 | |
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam 5 |
|||
23℃ 23℃ 5 |
kJ/m² | ISO 180/1U | |
装有测量仪表的落镖冲击 Dart impact equipped with measuring instruments |
|||
23℃,Total Energy 23℃,Total Energy |
J | ASTM D3763 | |
多轴向仪器化冲击能量 Multi axial instrumented impact energy |
J | ISO 6603-2 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火,64 mm跨距 1.8 MPa, unannealed, 64 mm span 7 |
℃ | ISO 75-2/Af | |
1.8 MPa,未退火,3.2 mm 1.8 MPa, unannealed, 3.2 mm |
℃ | ASTM D648 | |
0.45 MPa,未退火,64 mm跨距 0.45 MPa, unannealed, 64 mm span 7 |
℃ | ISO 75-2/Bf | |
0.45 MPa,未退火,3.2 mm 0.45 MPa, unannealed, 3.2 mm |
℃ | ASTM D648 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
TD:-30~30℃ TD:-30~30℃ |
1/℃ | ASTM D696 | |
MD:-30~30℃ MD:-30~30℃ |
1/℃ | ASTM D696 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 2.0 in/min |
3 类型 1, 0.20 in/min |
4 0.051 in/min |
5 0.079 in/min |
6 80*10*4 |
7 80*10*4 mm |
【新闻资讯】查看全部
科思创一季度净利增长58%
2016-04-28 路透社报道,科思创第一季度核心盈利增长了22%,因为较低的原料价对冲了它聚碳酸酯塑料和泡沫化学产品价格的下跌。 税息折旧及摊销前利润(EBITDA),增长了5.08亿欧(5.7094亿美元),同时还有3千万欧元的保险理赔。 这个数字比路透社预测的平均值4.37亿欧要高出不少。 还透漏对他们2016年销量的预测,包括主要产品个位数的百分比增长,流动资金不会有大变动但比往年平均数据要高。 科思创属拜耳内部独立的分支。他主要生产和研 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |