一种黑色高密度聚乙烯(HDPE)化合物,分类为PE100。含>2.2%分散性好的A1级碳黑,具有优异的耐候性,具有很高的拉伸强度和抗快速、缓慢裂纹扩展的能力。添加的炭黑由于粒径小,尽管具有吸湿性,但对水分的敏感性较低。在整个温度范围内,它还表现出很高的抗冲击性,加上对断裂的急性抵抗力,这在温度很低的应用中是一个显著的优势,因此它可以在-50°C到60°C的温度范围内使用。安全MP6004-100被归类为无危险材料。我们建议您遵守我们的材料安全数据表中的安全指南和建议。典型应用MP6004-100由符合ASTM D3035要求的高密度聚乙烯(HDPE)树脂制成,满足ASTM D2837对静水压设计基础的要求。MP6004-100推荐用于饮用水压力管道、采矿管道、工业管道、污水管道和波纹管等应用领域的管道系统。 A black high density polyethylene (HDPE) compound classified as PE100. It contains >2.2% well dispersed carbon black class A1 to ensure outstanding weather resistance, provides high tensile strength with high resistance against fast and slow crack propagation. The added carbon black type is less sensitive to moisture despite the hygroscopic behavior due to its fine particle size. It also shows a very high impact resistance throughout its entire temperature range combined with an acute resistance to fracture which is a significant advantage in applications where temperature is very low so it can be used at temperatures ranging from -50°C to 60°C. Safety MP6004-100 is classified as no-dangerous material. We advise you to follow our safety guidelines and recommendations in our Material Safety Data Sheet. Typical Applications MP6004-100 is manufactured from high density polyethylene (HDPE) resin meeting the requirements of ASTM D3035, it fulfills the requirements of ASTM D2837 for hydrostatic design basis. MP6004-100 is recommended for pipe systems in the applications field of drinking water pressure pipes, mining pipe, industrial pipes, sewage pipes and corrugated pipes. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density 2 |
0.960 | g/cm³ | ASTM D792 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,5.0kg 190℃,5.0kg |
0.40 | g/10min | ASTM D1238 |
抗环境应力开裂 ESCR(Environmental Stress Cracking Resistance) |
|||
10%非离子洗涤剂,F50 10% non-ionic detergent, F50 |
> 5000 | hr | ASTM D1693 |
炭黑含量 Carbon black content |
> 2.2 | % | ASTM D1603 |
Carbon Black Dispersion Carbon Black Dispersion |
A1 | ISO 18553 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
|||
23℃ 23℃ |
kJ/m² | ASTM D256 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 | |
熔融温度 Melting temperature |
℃ | ASTM D2117 | |
氧感应时间 Oxygen sensing time |
|||
200℃ 200℃ |
min | ASTM D3895 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 D Shaw's D |
ASTM D2240 | ||
拉伸强度 tensile strength |
ASTM D638 | ||
屈服 yield |
MPa | ASTM D638 | |
断裂 fracture |
MPa | ASTM D638 | |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ASTM D638 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 23°C |
【新闻资讯】查看全部
南京部分化工企业开端强迫性限产、停产!
2017-05-22 首届江苏发展大会定于5月20日在南京召开。大会由江苏省委、省政府主办,每两至三年举办一次,旨在增进与海内外江苏籍和在江苏学习、工作过的各领域知名人士的联系、交流和合作。 为切实保障江苏省发展大会期间南京市环境空气质量优良,南京市政府办公厅发文称,5月17日起全市重点石化、化工、钢铁等企业按照二氧化硫、氮氧化物、烟尘及挥发性有机物等各项污染物排放减少50%以上的要求,实施限产或阶段性停产方案。 市政府办公厅关于切实做好江苏发展大会 环境空气质量 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |