牌号简介 About |
---|
建议在需要高冲击强度的注塑工艺中使用repol c080mt。它是制造电池容器、汽车和工业产品的理想材料。repol c080mt包含汽车发动机罩下应用所需的长期热稳定装置。 Repol C080MT is recommended for use in Injection Moulding processes where high impact strength is required. It is an ideal material to use in making battery containers, automotive and industrial products. Repol C080MT contains long term heat stabiliser as required for under-the-hood applications in automotive. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
熔体质量流动速率 Melt Flow Rate |
|||
230℃,2.16kg 230℃,2.16kg |
11 | g/10min | ASTM D1238 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength 2 |
|||
屈服,注塑成型 Yield, injection molding 2 |
23.0 | MPa | ASTM D638 |
拉伸应变 Tensile strain 2 |
|||
屈服,注塑成型 Yield, injection molding 2 |
7.0 | % | ASTM D638 |
弯曲模量 Bending modulus |
|||
1% 正割,注塑成型 1% cut, injection molding |
1050 | MPa | ASTM D790-A |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
23℃,注塑成型 23 ℃, injection molding |
100 | J/m | ASTM D256 |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
0.45 MPa,未退火,注塑成型 0.45 MPa, unannealed, injection molded |
℃ | ASTM D648 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 类型 1, 2.0 in/min |
【新闻资讯】查看全部
丙烯市场多种生产工艺:甲醇制烯烃相对优势?
2015-11-27 随着全球经济的飞速发展,化工行业发展迅猛,世界各国对重要的石化原料丙烯的需求迅速增长。市场分析师表示,目前我国丙烯生产工艺三分天下,除了近几年迅速兴起的丙烷脱氢和煤制烯烃等新兴生产工艺之外,催化裂化和蒸汽裂解等传统工艺依然是目前我国丙烯最主要的来源,而丙烯作为重要的化工原料,其装置也是备受市场关注的。 油制丙烯:主要是副产品 油制丙烯属于老牌工艺,也是目前丙烯产能产量占比最多的,分为蒸汽热裂解和催化裂化两种,其中的相同点是丙 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |