公司信息及水印
牌号简介 About |
---|
高性能热塑性材料,30%碳纤维增强聚醚酮醚酮酮(PEKEKK),半结晶,注射成型颗粒,标准流程,颜色为黑色。在静态或动态系统中用于高温下更高强度和刚度的应用。耐磨性好,摩擦系数低,热膨胀系数低。抗腐蚀环境的化学反应。 High performance thermoplastic material, 30% carbon fibre reinforced PolyEtherKetoneEtherKetoneKetone (PEKEKK), semi crystalline, granules for injection moulding, standard flow, colour black. Applications for higher strength and stiffness at elevated temperatures in a static or dynamic system. Excellent wear resistance, low coefficient of friction, low coefficient of thermal expansion. Chemically resistant to aggressive environments. |
技术参数 Technical Data | |||
---|---|---|---|
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy notched Impact strength Charpy Notched Impact Strength |
|||
23℃ 23℃ |
7.0 | kJ/m² | ISO 179/1eA |
简支梁无缺口冲击强度 Charpy Unnotched Impact strength Charpy Unnotch Impact strength |
|||
23℃ 23℃ |
50 | kJ/m² | ISO 179/1U |
悬臂梁缺口冲击强度 Izod Notched Impact strength Izod Notched Impact strength |
|||
23℃ 23℃ |
9.0 | kJ/m² | ISO 180-A |
悬臂梁无缺口冲击强度 Izod Unnotched Impact strength Izod Unnotched Impact strength of cantilever beam |
|||
23℃ 23℃ |
50 | kJ/m² | ISO 180 |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 HDT Hot deformation temperature HDT |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
383 | ℃ | ISO 75-2/Af |
玻璃化转变温度 Glass Transition Temperature Glass Transition Temperature |
℃ | ISO 11357-2 | |
熔融温度 Melting temperature Melting temperature |
℃ | ISO 11357-3 | |
线性热膨胀系数 Coeff.of linear therm expansion Coeff. of linear thermal expansion |
ISO 11359-2 | ||
MD:< 162℃ MD:< 162℃ |
1/℃ | ||
MD:> 162℃ MD:> 162℃ |
1/℃ | ||
TD:< 162℃ TD:< 162℃ |
1/℃ | ||
TD:> 162℃ TD:> 162℃ |
1/℃ | ||
导热系数 Thermal Conductivity Thermal conductivity |
|||
23℃ 23℃ |
W/m/K | ISO 22007-4 | |
电气性能 ELECTRICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
体积电阻率 Volume Resistivity Volume Resistance |
|||
23℃ 23℃ |
ohms·cm | ASTM D4496 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness Shore hardness |
|||
邵氏 D,23℃ Shore D, 23 ℃ |
ISO 868 | ||
拉伸模量 Tensile Modulus Tensile Modulus |
|||
23℃ 23℃ |
MPa | ISO 527-2 | |
拉伸强度 Tensile Strength Tensile Strength |
ISO 527-2 | ||
断裂 brk,23℃ Broken BRK, 23 ℃ |
MPa | ||
断裂 brk,125℃ Broken BRK, 125 ℃ |
MPa | ||
断裂 brk,175℃ Broken BRK, 175 ℃ |
MPa | ||
断裂 brk,275℃ Broken BRK, 275 ℃ |
MPa | ||
拉伸应变 Tensile Strain Tensile Strain |
|||
断裂 brk,23℃ Broken BRK, 23 ℃ |
% | ISO 527-2 | |
弯曲模量 Flexural Modulus Flexural Modulus |
|||
23℃ 23℃ |
MPa | ISO 178 | |
弯曲强度 Flexural Strength Flexural Strength |
ISO 178 | ||
23℃ 23℃ |
MPa | ||
125℃ 125℃ |
MPa | ||
175℃ 175℃ |
MPa | ||
275℃ 275℃ |
MPa | ||
压缩强度 Compressive Strength Compressive Strength |
ISO 604 | ||
23℃ 23℃ |
MPa | ||
120℃ 120℃ |
MPa | ||
200℃ 200℃ |
MPa | ||
250℃ 250℃ |
MPa | ||
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density Density |
g/cm³ | ISO 1183 | |
螺旋流动长度 spiral flow length Spiral flow length |
内部方法 | ||
-- -- |
cm | ||
-- -- |
cm | ||
成型收缩率 Molding Shrinkage Molding shrinkage |
ISO 294-4 | ||
TD TD |
% | ||
MD MD |
% | ||
表观粘度 Apparent viscosity Apparent viscosity |
|||
420℃ 420℃ |
Pa·s | ISO 11443 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 Crystalline |
3 模具温度: 410°F, 熔体温度: 779°F |
4 1 mm |
5 3 mm |
6 415°C nozzle, 210°C tool |
7 Onset |
8 Midpoint |
9 Average |
10 Along flow |
11 1V |
【新闻资讯】查看全部
经济增长放缓担忧施压 原油期货集体收跌
2021-09-10 搜料网资讯: 北京时间10日凌晨,对全球经济增长放缓的担忧使油价承压,原油期货周四集体收跌。 纽约商品交易所10月份交割的西德克萨斯中质原油(WTI)下跌1.16美元,跌幅1.7%,收 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |