牌号简介 About |
---|
明矾是一种金属灰色、铝填充的聚酰胺12粉末,具有高硬度、金属外观和良好的后处理可能性。由明矾制成的激光烧结零件具有优良的材料性能:具有良好的尺寸精度、密度和刚度的平衡比、提高的热导率、良好的可加工性。明矾零件的表面可以很容易地通过研磨、抛光或涂层进行精整。通过铝填充料的切削破坏效应,简化了铝激光烧结件的加工。铝的典型应用是制造金属外观的硬零件,用于汽车制造(例如风洞试验或与安全无关的零件)、注射和成型小型生产运行的工具嵌件、说明模型(金属外观)、教育和夹具制造等。铝。 Alumide is a metallic grey, aluminium-filled polyamide 12 powder, which is characterised by its high stiffness, metallic appearance and good postprocessing possibilities. Laser-sintered parts made from Alumide possess excellent material properties: excellent dimensional accuracy well-balanced ratio of density and stiffness increased thermal conductivity good machinability The surfaces of Alumide parts can be refined very easily by grinding, polishing or coating. The machining of Alumide laser-sintered parts is simplified through the cut breaking effect of the aluminium filling. A typical application for Alumide is the manufacture of stiff parts of metallic appearance for applications in automotive manufacture (e.g. wind tunnel tests or parts that are not safety-relevant), for tool inserts for injecting and moulding small production runs, for illustrative models (metallic appearance), for education and jig manufacture et al. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.36 | g/cm³ | 内部方法 |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength 3 |
|||
23℃ 23℃ 3 |
4.6 | kJ/m² | ISO 179/1eA |
简支梁无缺口冲击强度 Charpy Unnotch Impact strength 3 |
|||
23℃ 23℃ 3 |
29 | kJ/m² | ISO 179/1eU |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature 3 |
|||
0.45 MPa,未退火 0.45 MPa, unannealed |
175 | ℃ | ISO 75-2/B |
1.8 MPa,未退火 1.8 MPa, unannealed |
144 | ℃ | ISO 75-2/A |
维卡软化温度 Vicat Softening Temp |
|||
B50 B50 |
℃ | ISO 306 | |
熔融温度 Melting temperature 4 |
℃ | ISO 11357 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
表面电阻率 Surface resistivity |
ohms | IEC 60093 | |
体积电阻率 Volume resistivity 3 |
ohms·cm | IEC 60093 | |
介电强度 Dielectric strength |
kV/mm | IEC 60243-1 | |
相对电容率 Relative permittivity |
IEC 60250 | ||
100 Hz 100 Hz |
IEC 60250 | ||
1 MHz 1 MHz |
IEC 60250 | ||
耗散因数 Dissipation factor |
|||
1 MHz 1 MHz |
IEC 60250 | ||
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 D,15 秒 Shore D, 15 seconds |
ISO 868 | ||
拉伸模量 Tensile modulus 2 |
MPa | ISO 527-2 | |
拉伸强度 tensile strength 3 |
MPa | ISO 527-2 | |
拉伸应变 Tensile strain 3 |
|||
断裂 fracture 3 |
% | ISO 527-2 | |
弯曲模量 Bending modulus 3 |
|||
23℃ 23℃ 3 |
MPa | ISO 178 | |
弯曲强度 bending strength 3 |
MPa | ISO 178 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 X Direction |
3 Y Direction |
4 20°C/min |
【新闻资讯】查看全部
一季度化学原料和制品业利润同比增长3.43倍
2021-04-30 搜料网资讯: 国家统计局公布的数据显示,一季度工业企业利润延续较快恢复态势。其中,化学原料和化学制品业利润同比增长3.43倍。 数据显示13月份,全国规模以上工业企业实现利润 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |