产品简介:Plexiglas Heatreist HW55 Clear是一种基于甲基丙烯酸甲酯(MMA)与共聚单体成分的共聚物。Plexiglas Heatreist HW55 Clear除了显示了标准Plexiglas模塑料熟悉的特性,例如高透光性、良好的流动性、高机械强度、表面硬度和耐磨性,以及优异的耐候性外,还提供了在LOA下增加热偏转温度的额外好处。并提高了抗应力咯咯声优化了固有颜色,美国医学协会上市。用途:Plexiglas Heatreist HW55 Clear特别适用于注塑工艺项目。例如:亮键、灯具盖、光纤。 PLEXIGLAS® Heatresist hw55 clear is a copolymer based on methyl methacrylate (MMA) with comonomer constituents. Besides showing the familiar properties of standard PLEXIGLAS® molding compound, such as high light transmission, good flowability, high mechanical strength, surface hardness and abrasion resistance, as well as excellent weatherability, PLEXIGLAS® Heatresist hw55 clear offers the additional benefits of increased heat deflection temperature under load and improved resistance to stress cacking optimised inherent color, AMECA listing. Application: PLEXIGLAS® Heatresist hw55 clear is particularly suitable for injection molding of technical items. Examples: lighted keys, luminaire covers, fiber optics. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.19 | g/cm³ | ISO 1183 |
熔体体积流动速率 Melt Volume Rate |
|||
230℃,3.8 kg 230℃,3.8 kg |
1.20 | cm³/10min | ISO 1133 |
吸水率 Water absorption rate |
ISO 62 | ||
23℃,24hr 23℃,24hr |
2.2 | % | ISO 62 |
平衡,23℃,50% RH Equilibrium, 23 ℃, 50% RH |
0.60 | % | ISO 62 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
3600 | MPa | ISO 527-1-2 |
拉伸强度 tensile strength |
|||
断裂 fracture |
MPa | ISO 527-2/5 | |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ISO 527-2/5 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
|||
23℃ 23℃ |
kJ/m² | ISO 179/1eU | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ISO 75-2/B | |
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
玻璃化转变温度 Glass transition temperature |
℃ | ISO 11357-2 | |
维卡软化温度 Vicat Softening Temp |
|||
B50 B50 |
℃ | ISO 306 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD:0~50℃ MD:0~50℃ |
1/℃ | ISO 11359-2 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
1.60 mm 1.60 mm |
UL 94 | ||
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
折射率 Refractive index |
ISO 489 | ||
透光率 Transmittance 3 |
% | ISO 13468-2 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 D65 |
【新闻资讯】查看全部
西湖化学(Westlake Chemical Corporation)将更名为Westlake Corporation
2022-02-18 2月15日,西湖化学(Westlake Chemical Corporation)宣布,计划于2022年2月18日正式更名为Westlake Corporation。 Westlake总裁兼首席执行官Albert Chao表示:我们的业务组合在过去十年中不断发展,特别 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |