公司信息及水印
牌号简介 About |
---|
产品描述:Trexprene A74NU是一种热稳定的PP/EPDM基热塑性硫化弹性体(TPV)。这种天然化合物主要用于发动机罩下的应用,如垫子、密封件、垫圈、风管、CVJ护套、盖子、索环或其他需要柔软性和一致性的零件。这种材料可以使用注塑、挤压、吹塑或其他熔融加工技术进行加工。 |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.930 to 0.970 | g/cm³ | ISO 1183 |
弹性体 elastic body |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength 2 |
ISO 37 | ||
TD,100% 应变 TD, 100% strain |
3.10 | MPa | ISO 37 |
MD,100% 应变 MD, 100% strain |
5.80 | MPa | ISO 37 |
拉伸强度 tensile strength 2 |
ISO 37 | ||
断裂 fracture |
7.70 | MPa | ISO 37 |
MD,断裂 MD, fracture |
6.20 | MPa | ISO 37 |
拉伸应变 Tensile strain 2 |
ISO 37 | ||
断裂 fracture |
% | ISO 37 | |
流量,断裂 Flow rate, fracture |
% | ISO 37 | |
撕裂强度 tear strength 3 |
ISO 34-1 | ||
TD TD |
kN/m | ISO 34-1 | |
MD MD |
kN/m | ISO 34-1 | |
压缩形变 Compression deformation |
ASTM D395B | ||
70℃,22 hr 70℃,22 hr |
% | ASTM D395B | |
125℃,70 hr 125℃,70 hr |
% | ASTM D395B | |
压缩形变 Compression deformation 4 |
ISO 815 | ||
70℃,22 hr 70℃,22 hr |
% | ISO 815 | |
125℃,70 hr 125℃,70 hr |
% | ISO 815 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
ISO 868 | ||
邵氏 A Shaw's A |
ISO 868 | ||
邵氏 A,15 秒 Shore A, 15 seconds |
ISO 868 | ||
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
脆化温度 Embrittlement temperature |
℃ | ASTM D746 | |
Brittleness Temperature(Type B) Brittleness Temperature(Type B) |
℃ | ISO 812 | |
老化性能 Aging performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
空气中拉伸强度的变化率 The rate of change in tensile strength in air |
ISO 188 | ||
135℃,1000 hr 135℃,1000 hr |
% | ISO 188 | |
150℃,168 hr 150℃,168 hr |
% | ISO 188 | |
在空气中断裂时拉伸应力变化 Changes in tensile stress during fracture in air |
ISO 188 | ||
135℃,1000 hr 135℃,1000 hr |
% | ISO 188 | |
150℃,168 hr 150℃,168 hr |
% | ISO 188 | |
Change in Tensile Stress(125℃,70 hr,in IRM 903 Oil) Change in Tensile Stress(125℃,70 hr,in IRM 903 Oil) |
% | ISO 1817 | |
Change in Tensile Strain at Break(125℃,70 hr,in IRM 903 Oil) Change in Tensile Strain at Break(125℃,70 hr,in IRM 903 Oil) |
% | ISO 1817 | |
体积变化 Volume change |
|||
125℃,70 hr,在IRM 903油中 125 ℃, 70 hr, in IRM 903 oil |
% | ISO 1817 | |
撕裂强度的变化率 Change rate of tear strength |
|||
70 hrs,in IRM 903 Oil,125℃ 70 hrs,in IRM 903 Oil,125℃ |
% | ISO 1817 | |
Change in Tensile Properties Change in Tensile Properties |
|||
Stress at 100% Elongation in Air,168 hrs:150℃ Stress at 100% Elongation in Air,168 hrs:150℃ |
% | ISO 188 | |
Stress at 100% Elongation in IRM 903 Oil,70 hrs:125℃ Stress at 100% Elongation in IRM 903 Oil,70 hrs:125℃ |
% | ISO 1817 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
燃烧速率 Burning rate |
mm/min | ISO 3795 | |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
耐臭氧性 Ozone resistance 5 |
|||
40℃ 40℃ 5 |
ISO 1431-1 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 类型 1, 20 in/min |
3 B 方法,直角形试样(不割口), 20 in/min |
4 类型 A |
5 100 pphm, Method A |
【新闻资讯】查看全部
消息称OPEC+增产低于预期,油价创近三年新高
2021-07-02 搜料网资讯: 据彭博,沙特和俄罗斯就提高石油产量达成初步协议,2021年12月前增产低于50万桶/天。 受此消息影响,WTI原油期货日内涨幅扩大近2%,报74.87美元/桶,布伦特原油期货现涨 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |