| 牌号简介 About |
|---|
| GP 100或是一种高密度聚乙烯混合物，具有高摩尔质量，专门用于制造气体加压管线的挤压管。该树脂采用双峰技术生产，具有优异的力学性能和很高的抗内压性能。根据ISO 9080，该树脂的MRS（最低要求强度）为10 MPa，根据ISO 12162，该树脂被归类为PE 100。GP 100或采用橙色制造，并含有防止紫外线辐射的添加剂。符合NBR 14462:00的要求。用途：用于气体分配的橙色PE 100压力管；水下电缆的护套 GP100OR is a High Density Polyethylene compound specially developed for the manufacturing of extruded pipes for gas distribution. It is produced with bimodal technology and has high molar mass. It shows excellent mechanical properties and resistance to hydrostatic pressure and stress cracking. This resin has MRS (Minimum Required Strength) of 10 MPa, according to ISO 9080, and is classified as PE 100, according to ISO 12162. GP100OR is manufactured in orange color and contains additives to protect it against ultraviolet radiation action and photodegradation. Application: Jacketing of underwater cables Process: Pipe Extrusion. |
产品描述 Product Description
用途：天然气输配;管道系统;
颜色：橙色
加工条件：挤出 Extrusion
性能特点： 高分子量; 耐候抗UV; 抗应力开裂; Weather resistance is good,High molecular weight,High ESCR
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
0.950 | g/cm³ | ASTM D792 |
|
熔体质量流动速率 Melt Flow Rate |
|||
|
190℃，5.0kg 190℃，5.0kg |
0.22 | g/10min | ASTM D1238 |
|
抗环境应力开裂 ESCR(Environmental Stress Cracking Resistance) |
|||
|
50 ℃，2.00 mm，100%非离子表面活性剂，模压成型，F50 50 ℃, 2.00 mm, 100% non-ionic surfactant, molded, F50 |
> 1000 | hr | ASTM D1693 |
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
邵氏硬度 Shore hardness |
|||
|
邵氏 D，模压成型 Shaw's D, molded |
64 | ASTM D2240 | |
|
拉伸强度 tensile strength |
|||
|
断裂，模压成型 Fracture, molded |
36.0 | MPa | ASTM D638 |
|
屈服，模压成型 Yield, molding |
MPa | ASTM D638 | |
|
拉伸应变 Tensile strain |
|||
|
断裂，模压成型 Fracture, molded |
% | ASTM D638 | |
|
屈服，模压成型 Yield, molding |
% | ASTM D638 | |
|
弯曲模量 Bending modulus |
|||
|
1% 正割，模压成型 1% cut, molded |
MPa | ASTM D790 | |
|
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
|
模压成型 Compression Molding |
J/m | ASTM D256 | |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
热变形温度 Hot deformation temperature |
|||
|
0.45 MPa，未退火，模压成型 0.45 MPa, unannealed, molded |
℃ | ASTM D648 | |
|
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 2 | |
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
| 2 压 力1 (10N) |
|
【新闻资讯】查看全部 
韩国三星与西班牙TR分别中标石化EPC项目合同
2021-02-22 搜料网资讯： 三星再中标泰国烯烃项目EPC合同 三星工程与泰国PTTGC签订一份1.27亿美元的EPC合同，合同的标的为改造泰国的MAP TA PHUT烯烃装置。项目计划于2023年完工。 三星的方案是通过 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付