牌号简介 About |
---|
材料代码符合ISO 1043-1:聚丙烯均聚物增强40%重量%长的玻璃纤维。纤维与聚丙烯基体发生化学耦合。球是圆柱形的,通常也包括10 mm长的嵌入纤维。(-0414=热稳定)Celstran成型的天然零件具有优异的机械性能,例如高强度和刚度以及高热变形。由于部件中内置了纤维骨架,因此在高温和低温下缺口冲击强度会增加。长纤维增强能显著降低蠕变。模制品的各向同性收缩使翘曲最小化。通过注射成型,可以制造出具有高再现性的复杂零件。应用领域:汽车功能/结构件 Material code according to ISO 1043-1: PP Polypropylene Homopolymer reinforced with 40 weight percent long glass fibers. The fibers are chemically coupled to the polypropylene matrix. The pellets are cylindrical and normally as well as the embedded fibers 10 mm long. (-0414 = heat stabilized) natural Parts molded of CELSTRAN have outstanding mechanical properties such as high strength and stiffness combined with high heat deflection. The notched impact strength is increased at elevated and low temperatures due to the fiber skeleton built in the parts. The long fiber reinforcement reduces creep significantly. The very isotropic shrinkage in the molded parts minimizes the warpage. Complex parts can be manufactured with high reproducibility by injection molding. Application field: Functional/structural parts for automotive |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.22 | g/cm³ | ISO 1183 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
|||
-- -- |
9300 | MPa | ISO 527-2/1A/1 |
80℃ 80℃ |
7000 | MPa | ISO 527-2/1A |
拉伸强度 tensile strength |
|||
断裂 fracture |
137 | MPa | ISO 527-2/1A/5 |
80℃ 80℃ |
80.0 | MPa | ISO 527-2/1A |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ISO 527-2/1A/5 | |
断裂,80℃ Fracture, 80 ℃ |
% | ISO 527-2/1A | |
弯曲模量 Bending modulus |
ISO 178 | ||
23℃ 23℃ |
MPa | ISO 178 | |
80℃ 80℃ |
MPa | ISO 178 | |
弯曲强度 bending strength |
ISO 178 | ||
23℃ 23℃ |
MPa | ISO 178 | |
80℃ 80℃ |
MPa | ISO 178 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
ISO 179/1eA | ||
-30℃ -30℃ |
kJ/m² | ISO 179/1eA | |
23℃ 23℃ |
kJ/m² | ISO 179/1eA | |
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
ISO 179/1eU | ||
-30℃ -30℃ |
kJ/m² | ISO 179/1eU | |
23℃ 23℃ |
kJ/m² | ISO 179/1eU | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
8.0 MPa,未退火 8.0 MPa, unannealed |
℃ | ISO 75-2/C | |
熔融温度 Melting temperature 2 |
℃ | ISO 11357-3 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 10°C/min |
【新闻资讯】查看全部
应国际塑料制品需求塑料托盘或将增速放缓
2016-05-09 据报道,我国塑料托盘从出现以来快速增长,有些行业的塑料制品出现过翻倍增长,如塑料托盘行业、塑料薄膜行业等等。但近年来,国内塑料制品需求增速放缓。 . 应国内塑料制品需求塑料托盘或将增速 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |