牌号简介 About |
---|
PLURIS9300是一种采用滚球技术生产的四元聚合物,是一种具有独特性能的LLDPE,例如与韧性相关的高刚度。在熔融指数相同的情况下,与传统的LLDPE相比,其制备工艺简单,气泡稳定性好。用该产品获得的薄膜具有非常低的凝胶值。它含有加工助剂、抗氧化剂和抗阻塞添加剂。用途:重型袋子;衬垫,低密度聚乙烯和高密度聚乙烯混合物;通用包装。 PLURIS9300 is a Quateropolymer unique properties, such as high stiffness associated with toughness. It is easier to process than conventional LLDPE with the same melt index and shows very good bubble stability. Films obtained with this product have very low gel values. It contains processing Aid, antioxidant and antiblock additives. Applications: Heavy-duty bags; liners, LDPE and HDPE blends; packages for general use. Process: Blown Film Extrusion. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.919 | g/cm³ | ASTM D1505 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
0.55 | g/10min | ASTM D1238 |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
|||
TD,断裂,100 µm,吹塑薄膜 TD, fracture, 100 µ m, blow molded film |
35.0 | MPa | ASTM D882 |
MD,断裂,100 µm,吹塑薄膜 MD, fracture, 100 µ m, blow molded film |
40.0 | MPa | ASTM D882 |
拉伸应变 Tensile strain |
|||
TD,断裂,100 µm,吹塑薄膜 TD, fracture, 100 µ m, blow molded film |
1300 | % | ASTM D882 |
MD,断裂,100 µm,吹塑薄膜 MD, fracture, 100 µ m, blow molded film |
% | ASTM D882 | |
弯曲模量 Bending modulus |
|||
1% 正割,TD,100 µm,吹塑薄膜 1% secant, TD, 100 µ m, blow molded film |
MPa | ASTM D790 | |
1% 正割,MD,100 µm,吹塑薄膜 1% secant, MD, 100 µ m, blow molded film |
MPa | ASTM D790 | |
落锤冲击 Drop hammer impact |
|||
100 µm,吹塑薄膜 100 µ m, blow molded film |
g | ASTM D1709 | |
撕裂强度 tear strength |
|||
TD,100 µm,吹塑薄膜 TD, 100 µ m, blow molded film |
g | ASTM D1922 | |
MD,100 µm,吹塑薄膜 MD, 100 µ m, blow molded film |
g | ASTM D1922 | |
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
光泽度 gloss |
|||
60°,100 µm,吹塑薄膜 60 °, 100 µ m, blow molded film |
ASTM D2457 | ||
雾度 Haze |
|||
100 µm,吹塑薄膜 100 µ m, blow molded film |
% | ASTM D1003 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
百吨级高强高模聚酰亚胺纤维项目通过鉴定
2022-03-23 3月21日,百吨级高强高模聚酰亚胺(PI)纤维制备技术及应用项目在北京通过了由中国石油和化学工业联合会组织的科技成果鉴定。由中国工程院院士曹湘洪、陈祥宝、蹇锡高,中国科学院 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |