牌号简介 About |
---|
高分子量高密度聚乙烯(HMW-HDPE)用于薄膜挤出特性。KPOL Chem-HD K-04/950树脂是一种采用双峰技术生产的用于挤出高分子量薄膜的高密度聚乙烯。由该树脂制得的薄膜具有高韧性和优异的抗冲击性能,即使在很小的厚度。这种树脂具有广泛的摩尔质量分布,使其易于加工。应用零售袋;穿孔辊;重新包装;土工膜;一般袋。 High Molecular Weight High Density Polyethylene (HMW-HDPE) for Film Extrusion Characteristics The KPOL Chem - HD K-04/950 resin is a high density polyethylene produced with bimodal technology developed for the extrusion of high molecular weight film. The film produced from this resin exhibits characteristics of high toughness and excellent impact resistance even in small thickness. This resin has wide molar mass distribution, giving it easier to process. Applications Retail bags; perforated rolls; repackaging; geomembranes; bags in general. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.950 | g/cm³ | ASTM D1505 |
熔体质量流动速率 Melt Flow Rate |
ASTM D1238 | ||
190℃,2.16kg 190℃,2.16kg |
0.040 | g/10min | |
190℃,21.6kg 190℃,21.6kg |
8.6 | g/10min | |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
ASTM D882 | ||
MD,屈服 MD, yield |
40.0 | MPa | |
TD,屈服 TD, yield |
30.0 | MPa | |
MD,断裂 MD, fracture |
MPa | ||
TD,断裂 TD, fracture |
MPa | ||
拉伸应变 Tensile strain |
ASTM D882 | ||
MD,断裂 MD, fracture |
% | ||
TD,断裂 TD, fracture |
% | ||
落锤冲击 Drop hammer impact 1 |
g | ASTM D1709 | |
埃尔曼多夫抗撕强度 Elmandorf tear strength |
ASTM D1922 | ||
MD MD |
g | ||
TD TD |
g | ||
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
熔融温度 Melting temperature |
℃ | DSC |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 F50 |
【新闻资讯】查看全部
落成!英威达年产40万吨己二腈生产基地于上海化学工业区正式竣工
2022-11-30 扫描上图二维码,可以免费下载 搜料 APP 2022年11月25日,英威达尼龙化工(中国)有限公司于上海化学工业区(SCIP)举办尼龙化工己二腈(ADN)生产基地落成仪式。作为英威达历史上最 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |