| 牌号简介 About |
|---|
| Menzolit® BMC 2300是一种基于不饱和聚酯树脂的整体模塑料。该产品是玻璃纤维增强，含有矿物填料。如果发生火灾，产品不会熔化，也不会形成液滴，也不会产生过量的烟雾。这种材料是在加热的钢模中注射成型的。建议使用镀铬工具。该产品不含卤素。Menzolit® BMC 2300是一种特殊的BMC，具有极高的阻燃性。将玻璃含量设置为能够提供足够的可塑性和高强度和刚度特性的水平。阻燃性极高，材料不可燃。高阻燃性使其特别适用于开关设备部件，高压和大电流应用。 Menzolit® BMC 2300 is a bulk moulding compound based on unsaturated polyester resin. The product is glass fibre reinforced and contains mineral fillers. In case of fire the product doesn't melt, neither does it form droplets nor is smoke generation excessive. The material is injection moulded in heated steel moulds. It is recommended to work with chrome plated tools. The product contains no halogens. Menzolit® BMC 2300 is a special BMC with exceptional high fire retardancy. The glass content is set to a level that provides sufficient mouldability with high strength and stiffness properties. Fire retardancy is exceptionally high and the material is not burnable. The high fire retardancy makes it especially suited for switch gear components, for high voltage and high current applications. |
产品描述 Product Description
用途：电气元件;电气/电子应用领域;
颜色：可用颜色
加工条件：注射成型 Injection Molding
性能特点： 无卤; 低烟; 机械强度好; 耐高温; 阻燃; 易加工; Good Rigidity,Excellent Processability,Low smoke,Halogen free,Flame Characteristics,High Heat Resistance
填料：玻璃纤维
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
1.90 | g/cm³ | ISO 1183 |
|
收缩率 Shrinkage rate |
|||
|
-- -- |
0.080 | % | ISO 2577 |
|
-- -- 2 |
0.0 | % | DIN 53464 |
|
吸水率 Water absorption rate |
|||
|
饱和，23℃ Saturation, 23 ℃ |
< 0.50 | % | ISO 62 |
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
拉伸模量 Tensile modulus |
|||
|
模压成型 Compression Molding |
13000 | MPa | ISO 527-2 |
|
拉伸强度 tensile strength |
|||
|
屈服，模压成型 Yield, molding |
MPa | ISO 527-2 | |
|
弯曲模量 Bending modulus |
|||
|
模压成型 Compression Molding |
MPa | ISO 178 | |
|
弯曲强度 bending strength |
|||
|
模压成型 Compression Molding |
MPa | ISO 178 | |
|
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
简支梁缺口冲击强度 Charpy Notched Impact Strength |
|||
|
模压成型 Compression Molding |
kJ/m² | ISO 179 | |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
热变形温度 Hot deformation temperature |
|||
|
1.8 MPa，未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
|
连续使用温度 Continuous use temperature |
℃ | 内部方法 | |
|
玻璃化转变温度 Glass transition temperature |
℃ | DSC | |
|
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
|
MD MD |
1/℃ | ISO 11359-2 | |
|
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
表面电阻率 Surface resistivity |
ohms | IEC 60093 | |
|
体积电阻率 Volume resistivity |
ohms·cm | IEC 60093 | |
|
耐电弧性 Arc resistance |
sec | ASTM D495 | |
|
相比漏电起痕指数 Compared to the leakage tracing index |
V | IEC 1006 | |
|
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
灼热丝起燃温度 Igniting temperature of the hot wire |
℃ | IEC 60695-2-13 | |
|
极限氧指数 Extreme oxygen index |
% | ISO 4589-2 | |
|
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
Glow Bar Glow Bar |
IEC 60707-3 | ||
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
| 2 Post Molding Shrinkage |
|
【新闻资讯】查看全部 
达2355亿！中国化学签新合同，化工项目项目基建集中性增长
2022-10-19 扫描上图二维码，可以免费下载 搜料 APP 中国化工第三季度财务报告显示，2022年1-9月，中国化学累计营业收入1204.76亿元，同比增长33.44%；累计新签合同额2355.11亿元，同比增长36.66%。今 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付