牌号简介 About |
---|
Lupoy PC 1200-08树脂专为挤出和注塑产品设计。它在耐热性、透明度和冲击强度方面表现出良好的物理性能平衡。 LUPOY PC 1200-08 resin is designed for extrusion and injection molding products. It exhibits an excellent physical property balance of heat resistance, transparency and impact strength. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.20 | g/cm³ | ASTM D792 |
熔体质量流动速率 Melt Flow Rate |
|||
300℃,1.20kg 300℃,1.20kg |
8.0 | g/10min | ASTM D1238 |
收缩率 Shrinkage rate |
|||
MD MD |
0.50 to 0.70 | % | ASTM D955 |
吸水率 Water absorption rate |
|||
平衡,23℃,50% RH Equilibrium, 23 ℃, 50% RH |
0.32 | % | ASTM D570 |
23℃,24hr 23℃,24hr |
0.15 | % | ASTM D570 |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
23℃,3.2mm 23℃,3.2mm 4 |
J/m | ASTM D256 | |
23℃ 23℃ |
ASTM D256 | ||
装有测量仪表的落镖冲击 Dart impact equipped with measuring instruments 5 |
|||
23℃,3.20 mm,Total Energy 23℃,3.20 mm,Total Energy 5 |
J | ASTM D3763 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,退火,4.0 mm 1.8 MPa, annealed, 4.0 mm |
℃ | ASTM D648 | |
1.8 MPa,未退火,4.0 mm 1.8 MPa, unannealed, 4.0 mm |
℃ | ASTM D648 | |
0.45 MPa,退火,4.0 mm 0.45 MPa, annealed, 4.0 mm |
℃ | ASTM D648 | |
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 6 | |
球压温度 Ball pressure temperature |
℃ | IEC 60598-1 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD:-40~82℃ MD:-40~82℃ |
1/℃ | ASTM D696 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
体积电阻率 Volume resistivity |
|||
23℃ 23℃ |
ohms·cm | ASTM D257 | |
介电强度 Dielectric strength |
kV/mm | ASTM D149 | |
介电常数 Dielectric constant |
|||
60 Hz 60 Hz |
ASTM D150 | ||
耗散因数 Dissipation factor |
|||
60 Hz 60 Hz |
ASTM D150 | ||
相比漏电起痕指数 Compared to the leakage tracing index |
|||
2.00 mm 2.00 mm |
V | IEC 60112 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
UL 94 | ||
3.00 mm 3.00 mm |
UL 94 | ||
0.50 mm 0.50 mm |
UL 94 | ||
1.60 mm 1.60 mm |
UL 94 | ||
2.50 mm 2.50 mm |
UL 94 | ||
2.70 mm 2.70 mm |
UL 94 | ||
灼热丝起燃温度 Igniting temperature of the hot wire 7 |
|||
2 mm 2 mm 7 |
℃ | IEC 60695-2-13 | |
极限氧指数 Extreme oxygen index |
% | ASTM D2863 | |
平均燃烧程度 Average combustion degree |
cm | ASTM D635 | |
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
折射率 Refractive index |
ASTM D542 | ||
透光率 Transmittance |
% | ASTM D1003 | |
雾度 Haze |
% | ASTM D1003 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
MPa | ASTM D638 | |
拉伸强度 tensile strength 2 |
|||
断裂 fracture |
MPa | ASTM D638 | |
屈服,23℃ Yield, 23 ℃ 2 |
MPa | ASTM D638 | |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ASTM D638 | |
屈服 yield |
% | ASTM D638 | |
弯曲模量 Bending modulus |
MPa | ASTM D790 | |
弯曲强度 bending strength |
MPa | ASTM D790 | |
耐磨耗性 Wear resistance 3 |
|||
Change in Haze Change in Haze 3 |
% | ASTM D1004 | |
洛氏硬度 Rockwell hardness |
ASTM D785 | ||
M 级 M-level |
ASTM D785 | ||
R 级 R-level |
ASTM D785 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 2.0 in/min |
3 1000g, 500 cycles, CS-10F Wheel |
4 9.8 mil 缺口深度 |
5 11.1 ft/sec |
6 速率 A (50°C/h), 载荷2 (50N) |
7 5 sec |
【新闻资讯】查看全部
金发科技成都基地开工
2016-01-21 1月7日,以成都金发为主要代表的成都市双流区工业项目集中开工仪式在成都金发建设施工现场隆重举行。双流区委副书记徐刚、副区长易恩弟、金发科技董事长袁志敏、成都金发总经理陈力等相关领导出席了仪式。 双流区委常委、副区长易恩弟发表致辞,他表示,以成都金发为代表的11个工业项目投资总量大、科技含量高、带动能力强,这批项目的开工建设,必将为双流推进工业产业的快速发展提供新的增长点,为双流新一轮发展注入新的活力。 |
金发科技成都基地开工 1月7日,以成都金发为关键代表的成都市双流区工业生产新项目集中化动工仪式在成都金发基本建设施工工地隆重召开。双流市委组织部部长徐刚、区长易恩弟、金发科技老总袁志敏、成都金发经理李晨等有关领导干部参加了典礼。 双流区委常委、区长易恩弟发布致词,他表明,以成都金发为代表的11个工业生产投资项目总产量大、技术含量高、推动工作能力强,这批新项目的动工基本建设,终将为双流推动工业生产产业链的迅速发展趋势出示新的突破点,为双流新一轮发展趋势引入新的魅力。 袁志敏老总做为创业者代表讲话 袁志敏老总做为动工新项目创业者代表发布了发言。他关键详细介绍了成都金发的工程规模和建设规划。成都金发做为金发科技进一步发展西北的关键战略部署,建设项目实际意义长远。成都金发发展为金发科技的中西部提高模块后,将为金发科技千亿元总体目标的完成确立夯实基础。袁志敏老总表明,成都金发有信心、有工作能力将建设项目好,争得尽早建成投产、早创经济效益! 金发科技成都基地情况 金发科技2015年6月8日午间公告称,企业拟在四川省成都市双流县项目投资修建新型材料生产制造产品研发基地,并开设成都金发科技有限责任公司,拟订注册资金五亿元。 企业表明,本次境外投资开设控股子公司有益于增加对华西医院销售市场的辐射源幅度,扩宽企业主营业务收入来源于。 成都将变成金发科技全国各地第八个生产制造基地 金发科技已在全国各地已合理布局了广州市、厦门、上海市、昆山市、天津市、武汉市、绵阳市七个基地,再再加上成都基地,金发科技在全国各地合理布局八个基地。在其中珠三角2 个(广州市、厦门)、长三角两个(上海市、昆山市)、环勃海一个(天津市)、中间一个(武汉市)、中西部两个(成都、绵阳市)。金发科技大部分产生了以武汉市为管理中心的 1000千米内运送圈。 学习培训京东商城方式可否协助金发紧跟一层楼? 中西部地区正日渐变成我国极其重要的电子设备及其轿车的生产制造基地,金发科技合理布局中西部地区基地,可能接近用户账户,给与客户更强的服务项目感受。 金发科技的合理布局让人想到了电商企业京东商城。当电子商务平台都会发展趋势丰富多彩类目的情况下,京东商城另辟蹊径发展趋势全国物流,促使网上购物交货的時间减少到1天,京东商城的服务平台进而得到了非常高的客户忠诚度。在改性工程塑料市场竞争愈来愈猛烈的今日,这类合理布局可否协助金发再上一层楼? 来源于:unima塑胶新材网 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |
价格走势图
抱歉!该牌号暂无认证数据。
抱歉!暂无数据。
抱歉!暂无数据。