牌号简介 About |
---|
DuraGrip 6070BK是一种通用热塑性弹性体(TPE),设计用于注塑和挤出工艺。它具有较高的摩擦系数、较低的熔体粘度和良好的聚丙烯粘结性。DuraGrip 6070BK不吸湿,正常情况下不需要干燥。 DuraGrip® 6070BK is a general purpose Thermoplastic Elastomer (TPE) designed for injection molding and extrusion processes. It has a high coefficient of friction, low melt viscosity and bonds well to polypropylene. DuraGrip® 6070BK is not hygroscopic and under normal conditions does not require drying. |
技术参数 Technical Data | |||
---|---|---|---|
弹性体 elastic body |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
|||
屈服 yield |
8.34 | MPa | ASTM D412 |
屈服 yield |
8.34 | MPa | ISO 37 |
300% 应变 300% strain |
3.43 | MPa | ISO 37 |
300% 应变 300% strain |
3.43 | MPa | ASTM D412 |
100% 应变 100% strain |
2.62 | MPa | ISO 37 |
100% 应变 100% strain |
MPa | ASTM D412 | |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ASTM D412 | |
断裂 fracture |
% | ISO 37 | |
撕裂强度 tear strength |
kN/m | ASTM D624 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 A,5 秒 Shore A, 5 seconds |
ASTM D2240 | ||
邵氏 A,5 秒 Shore A, 5 seconds |
ISO 868 | ||
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
g/cm³ | ASTM D792 | |
密度 Density |
g/cm³ | ISO 1183 | |
收缩率 Shrinkage rate |
|||
MD:1.59 mm MD:1.59 mm |
% | ASTM D955 | |
MD:3.2 mm MD:3.2 mm |
% | ASTM D955 | |
TD:1.59 mm TD:1.59 mm |
% | ASTM D955 | |
TD:3.2 mm TD:3.2 mm |
% | ASTM D955 | |
熔体表观粘度 Apparent viscosity of melt |
|||
190℃,294 sec^-1 190℃,294 sec^-1 |
Pa·s | ASTM D3835 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 C 模具 |
【新闻资讯】查看全部
5月起,这些新规将影响你我生活!
2022-04-29 修订后的《中华人民共和国职业教育法》施行! 十三届全国人大常委会第三十四次会议近日表决通过了新修订的职业教育法,将于2022年5月1日起施行。这是该法自1996年颁布施行以来的首 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |