牌号简介 About |
---|
Novalloy-B B5706是一种丙烯腈丁二烯苯乙烯 + PBT (ABS+PBT)产品,含有的填充物为30% 玻璃纤维增强材料。 它可以通过涂层或注射成型进行加工,在北美洲有供货。 Novalloy-B B5706的应用领域包括电气/电子应用、房屋、商业/办公用品 和 涂覆应用。 特性包括: 阻燃/额定火焰 耐化学品 耐磨 Flame Retardant 附着力强 Novalloy-B B5706 is an Acrylonitrile Butadiene Styrene + PBT (ABS+PBT) product filled with 30% glass fiber. It can be processed by coating or injection molding and is available in North America. Applications of Novalloy-B B5706 include electrical/electronic applications, business/office goods, coating applications and housings. Characteristics include: Flame Rated Chemical Resistant Wear Resistant Flame Retardant Good Adhesion |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.55 | g/cm³ | ASTM D792 |
收缩率 Shrinkage rate |
|||
MD MD |
0.30 到 0.50 | % | ASTM D955 |
吸水率 Water absorption rate |
|||
24hr 24hr |
0.15 | % | ASTM D570 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
|||
屈服 yield |
123 | MPa | ASTM D638 |
拉伸应变 Tensile strain |
|||
断裂 fracture |
2.2 | % | ASTM D638 |
弯曲模量 Bending modulus |
MPa | ASTM D790 | |
弯曲强度 bending strength |
|||
屈服 yield |
MPa | ASTM D790 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
23℃,3.2mm 23℃,3.2mm |
J/m | ASTM D256 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
ASTM D648 | ||
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ASTM D648 | |
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ASTM D648 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD MD |
1/℃ | ASTM D696 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
体积电阻率 Volume resistivity |
ohms·cm | ASTM D257 | |
介电强度 Dielectric strength |
kV/mm | ASTM D149 | |
介电常数 Dielectric constant |
|||
100 Hz 100 Hz |
ASTM D150 | ||
耗散因数 Dissipation factor |
|||
100 Hz 100 Hz |
ASTM D150 | ||
耐电弧性 Arc resistance |
|||
3.18 mm 3.18 mm |
sec | ASTM D495 | |
相比耐漏电起痕指数 Compared to the resistance to leakage and marking index |
|||
3.18 mm 3.18 mm |
V | UL 746 | |
高电弧燃烧指数(HAI) High Arc Burning Index (HAI) |
UL 746 | ||
1.59 mm 1.59 mm |
UL 746 | ||
3.18 mm 3.18 mm |
UL 746 | ||
高电压电弧起痕速率(HVTR)(3.18 mm) High voltage arc marking rate (HVTR) (3.18 mm) |
mm/min | UL 746 | |
热丝引燃 Hot wire ignition |
|||
HWI HWI |
UL 746 | ||
1.59 mm 1.59 mm |
sec | UL 746 | |
3.18 mm 3.18 mm |
sec | UL 746 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
1.60 mm 1.60 mm |
UL 94 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
乙烯生产突破性新技术由大连化物所与惠生联合成功开发
2021-09-14 搜料网资讯: 近日,由中科院大连化物所与惠生工程(中国)有限公司联合开发的乙烷氧化脱氢制乙烯(ODHE)技术顺利通过中国石油和化学工业联合会组织的单管中试技术评价,标志着 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |