牌号简介 About |
---|
Vydyne ECO366 BK13是一种非卤化、未填充、阻燃的PA66均聚物,可用于填充薄壁、复杂的零件。它是润滑的机器饲料和易于模具释放,UL 94可燃性分级V-0在0.4毫米厚。 Vydyne ECO366 BK13 is a non-halogenated, unfilled, flame-retardant PA66 homopolymer designed with superior flow properties to assist in filling thin-walled, intricate parts. It is lubricated for machine feed and easy mold release and has an Underwriters Laboratories UL 94 flammability classification of V-0 at 0.4 mm (0.016") thick. |
产品描述 Product Description
厂家:美国奥升德 Ascend
类别:PA66 PA66
颜色:黑色
性能特点: 防火阻燃等级V-0; 机械强度好; 低分子量; 易加工; Good Rigidity,Excellent Processability,Low molecular weight,V-0
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.17 | g/cm³ | ISO 1183 |
收缩率 Shrinkage rate |
ISO 294-4 | ||
TD:23℃,2.0 mm TD:23℃,2.0 mm |
0.60 | % | ISO 294-4 |
MD:23℃,2.0 mm MD:23℃,2.0 mm |
0.90 | % | ISO 294-4 |
吸水率 Water absorption rate |
|||
平衡,23℃,50% RH Equilibrium, 23 ℃, 50% RH |
2.3 | % | ISO 62 |
23℃,24hr 23℃,24hr |
0.80 | % | ISO 62 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
|||
屈服,23℃ Yield, 23 ℃ |
MPa | ISO 527-2 | |
拉伸应变 Tensile strain |
|||
断裂,23℃ Fracture, 23 ℃ |
% | ISO 527-2 | |
弯曲模量 Bending modulus |
|||
23℃ 23℃ |
MPa | ISO 178 | |
弯曲强度 bending strength |
|||
23℃ 23℃ |
MPa | ISO 178 | |
泊松比 Poisson's ratio |
ISO 527-2 | ||
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
ISO 179/1eA | ||
-30℃ -30℃ |
kJ/m² | ISO 179/1eA | |
23℃ 23℃ |
kJ/m² | ISO 179/1eA | |
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
ISO 179/1eU | ||
-30℃ -30℃ |
kJ/m² | ISO 179/1eU | |
23℃ 23℃ |
kJ/m² | ISO 179/1eU | |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
23℃ 23℃ |
kJ/m² | ISO 180 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ISO 75-2/B | |
熔融温度 Melting temperature |
℃ | ISO 11357-3 | |
相对温度指数 Relative temperature index |
|||
电气性能 Electrical performance |
UL 746 | ||
0.40 mm 0.40 mm |
℃ | UL 746 | |
0.75 mm 0.75 mm |
℃ | UL 746 | |
1.5 mm 1.5 mm |
℃ | UL 746 | |
3.0 mm 3.0 mm |
℃ | UL 746 | |
强度机械性能 Strength mechanical performance |
UL 746 | ||
0.40 mm 0.40 mm |
℃ | UL 746 | |
0.75 mm 0.75 mm |
℃ | UL 746 | |
1.5 mm 1.5 mm |
℃ | UL 746 | |
3.0 mm 3.0 mm |
℃ | UL 746 | |
冲击机械性能 Impact mechanical performance |
UL 746 | ||
0.40 mm 0.40 mm |
℃ | UL 746 | |
0.75 mm 0.75 mm |
℃ | UL 746 | |
1.5 mm 1.5 mm |
℃ | UL 746 | |
3.0 mm 3.0 mm |
℃ | UL 746 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
体积电阻率 Volume resistivity |
|||
0.75 mm 0.75 mm |
ohms·cm | IEC 60093 | |
介电强度 Dielectric strength |
|||
1 mm 1 mm |
kV/mm | IEC 60243 | |
耐电弧性 Arc resistance |
|||
3.0 mm 3.0 mm |
ASTM D495 | ||
相比漏电起痕指数 Compared to the leakage tracing index |
|||
3.00 mm 3.00 mm |
V | IEC 60112 | |
高电弧燃烧指数(HAI) High Arc Burning Index (HAI) |
UL 746 | ||
0.40 mm 0.40 mm |
UL 746 | ||
0.75 mm 0.75 mm |
UL 746 | ||
1.5 mm 1.5 mm |
UL 746 | ||
3.0 mm 3.0 mm |
UL 746 | ||
高电压电弧起痕速率 High voltage arc marking rate |
|||
HVTR HVTR |
UL 746 | ||
热丝引燃 Hot wire ignition |
|||
HWI HWI |
UL 746 | ||
0.40 mm 0.40 mm |
UL 746 | ||
0.75 mm 0.75 mm |
UL 746 | ||
1.5 mm 1.5 mm |
UL 746 | ||
3.0 mm 3.0 mm |
UL 746 | ||
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
UL 94 | ||
0.40 mm 0.40 mm |
UL 94 | ||
0.75 mm 0.75 mm |
UL 94 | ||
1.50 mm 1.50 mm |
UL 94 | ||
3.00 mm 3.00 mm |
UL 94 | ||
灼热丝可燃性指数 Glowing wire flammability index |
IEC 60695-2-12 | ||
0.40 mm 0.40 mm |
℃ | IEC 60695-2-12 | |
0.75 mm 0.75 mm |
℃ | IEC 60695-2-12 | |
1.5 mm 1.5 mm |
℃ | IEC 60695-2-12 | |
3.0 mm 3.0 mm |
℃ | IEC 60695-2-12 | |
灼热丝起燃温度 Igniting temperature of the hot wire |
IEC 60695-2-13 | ||
0.4 mm 0.4 mm |
℃ | IEC 60695-2-13 | |
0.75 mm 0.75 mm |
℃ | IEC 60695-2-13 | |
1.5 mm 1.5 mm |
℃ | IEC 60695-2-13 | |
3 mm 3 mm |
℃ | IEC 60695-2-13 | |
极限氧指数 Extreme oxygen index |
% | ISO 4589-2 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
Yoloha利用HEXPOL TPE生物基材料为瑜伽垫带来环保设计
2022-01-14 搜料网资讯: Yoloha是一家精益求精的公司。为了追求由高水平的可再生材料制成的优质瑜伽垫,他们选择与HEXPOLTPE合作。 为了支持Yoloha的可持续发展目标,HEXPOL TPE从Dryflex Green系列的生 |
Yoloha利用HEXPOL TPE生物基材料为瑜伽垫带来环保设计 搜料网资讯:Yoloha是一家精益求精的公司。为了追求由高水平的可再生材料制成的优质瑜伽垫,他们选择与HEXPOL TPE合作。
为了支持Yoloha的可持续发展目标,HEXPOL TPE从Dryflex Green系列的生物基热塑性弹性体(TPE)中开发了一种定制的材料。这种TPE的生物基含量为55%。它具有较高的熔体强度和可抽拉性,可轻松生产出具有均匀泡沫结构的发泡材料。发泡材料在垫子、防护服和座椅等应用中带来了轻质优势和缓冲作用。 Yoloha创始人Chris Willey评论说:“我使用并测试了市场上大多数天然橡胶、EVA、聚氨酯等泡沫材料,我发现TPE泡沫是支撑力、耐久性和重量的完美结合。考虑到这一点,我发现了HEXPOL TPE,他们专注于可持续性。我们很快建立了良好的关系,并共同开发了一种定制的材料。” Dryflex Green系列的生物基TPE含有来自可再生资源的原材料,包括富含碳水化合物的农业副产品,特别是谷物、甜菜或甘蔗等糖类。TPE的生物基含量超过90%(ASTM D 6866),硬度从15 Shore A到60 Shore D。 HEXPOL TPE有限公司可持续TPE技术销售部的Kathrin Heilmann补充说:“我们很自豪能与Yoloha在这个项目上合作。我们的目标是在保持机械性能和可加工性的同时实现高生物基含量。该材料显示出良好的发泡性,适用于地垫和其他挤出类产品。” |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |
价格走势图
开始时间:
结束时间:
材料厂家:
【牌号齐全,内容全面】
全网共2500+项牌号+上游原料单体+原油价格,最长可追溯近20年价格行情
【精准,及时,权威!】
专业团队挖掘行情信息,第一时间发布行情
抱歉!该牌号暂无认证数据。
免责声明:参考价格是搜料网根据网络大数据拟合分析的结果,仅供参考。实际成交价取决但不限于以下因素:下单时间,付款方式,交货方式,数量,税费,色号,产地,项目信息。
- 电缆线的密封接头
- 2019-03-31 151
- Vydyne® ECO366 BK13是一种PA66(尼龙66)均聚共聚物,具有优良的耐磨性、自润滑性,机械强度较高
- 阅读全文
电缆线的密封接头
1-Vydyne® ECO366 BK13是一种PA66(尼龙66)均聚共聚物。
2-Vydyne® ECO366 BK13具有优良的耐磨性、自润滑性,机械强度较高
3-Vydyne® ECO366 BK13自润性、耐磨性佳、耐药品性优
2-Vydyne® ECO366 BK13具有优良的耐磨性、自润滑性,机械强度较高
3-Vydyne® ECO366 BK13自润性、耐磨性佳、耐药品性优
收起
抱歉!暂无数据。