| 牌号简介 About |
|---|
| LL5800N树脂是一种线性低密度聚乙烯，辛烯-1共聚物，溶液法生产，用于吹塑薄膜挤出，具有优良的机械性能。它含有加工助剂和抗氧化剂添加剂。 LL5800N resin is a Linear Low Density Polyethylene for blown film extrusion with excellent mechanical properties. It contains processing aid and antioxidant additives. Applications: Heavy-duty bags; stretch; liners, LDPE and HDPE blends; packages for general use. Additive: Processing Aid Process: LL5800N resin should be processed on specific extruders for LLDPE. The optimum processing conditions will vary according to the type of equipment used, but the best results are obtained at a melt temperature within the range of 200 to 220° and blends with LDPE with a maximum ratio of 30%. Recommended blow up ratio: 1.8 to 3:1. |
产品描述 Product Description
用途：薄膜;衬里;包装;袋子;混合;
加工条件：吹塑薄膜
性能特点： 抗氧化; 辛烯共聚单体; Inoxidizability,Octene copolymer
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
0.918 | g/cm³ | ASTM D792 |
|
熔体质量流动速率 Melt Flow Rate |
|||
|
190℃，2.16kg 190℃，2.16kg |
1.0 | g/10min | ASTM D1238 |
|
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
拉伸强度 tensile strength |
|||
|
TD，断裂，100 µm，吹塑薄膜 TD, fracture, 100 µ m, blow molded film |
40.0 | MPa | ASTM D882 |
|
MD，断裂，100 µm，吹塑薄膜 MD, fracture, 100 µ m, blow molded film |
45.0 | MPa | ASTM D882 |
|
拉伸应变 Tensile strain |
|||
|
TD，断裂，100 µm，吹塑薄膜 TD, fracture, 100 µ m, blow molded film |
1400 | % | ASTM D882 |
|
MD，断裂，100 µm，吹塑薄膜 MD, fracture, 100 µ m, blow molded film |
% | ASTM D882 | |
|
弯曲模量 Bending modulus |
|||
|
1% 正割，TD，100 µm，吹塑薄膜 1% secant, TD, 100 µ m, blow molded film |
MPa | ASTM D790 | |
|
1% 正割，MD，100 µm，吹塑薄膜 1% secant, MD, 100 µ m, blow molded film |
MPa | ASTM D790 | |
|
落锤冲击 Drop hammer impact |
|||
|
100 µm，吹塑薄膜 100 µ m, blow molded film |
g | ASTM D1709 | |
|
撕裂强度 tear strength |
|||
|
TD，100 µm，吹塑薄膜 TD, 100 µ m, blow molded film |
g | ASTM D1922 | |
|
MD，100 µm，吹塑薄膜 MD, 100 µ m, blow molded film |
g | ASTM D1922 | |
|
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
光泽度 gloss |
|||
|
60°，100 µm，吹塑薄膜 60 °, 100 µ m, blow molded film |
ASTM D2457 | ||
|
雾度 Haze |
|||
|
100 µm，吹塑薄膜 100 µ m, blow molded film |
% | ASTM D1003 | |
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
|
【新闻资讯】查看全部
简介三维激光扫描仪
2016-09-19 三维激光扫描仪是借着扫描技术来测量工件的尺寸及形状等工作的一种仪器，激光扫描仪必须采用一个稳定度及精度良好的旋转马达，当光束打(射)到由马达所带动的多面棱规反射而形成扫描光束。由于多面棱规位于扫描透镜的前焦面上，并均匀旋转使激光束对反射镜而言其入射角相对的连续改变，因而反射角也作连续性改变，经由扫描透镜的作用，形成一条平行且连续由上而下的扫描线。 三维激光扫描系统本身主要包括激光测距系统和激光扫描系统，同时也集成CCD和仪器内部控制和校正系统等。在仪器内，通过两个同步反射镜 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付