牌号简介 About |
---|
EpoxAcast® 650是一种矿物填充通用铸造环氧树脂,成本低,用途广泛。它的特点是混合粘度低,气泡截留最小。选择快速、中等或缓慢的Catalyst以适合您的项目。你也可以使用高温硬化剂来提高铸件的耐热性。EpoxAcast® 650用于制造金属冲压的硬质模具以及模具和夹具。它还可用于电气封装,以延长封装电子器件的寿命,提高封装电子器件的性能。高抗压强度EpoxAcast® 650,是制作金属饰品冲压模具的理想选择。 EpoxAcast® 650 is a mineral filled general purpose casting epoxy that is low cost and versatile. It features a low mixed viscosity for minimal bubble entrapment. Choose Fast, Medium or Slow catalyst to fit your project. You can also use HT Hardener to give your castings higher heat resistance. EpoxAcast® 650 is used for making hard dies for metal stamping as well as patterns and fixtures. It is also used for electrical encapsulation to extend the life cycles and enhance the performance of potted electronic devices. The high compressive strength of EpoxAcast® 650 makes it ideal for making stamping dies for production pressing of metal ornaments. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.52 | g/cm³ | ASTM D1475 |
特定体积 Specific volume |
0.658 | cm³/g | ASTM D792 |
热固性混合粘度 Thermosetting mixed viscosity |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
-- -- 3 |
7000 | cP | |
-- -- 2 |
5000 | cP | |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
固化时间 Curing time |
|||
23℃ 23℃ 6 |
1.0 | hr | |
23℃ 23℃ 7 |
hr | ||
23℃ 23℃ 8 |
hr | ||
66℃ 66℃ 6 |
hr | ||
66℃ 66℃ 7 |
hr | ||
66℃ 66℃ 8 |
hr | ||
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
巴氏硬度 Babbitt hardness |
ASTM D2240 | ||
拉伸模量 Tensile modulus |
ASTM D638 | ||
-- -- 2 |
MPa | ASTM D638 | |
-- -- 3 |
MPa | ASTM D638 | |
拉伸强度 tensile strength |
ASTM D638 | ||
断裂 fracture 2 |
MPa | ASTM D638 | |
断裂 fracture 3 |
MPa | ASTM D638 | |
拉伸应变 Tensile strain |
ASTM D638 | ||
断裂 fracture 3 |
% | ASTM D638 | |
断裂 fracture 2 |
% | ASTM D638 | |
弯曲模量 Bending modulus |
ASTM D790 | ||
-- -- 2 |
MPa | ASTM D790 | |
-- -- 3 |
MPa | ASTM D790 | |
弯曲强度 bending strength |
ASTM D790 | ||
-- -- 3 |
MPa | ASTM D790 | |
-- -- 2 |
MPa | ASTM D790 | |
压缩模量 Compression modulus |
ASTM D695 | ||
-- -- 2 |
MPa | ASTM D695 | |
-- -- 3 |
MPa | ASTM D695 | |
压缩强度 compressive strength |
ASTM D695 | ||
-- -- 3 |
MPa | ASTM D695 | |
-- -- 2 |
MPa | ASTM D695 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
ASTM D648 | ||
1.8 MPa,未退火 1.8 MPa, unannealed 4 |
℃ | ASTM D648 | |
1.8 MPa,未退火 1.8 MPa, unannealed 5 |
℃ | ASTM D648 | |
热固组件 Thermosetting components |
|||
部件 A Component A 9 |
|||
部件 B Component B 6 |
|||
部件 B Component B 7 |
|||
部件 B Component B 8 |
|||
部件 B Component B 9 |
|||
储存稳定性 storage stability |
|||
23℃ 23℃ 6 |
min | ||
23℃ 23℃ 7 |
min | ||
23℃ 23℃ 8 |
min | ||
23℃ 23℃ 9 |
min |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 Using 101,102 or 103 Hardener |
3 Using HT Hardener |
4 Using HT Hardener, Post cured |
5 Using 101,102 or 103 Hardener, Cured at 73°F |
6 HT HIGH TEMP Hardener |
7 103 SLOW Hardener |
8 102 MEDIUM Hardener |
9 101 FAST Hardener |
10 HT HIGH TEMP Hardener, followed by 2 hr at 175°F and 3 hr at 300°F |
【新闻资讯】查看全部
LG化学低密度聚乙烯LDPE应用于环保次抛包装领域
2023-09-12 扫描上图二维码,可以免费下载 搜料 APP 低密度聚乙烯(LDPE)原本主要用于制作医药行业的无菌次抛产品,如今美妆行业发展迅速,微剂量包装的产品需求量日益增加,LDPE之称的包装 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |