牌号简介 About |
---|
说明:CP 195是一种非常高的熔体流动速率的异相共聚物,开发用于高速注塑机和高生产率的薄壁注塑件。该产品具有高冲击强度,即使在零下温度,它是适合食品接触应用,因为它具有良好的感官性能。用途:家用;低温包装;冷冻甜点包装;感官性能优良的包装。 CP 195 is a very high melt flow rate heterophasic copolymer developed for high speed injection moulding machines and high productivity thin-walled injection moulded parts. The product features high impact strength even at sub-zero temperatures and it is suitable for food contact applications due to its excellent organoleptic properties. Applications: Packaging for food sensitive to changes in odor and taste; Housewares; Packaging for frozen desserts; Injected lids for margarine. Processing: Injection Molding |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.895 | g/cm³ | ASTM D792 |
密度 Density |
0.895 | g/cm³ | ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
|||
230℃,2.16kg 230℃,2.16kg |
60 | g/10min | ASTM D1238 |
230℃,2.16kg 230℃,2.16kg |
60 | g/10min | ISO 1133 |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
ASTM D256 | ||
-20℃,注塑成型 -20 ℃, injection molding |
40 | J/m | ASTM D256 |
23℃,注塑成型 23 ℃, injection molding |
J/m | ASTM D256 | |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
ISO 180 | ||
-20℃,注塑成型 -20 ℃, injection molding |
kJ/m² | ISO 180 | |
23℃,注塑成型 23 ℃, injection molding |
kJ/m² | ISO 180 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火,注塑 1.8 MPa, unannealed, injection molded |
℃ | ASTM D648 | |
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
0.45 MPa,未退火,注塑成型 0.45 MPa, unannealed, injection molded |
℃ | ASTM D648 | |
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ISO 75-2/B | |
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 3 | |
维卡软化温度 Vicat Softening Temp |
℃ | ISO 306/A | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
|||
屈服,注塑成型 Yield, injection molding |
MPa | ASTM D638 | |
屈服,注塑成型 Yield, injection molding |
MPa | ISO 527-2 | |
拉伸应变 Tensile strain |
|||
屈服,注塑成型 Yield, injection molding |
% | ASTM D638 | |
屈服,注塑成型 Yield, injection molding |
% | ISO 527-2 | |
弯曲模量 Bending modulus |
|||
1% 正割,注塑成型 1% cut, injection molding |
MPa | ISO 178 | |
1% 正割,注塑成型 1% cut, injection molding |
MPa | ASTM D790 | |
洛氏硬度 Rockwell hardness |
|||
R 级 R-level 2 |
ISO 2039-2 | ||
R 级 R-level |
ASTM D785 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 压 力1 (10N) |
【新闻资讯】查看全部
传统模具产业转型路在何方?
2016-06-23 6月14日―16日,2016广东机械模具产业领袖峰会暨首届广东机械模具产业创新成果展示交易会在东莞市横沥镇举行。在全省专业镇协同创新工作现场会举行的同时,横沥举办此次机械模具产业创新成果展示交易会,体现了专业镇办专业展、为创新者搭台办成果展的特色定位。 本次活动有63家企业、院校及相关机构参展,有两位中国工程院院士及省内外专家教授、省内重点企业领导近300人参加了峰会。来自广州、深圳、佛山、珠海、东莞、揭阳等地的18家机械模具产业龙头骨干企业的参展,进一步凸显了横沥镇在近年 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |