Sarlink 24946DN-1 XRD是一种用于汽车应用的高性能热塑性硫化胶。Sarlink 24946DN-1 XRD是一种高硬度润滑材料,具有耐日光和紫外线吸收特性。这一等级可以通过注射成型和挤压加工。 Sarlink 24946DN-1 XRD is a high performance thermoplastic vulcanizate used in automotive applications. Sarlink 24946DN-1 XRD is a high hardness lubricated grade exhibiting sunlight resistance and UV absorbing characteristics. This grade can be processed by injection molding and extrusion. |
技术参数 Technical Data | |||
---|---|---|---|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
ISO 868 | ||
邵氏 D,1 秒,注塑成型 Shore D, 1 second, injection molding |
47 | ISO 868 | |
邵氏 D,5 秒,注塑成型 Shore D, 5 seconds, injection molding |
45 | ISO 868 | |
邵氏 D,15 秒,注塑成型 Shore D, 15 seconds, injection molding |
44 | ISO 868 | |
弹性体 elastic body |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength 2 |
ISO 37 | ||
TD,100% 应变 TD, 100% strain |
8.70 | MPa | ISO 37 |
MD,100% 应变 MD, 100% strain |
12.5 | MPa | ISO 37 |
拉伸应变 Tensile strain 2 |
ISO 37 | ||
TD,断裂 TD, fracture |
% | ISO 37 | |
流量,断裂 Flow rate, fracture |
% | ISO 37 | |
撕裂强度 tear strength 3 |
ISO 34-1 | ||
TD TD |
kN/m | ISO 34-1 | |
MD MD |
kN/m | ISO 34-1 | |
压缩形变 Compression deformation 4 |
ISO 815 | ||
23℃,22 hr 23℃,22 hr |
% | ISO 815 | |
70℃,22 hr 70℃,22 hr |
% | ISO 815 | |
90℃,70 hr 90℃,70 hr |
% | ISO 815 | |
125℃,70 hr 125℃,70 hr |
% | ISO 815 | |
老化性能 Aging performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
空气中拉伸强度的变化率 The rate of change in tensile strength in air 5 |
ISO 188 | ||
TD:110℃,1008 hr TD:110℃,1008 hr |
% | ISO 188 | |
MD:110℃,1008 hr MD:110℃,1008 hr |
% | ISO 188 | |
TD:100% 应变 110℃,1008 hr TD: 100% strain at 110 ℃, 1008 hr |
% | ISO 188 | |
MD:100% 应变 110℃,1008 hr MD: 100% strain at 110 ℃, 1008 hr |
% | ISO 188 | |
TD:125℃,168 hr TD:125℃,168 hr |
% | ISO 188 | |
MD:125℃,168 hr MD:125℃,168 hr |
% | ISO 188 | |
TD:100% 应变 125℃,168 hr TD: 100% strain 125 ℃, 168 hr |
% | ISO 188 | |
MD:100% 应变 125℃,168 hr MD: 100% strain 125 ℃, 168 hr |
% | ISO 188 | |
在空气中断裂时拉伸应力变化 Changes in tensile stress during fracture in air 5 |
ISO 188 | ||
TD:110℃,1008 hr TD:110℃,1008 hr |
% | ISO 188 | |
流量:110℃,1008 hr Flow rate: 110 ℃, 1008 hr |
% | ISO 188 | |
TD:125℃,168 hr TD:125℃,168 hr |
% | ISO 188 | |
流量:125℃,168 hr Flow rate: 125 ℃, 168 hr |
% | ISO 188 | |
空气中邵氏硬度的变化率 The rate of change of Shore hardness in air |
|||
支撐 D,110℃,1008 hr Support D, 110 ℃, 1008 hr 6 |
ISO 188 | ||
支撐 D,110℃,1008 hr Support D, 110 ℃, 1008 hr 7 |
ISO 188 | ||
支撐 D,125℃,168 hr Support D, 125 ℃, 168 hr 6 |
ISO 188 | ||
支撐 D,125℃,168 hr Support D, 125 ℃, 168 hr 8 |
ISO 188 | ||
支撐 D,125℃,168 hr Support D, 125 ℃, 168 hr 7 |
ISO 188 | ||
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
g/cm³ | ISO 1183 | |
熔体质量流动速率 Melt Flow Rate |
|||
230℃,2.16kg 230℃,2.16kg |
g/10min | ASTM D1238 | |
熔体表观粘度 Apparent viscosity of melt |
|||
200℃,206 sec^-1 200℃,206 sec^-1 |
Pa·s | ASTM D3835 | |
特殊值 Special value |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
TD,断裂 TD, fracture |
MPa | ISO 37 | |
MD,断裂 MD, fracture |
MPa | ISO 37 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 类型 1, 20 in/min |
3 B 方法,直角形试样(不割口), 20 in/min |
4 类型 A |
5 类型 1 |
6 1 sec |
7 5 sec |
8 15 sec |
【新闻资讯】查看全部
全球独一BOPP薄膜-聚丙烯-丙烯三级全产业链将于2018年…
2017-09-21 秋日的福州江阴半岛,海风猎猎。江阴港10万吨级专用码头已整装待发,进口的液化石油气将通过2公里长的输油管道直接进入中景石化科技园生产。放眼科技园区,高耸的“亚洲第一塔”丙烯丙烷精馏塔正加紧安装,预计明年6月底投产,年产80万吨丙烯;而提前10个月开工的年产150万吨多元共聚聚丙烯项目,计划2018年投产。这两个目前世界上单产产能最大的装置,将改变国内高品质工程塑料原材料大部分依靠进口的局面。 “我们正加紧建设,5年内打造高效集聚的千亿产值科技园。”中国软包装集团董事局主席翁 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |