牌号简介 About |
---|
用于评估HD 21.14软电缆护套等应用的柔性和非卤化阻燃挤出级。阻燃性能满足EN 50265-2-1要求。 Flexible and non-halogenated flame retardant extrusion grade intended for evaluation in applications such as jacket of HD 21.14 flexible cables. Flame retardant performance capable of meeting EN 50265-2-1 requirement. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.17 | g/cm³ | ASTM D792 |
熔体质量流动速率 Melt Flow Rate |
|||
250℃,10.0kg 250℃,10.0kg |
4.0 | g/10min | ASTM D1238 |
吸水率 Water absorption rate |
|||
23℃,24hr 23℃,24hr |
0.020 | % | ISO 62 |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
Heat Deformation(100℃) Heat Deformation(100℃) 5 |
23 | % | UL 1581 |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
表面电阻率 Surface resistivity |
2.5E+16 | ohms | ASTM D257 |
体积电阻率 Volume resistivity |
ohms·cm | ASTM D257 | |
介电强度 Dielectric strength |
|||
2 mm,在油中 2 mm in oil |
kV/mm | ASTM D149 | |
介电常数 Dielectric constant |
|||
1.00 GHz 1.00 GHz |
ASTM D150 | ||
耗散因数 Dissipation factor |
|||
1 GHz 1 GHz |
ASTM D150 | ||
相比漏电起痕指数 Compared to the leakage tracing index |
V | IEC 60112 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
灼热丝可燃性指数 Glowing wire flammability index |
|||
3.0 mm 3.0 mm |
℃ | IEC 60695-2-12 | |
灼热丝起燃温度 Igniting temperature of the hot wire |
|||
3 mm 3 mm |
℃ | IEC 60695-2-13 | |
极限氧指数 Extreme oxygen index |
% | ISO 4589-2 | |
Vertical Flame Test Vertical Flame Test |
EN 50265-2-1 | ||
烟雾密度 Smoke density |
ASTM E662 | ||
Flame,0.5 mm plaque,Ds,max Flame,0.5 mm plaque,Ds,max |
ASTM E662 | ||
Non-Flame,0.5 mm plaque,Ds,max Non-Flame,0.5 mm plaque,Ds,max |
ASTM E662 | ||
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 A,30 秒 Shore A, 30 seconds |
ASTM D2240 | ||
拉伸强度 tensile strength |
|||
断裂 fracture |
MPa | UL 1581 | |
断裂 fracture 2 |
MPa | ASTM D638 | |
断裂,136℃ Fracture, 136 ℃ 3 |
MPa | UL 1581 | |
断裂 fracture |
MPa | ISO 527-2/50 | |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | UL 1581 | |
断裂 fracture 2 |
% | ASTM D638 | |
断裂,136℃ Fracture, 136 ℃ 3 |
% | UL 1581 | |
断裂 fracture |
% | ISO 527-2/50 | |
弯曲模量 Bending modulus 4 |
|||
100 mm跨距 100 mm span |
MPa | ASTM D790 | |
-- -- |
MPa | ISO 178 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 类型 1, 2.0 in/min |
3 After 7 days |
4 0.49 in/min |
5 250 g |
【新闻资讯】查看全部
普立万推出生物基热塑性弹性体,成分来自甘蔗萃取物
2021-04-19 搜料网资讯: 普立万(PolyOne)推出reSoundOM(包覆成型)热塑性弹性体(TPE),为其可持续解决方案产品组合又添新成员。新配方40%~50%的成分来自从甘蔗萃取的生物可再生成分,在硬度和性能可 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |