牌号简介 About |
---|
己烯线性低密度树脂良好的强度和刚度符合美国FDA 21 177.1520(c)3.2a的要求。有关完整的详细信息,请参考相关法规。TUFLIN™ HS-7066 NT 7线性低密度聚乙烯树脂是一种分数熔融、乙烯-己烯共聚物、线性低密度(LLDPE)树脂,具有良好的韧性和刚度。本产品推荐用于薄和厚规格应用,如消费垃圾袋和工业重型运输袋,需要强度和机械加工性。 Hexene Linear Low Density Resin Good Strength and Stiffness Complies with U.S. FDA 21 177.1520 (c) 3.2a Consult the regulations for complete details. TUFLIN™ HS-7066 NT 7 Linear Low Density Polyethylene Resin is a fractional melt, ethylene-hexene copolymer, linear low density (LLDPE) resin designed for good toughness and stiffness. This product is recommended for thin and thick gauge applications such as consumer trash bags and industrial heavy-duty shipping sacks that require strength and machinability. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.926 | g/cm³ | ASTM D792 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
0.80 | g/10min | ASTM D1238 |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
膜刺穿强度 Membrane puncture strength |
内部方法 | ||
20 µm 20 µm |
2.37 | J | 内部方法 |
51 µm 51 µm |
5.42 | J | 内部方法 |
膜刺穿力 Membrane puncture force |
内部方法 | ||
20 µm 20 µm |
40.0 | N | 内部方法 |
51 µm 51 µm |
N | 内部方法 | |
膜耐刺穿性 Membrane puncture resistance |
内部方法 | ||
20 µm 20 µm |
J/cm³ | 内部方法 | |
51 µm 51 µm |
J/cm³ | 内部方法 | |
膜强度 Membrane strength |
ASTM D882 | ||
MD:20 µm MD:20 µm |
J/cm³ | ASTM D882 | |
MD:51 µm MD:51 µm |
J/cm³ | ASTM D882 | |
TD:20 µm TD:20 µm |
J/cm³ | ASTM D882 | |
TD:51 µm TD:51 µm |
J/cm³ | ASTM D882 | |
割线模量 Secant modulus |
ASTM D882 | ||
2% 正割,MD:20 µm 2% secant, MD: 20 µ m |
MPa | ASTM D882 | |
2% 正割,MD:51 µm 2% secant, MD: 51 µ m |
MPa | ASTM D882 | |
2% 正割,TD:20 µm 2% secant, TD: 20 µ m |
MPa | ASTM D882 | |
2% 正割,TD:51 µm 2% secant, TD: 51 µ m |
MPa | ASTM D882 | |
拉伸强度 tensile strength |
ASTM D882 | ||
MD,屈服,20 µm MD, yield, 20 µ m |
MPa | ASTM D882 | |
MD,屈服,51 µm MD, yield, 51 µ m |
MPa | ASTM D882 | |
TD,屈服,20 µm TD, yield, 20 µ m |
MPa | ASTM D882 | |
TD,屈服,51 µm TD, yield, 51 µ m |
MPa | ASTM D882 | |
MD,断裂,20 µm MD, fracture, 20 µ m |
MPa | ASTM D882 | |
MD,断裂,51 µm MD, fracture, 51 µ m |
MPa | ASTM D882 | |
TD,断裂,20 µm TD, fracture, 20 µ m |
MPa | ASTM D882 | |
TD,断裂,51 µm TD, fracture, 51 µ m |
MPa | ASTM D882 | |
拉伸应变 Tensile strain |
ASTM D882 | ||
MD,断裂,20 µm MD, fracture, 20 µ m |
% | ASTM D882 | |
MD,断裂,51 µm MD, fracture, 51 µ m |
% | ASTM D882 | |
TD,断裂,20 µm TD, fracture, 20 µ m |
% | ASTM D882 | |
TD,断裂,51 µm TD, fracture, 51 µ m |
% | ASTM D882 | |
落锤冲击 Gardner Impact |
|||
20 µm 20 µm |
g | ASTM D1709-A | |
20 µm 20 µm |
g | ASTM D1709-B | |
51 µm 51 µm |
g | ASTM D1709-A | |
51 µm 51 µm |
g | ASTM D1709-B | |
埃尔曼多夫抗撕强度 Elmandorf tear strength 2 |
ASTM D1922 | ||
MD:20 µm MD:20 µm |
g | ASTM D1922 | |
MD:51 µm MD:51 µm |
g | ASTM D1922 | |
TD:20 µm TD:20 µm |
g | ASTM D1922 | |
TD:51 µm TD:51 µm |
g | ASTM D1922 | |
始封温度 Initial sealing temperature 3 |
内部方法 | ||
20 µm 20 µm |
℃ | 内部方法 | |
51 µm 51 µm |
℃ | 内部方法 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
维卡软化温度 Vicat Softening Temperature |
℃ | ASTM D1525 | |
熔融温度 Melting temperature |
|||
DSC DSC |
℃ | 内部方法 | |
光学性能 OPTICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
光泽度 gloss |
ASTM D2457 | ||
20°,20.3 µm 20°,20.3 µm |
ASTM D2457 | ||
20°,50.8 µm 20°,50.8 µm |
ASTM D2457 | ||
45°,20.3 µm 45°,20.3 µm |
ASTM D2457 | ||
45°,50.8 µm 45°,50.8 µm |
ASTM D2457 | ||
雾度 Haze |
ASTM D1003 | ||
20.3 µm 20.3 µm |
% | ASTM D1003 | |
50.8 µm 50.8 µm |
% | ASTM D1003 | |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密封强调 Sealing emphasis 4 |
内部方法 | ||
160℃,20.3 µm 160℃,20.3 µm |
g | 内部方法 | |
180℃,50.8 µm 180℃,50.8 µm |
g | 内部方法 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 方法 B |
3 实现 1 磅/英寸 (4.4 N/25.4 mm) 热封强度的温度。 热封强度,Topwave HT 测试仪 0.5 S 保压,40 psi 压力,拉动速度 10(英寸/分)。 |
4 热封强度,Topwave HT 测试仪 0.5 S 保压,40 psi 压力,拉动速度 10(英寸/分)。 |
【新闻资讯】查看全部
中科炼化成功生产聚丙烯双向拉伸薄膜材料
2022-07-21 7月15日,中科炼化35万吨/年聚丙烯装置成功生产1000吨双向拉伸薄膜产品,进一步丰富了无规共聚系列聚丙烯产品的结构。 双向拉伸薄膜产品无毒、无味、防潮、美观,被誉为包装女王 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |