牌号简介 About |
---|
BaydUR 646是一种用于反应注射成型(RIM)工艺的硬质聚氨酯结构发泡体系。该系统作为两种反应性液体成分提供:组分A是聚合物二苯甲烷二异氰酸酯(PMDI),组分B是不含CFC-或HCFC发泡添加剂的配方多元醇系统。BaydUR 646系统用于生产复合材料的泡沫芯,例如滑水板、尾板、雪板以及运输和海洋市场的各种部件。与任何产品一样,在给定应用中使用Baydur 646系统必须由用户提前进行测试(包括现场测试等),以确定适用性。 Baydur 646 is a rigid polyurethane structural foam system used in the reaction injection molding (RIM) process. The system is supplied as two reactive liquid components: Component A is a polymeric diphenylmethane diisocyanate (PMDI), and Component B is a formulated polyol system containing no CFC- or HCFC-blowing additives. The Baydur 646 system is used to produce foam cores for composite applications, such as water skis, wake boards, snow boards, and various components for the transportation and marine markets. As with any product, use of the Baydur 646 system in a given application must be tested (including field testing, etc.) in advance by the user to determine suitability. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.399 | g/cm³ | ASTM D792 |
收缩率 Shrinkage rate |
|||
MD:6.35 mm MD:6.35 mm |
0.30 到 0.50 | % | ASTM D955 |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
内部方法 | ||
-- -- 2 |
7.4 | kJ/m² | 内部方法 |
-- -- 3 |
8.0 | kJ/m² | 内部方法 |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热固组件 Thermosetting components |
|||
部件 A Component A |
按重量计算的混合比: 110 | ||
部件 B Component B |
|||
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
ASTM D2240 | ||
邵氏 D,6.35 mm Shaw D, 6.35 mm |
ASTM D2240 | ||
邵氏 D,12.70 mm Shore D, 12.70 mm |
ASTM D2240 | ||
拉伸强度 tensile strength |
ASTM D638 | ||
断裂,6.35 mm Fracture, 6.35 mm |
MPa | ASTM D638 | |
断裂,12.70 mm Fracture, 12.70 mm |
MPa | ASTM D638 | |
拉伸应变 Tensile strain |
ASTM D638 | ||
断裂,6.35 mm Fracture, 6.35 mm |
% | ASTM D638 | |
断裂,12.70 mm Fracture, 12.70 mm |
% | ASTM D638 | |
弯曲模量 Bending modulus |
ASTM D790 | ||
6.35 mm 6.35 mm |
MPa | ASTM D790 | |
12.70 mm 12.70 mm |
MPa | ASTM D790 | |
弯曲强度 bending strength |
ASTM D790 | ||
6.35 mm 6.35 mm |
MPa | ASTM D790 | |
12.70 mm 12.70 mm |
MPa | ASTM D790 | |
压缩强度 compressive strength |
ASTM D695 | ||
6.35 mm 6.35 mm |
MPa | ASTM D695 | |
12.7 mm 12.7 mm |
MPa | ASTM D695 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 0.5 |
3 0.25 in |
【新闻资讯】查看全部
我国塑料管材行业开展制约要素解析
2016-09-27 目前全国塑料管材市场化程度较高,生产经营企业数量较多,但以中小企业为主,企业的竞争能力弱,规模经济差,而且由于塑料管材行业品牌意识淡漠,市场秩序混乱,结构不合理,造成技术壁垒较低的普通管材生产能力过剩,而技术含量较高的城镇燃气、给水、排水排污用PE压力管道以及大口径塑料管材还不能完全满足市场需求,尤其是技术含量高、生产工艺复杂的管件,如电熔管件和PE球阀,能生产的厂家更少,能够提供全系列产品配套的厂家则更在少数,一些管件尚需要进口。另外国家级大型交通、能源工程项目需要的合格超大口径塑料管材 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |