牌号简介 About |
---|
21.采用Unipol PP技术,采用高活性催化剂体系的气相流化床反应器,制备了具有成核和抗静电性能的熔体流动均聚聚丙烯,用于注塑成型,聚丙烯1120H,确保了物理性能的均匀性和批次间的一致性。本产品适用于餐具、瓶盖和薄壁容器的通用注塑成型。1120H含有成核剂和抗静电添加剂包装。1120H产品提供:优良的颜色和加工稳定性,良好的流动特性,低气味和味道,抗静电性能,UL列出的Pinnacle的聚丙烯,由Pinnacle聚合物销售,天然,未着色颗粒形式,符合CFR标题21,第177部分,B子部分,第177.1520(c)1.1a节的适当要求。美国食品、药品和化妆品法案1958年食品添加剂修正案中的“烯烃聚合物”。 21 MELT FLOW HOMOPOLYMER POLYPROPYLENE WITH NUCLEATION AND ANTISTAT FOR INJECTION MOLDING Pinnacle Polymers Polypropylene 1120 H is made via UNIPOL™ PP technology, which utilizes gas-phase fluidized bed reactors with a high activity catalyst system to ensure uniform physical properties and lot-to-lot consistency. This product is intended for general-purpose injection molding of cutlery, closures and thin wall containers. 1120 H contains both a nucleation and antistatic additive package. The 1120 H product provides: Superior color and processing stability Good flow characteristics Low odor and taste Antistatic properties UL Listed Pinnacle's polypropylene, as marketed by Pinnacle Polymers, in natural, uncolored pellet form complies with appropriate requirements of CFR Title 21, Part 177, Subpart B, Section 177.1520 (c) 1.1a entitled "Olefin Polymers" of the Food Additives Amendment of 1958 to the United States Food, Drug and Cosmetic Act of 1938. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.900 | g/cm³ | ASTM D1505 |
熔体质量流动速率 Melt Flow Rate |
|||
230℃,2.16kg 230℃,2.16kg |
21 | g/10min | ASTM D1238 |
收缩率 Shrinkage rate |
|||
MD MD |
1.4 | % | ASTM D955 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength 3 |
|||
屈服,3.20 mm,注塑成型 Yield, 3.20 mm, injection molding 3 |
39.3 | MPa | ASTM D638 |
拉伸应变 Tensile strain 3 |
|||
屈服,3.20 mm,注塑成型 Yield, 3.20 mm, injection molding 3 |
8.0 | % | ASTM D638 |
弯曲模量 Bending modulus 4 |
|||
1% 正割,3.20 mm,注塑成型 1% cut, 3.20 mm, injection molded 4 |
MPa | ASTM D790-A | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch 5 |
|||
23℃,3.2mm,注塑成型 23 ℃, 3.2mm, injection molding 5 |
kJ/m² | ASTM D256 | |
23℃,3.2mm,注塑成型 23 ℃, 3.2mm, injection molding 5 |
J/m | ASTM D256 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ASTM D648 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 类型 1, 2.0 in/min |
3 类型 1, 0.050 in/min |
4 Type I |
【新闻资讯】查看全部
美国空军学院学员使用环氧树脂制成新型防弹盔甲
2017-05-24 美国空军学院学员通过在课堂练习中将粘性体制成的新的防弹盔甲,证明了学校课程的作用不仅仅是翻新旧地。2014年,一年级的Hayley Weir将环氧树脂,芳纶纤维和碳纤维复合成一种防弹材料的任务启发了她将这项任务发展成一种新型的柔性弹塞。 复合护甲并不新颖,而且Weir的任务只是一个标准规格的任务,但是她对结果并不满意,虽然该复合物可能会阻止一个子弹,但是材料本身太硬而且易碎。根据学院化学顾问的建议,她用剪切增稠的液体换掉了环氧树脂。 这也不是新的物质。剪切增 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |