牌号简介 About |
---|
TA210LW是一种低磨损的无增强聚酰胺66产品。 Features TA210LW is a unreinforced polyamide 66 product for low wear friction. Application Chair parts. Drying Product is dried and packed with a moisture content of <0.16%. Should the packing become damaged or be left open too long, then the material must be dried. A too high moisture content can lead to a reduction of optical and mechanical properties. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.14 | g/cm³ | ASTM D792 |
收缩率 Shrinkage rate |
|||
MD MD |
1.5 | % | ASTM D955 |
吸水率 Water absorption rate |
|||
23℃,24hr 23℃,24hr |
1.2 | % | ASTM D570 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength 2 |
|||
断裂 fracture 2 |
83.4 | MPa | ASTM D638 |
拉伸应变 Tensile strain 2 |
|||
断裂 fracture 2 |
65 | % | ASTM D638 |
弯曲模量 Bending modulus 3 |
MPa | ASTM D790 | |
弯曲强度 bending strength 3 |
MPa | ASTM D790 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
23℃,3.2mm 23℃,3.2mm |
J/m | ASTM D256 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
ASTM D648 | ||
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ASTM D648 | |
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ASTM D648 | |
熔融峰值温度 Melting peak temperature |
℃ | ASTM D3418 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
UL 94 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 2.0 in/min |
3 0.12 in/min |
【新闻资讯】查看全部
将来中国塑料制操行业大有可为!
2018-08-10 经过数十年的快速发展,我国塑料制品行业发生了巨大的变化。特别是近年来,我国塑料制品行业在产业结构调整、转型和升级中不断发展,保持快速发展的态势,产销量都位居全球首 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |