牌号简介 About |
---|
高性能热塑性材料聚芳醚酮(PAEK),用耐磨添加剂增强,半结晶,注射成型颗粒,易流动,符合FDA食品接触标准,颜色为黑色。WG101不含聚四氟乙烯(PTFE)或其他卤化添加剂。具有较薄横截面或较长流动长度、较高强度和刚度的摩擦学应用。优异的耐磨性,极低的摩擦系数和低的热膨胀系数。抗腐蚀环境的化学反应。 High performance thermoplastic material, PolyArylEtherKetone (PAEK), reinforced with wear additives, semi crystalline, granules for injection moulding, easy flow, FDA food contact compliant, colour black. WG101 does not contain polytetrafluoroethylene (PTFE) or other halogenated additives. Tribological applications with thin cross sections or long flow lengths, with higher strength and stiffness. Excellent wear resistance, very low coefficient of friction and low coefficient of thermal expansion. Chemically resistant to aggressive environments. |
技术参数 Technical Data | |||
---|---|---|---|
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy notched Impact strength Charpy Notched Impact Strength |
|||
23℃ 23℃ |
5.0 | kJ/m² | ISO 179/1eA |
简支梁无缺口冲击强度 Charpy Unnotched Impact strength Charpy Unnotch Impact strength |
|||
23℃ 23℃ |
35 | kJ/m² | ISO 179/1U |
悬臂梁缺口冲击强度 Izod Notched Impact strength Izod Notched Impact strength |
|||
23℃ 23℃ |
6.0 | kJ/m² | ISO 180-A |
悬臂梁无缺口冲击强度 Izod Unnotched Impact strength Izod Unnotched Impact strength of cantilever beam |
|||
23℃ 23℃ |
35 | kJ/m² | ISO 180 |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 HDT Hot deformation temperature HDT |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
343 | ℃ | ISO 75-2/Af |
玻璃化转变温度 Glass Transition Temperature Glass Transition Temperature |
ISO 11357-2 | ||
-- -- |
℃ | ISO 11357-2 | |
-- -- |
℃ | ISO 11357-2 | |
熔融温度 Melting temperature Melting temperature |
℃ | ISO 11357-3 | |
线性热膨胀系数 Coeff.of linear therm expansion Coeff. of linear thermal expansion |
ISO 11359-2 | ||
MD:< 143℃ MD:< 143℃ |
1/℃ | ISO 11359-2 | |
MD:> 143℃ MD:> 143℃ |
1/℃ | ISO 11359-2 | |
TD:< 143℃ TD:< 143℃ |
1/℃ | ISO 11359-2 | |
TD:> 143℃ TD:> 143℃ |
1/℃ | ISO 11359-2 | |
导热系数 Thermal Conductivity Thermal conductivity |
ISO 22007-4 | ||
23℃ 23℃ |
W/m/K | ISO 22007-4 | |
23℃ 23℃ |
W/m/K | ISO 22007-4 | |
电气性能 ELECTRICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
体积电阻率 Volume Resistivity Volume Resistance |
|||
23℃ 23℃ |
ohms·cm | IEC 60093 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness Shore hardness |
|||
邵氏 D,23℃ Shore D, 23 ℃ |
ISO 868 | ||
拉伸模量 Tensile Modulus Tensile Modulus |
|||
23℃ 23℃ |
MPa | ISO 527-2 | |
拉伸强度 Tensile Strength Tensile Strength |
ISO 527-2 | ||
断裂 brk,23℃ Broken BRK, 23 ℃ |
MPa | ISO 527-2 | |
断裂 brk,125℃ Broken BRK, 125 ℃ |
MPa | ISO 527-2 | |
断裂 brk,175℃ Broken BRK, 175 ℃ |
MPa | ISO 527-2 | |
断裂 brk,225℃ Broken BRK, 225 ℃ |
MPa | ISO 527-2 | |
断裂 brk,275℃ Broken BRK, 275 ℃ |
MPa | ISO 527-2 | |
拉伸应变 Tensile Strain Tensile Strain |
|||
断裂 brk,23℃ Broken BRK, 23 ℃ |
% | ISO 527-2 | |
弯曲模量 Flexural Modulus Flexural Modulus |
|||
23℃ 23℃ |
MPa | ISO 178 | |
弯曲强度 Flexural Strength Flexural Strength |
ISO 178 | ||
23℃ 23℃ |
MPa | ISO 178 | |
125℃ 125℃ |
MPa | ISO 178 | |
175℃ 175℃ |
MPa | ISO 178 | |
275℃ 275℃ |
MPa | ISO 178 | |
压缩强度 Compressive Strength Compressive Strength |
ISO 604 | ||
23℃ 23℃ |
MPa | ISO 604 | |
120℃ 120℃ |
MPa | ISO 604 | |
200℃ 200℃ |
MPa | ISO 604 | |
250℃ 250℃ |
MPa | ISO 604 | |
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density Density |
g/cm³ | ISO 1183 | |
螺旋流动长度 spiral flow length Spiral flow length |
cm | 内部方法 | |
成型收缩率 Molding Shrinkage Molding shrinkage |
ISO 294-4 | ||
TD TD |
% | ISO 294-4 | |
MD MD |
% | ISO 294-4 | |
吸水率 Water Absorption Water Absorption |
|||
饱和,23℃ Saturation, 23 ℃ |
% | ISO 62 | |
饱和,100℃ Saturation, 100 ℃ |
% | ISO 62 | |
表观粘度 Apparent viscosity Apparent viscosity |
|||
400℃ 400℃ |
Pa·s | ISO 11443 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 Crystalline |
3 模具温度: 392°F, 熔体温度: 734°F |
4 1 mm |
5 390°C nozzle, 200°C tool |
6 Onset |
7 Midpoint |
8 Average |
9 Along flow |
10 1V |
【新闻资讯】查看全部
发展数字经济,代表委员最关注什么
2022-03-16 今年全国两会期间,数字经济再次成为代表委员们关注的热点。他们围绕数字经济这一领域,为工业软件国产化、数据安全、数据权立法等话题建言献策,同时对双碳、中小企业数字化 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |