牌号简介 About |
---|
EEC MD 3904 U是一种聚乙烯产品,。 它可以通过滚塑成型进行加工,在非洲和中东或欧洲有供货。 EEC MD 3904 U的应用领域包括罐子、容器、工业应用、农业 和 生活消费品。 特性包括: 良好的抗紫外线能力 紫外线稳定 EEC MD 3904 U is a Polyethylene product. It can be processed by rotational molding and is available in Africa & Middle East or Europe. Applications of EEC MD 3904 U include containers, tanks, agricultural, consumer goods and industrial applications. Characteristics include: UV Resistant UV Stabilized |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.939 | g/cm³ | ASTM D1505 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
3.5 | g/10min | ASTM D1238 |
抗环境应力开裂 ESCR(Environmental Stress Cracking Resistance) |
|||
23℃,100%非离子型表面活性剂,F50 23 ℃, 100% non-ionic surfactant, F50 |
> 150 | hr | ASTM D1693B |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
脆化温度 Embrittlement temperature |
< -75.0 | ℃ | ASTM D746 |
维卡软化温度 Vicat Softening Temp |
119 | ℃ | ASTM D1525 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
ASTM D2240 | ||
拉伸强度 tensile strength |
ASTM D638 | ||
屈服 yield |
MPa | ASTM D638 | |
断裂 fracture |
MPa | ASTM D638 | |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ASTM D638 | |
弯曲模量 Bending modulus |
|||
1% 正割 1% secant |
MPa | ASTM D790 | |
弯曲强度 bending strength |
MPa | ASTM D790 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
塑料生产企业喜欢防老剂
2015-11-24 和其它高分子材料一样,聚氨酯泡沫塑料在光、热等外界因素作用下会发生老化,发生黄变,材料的物理性能会下降。添加抗氧剂、紫外光吸收剂等防老剂会延缓这种作用。 在聚氨酯原料或配方中加入微量的抗氧剂即可起阻滞聚氨酯热氧化的作用。抗氧剂的作用在于阻止氧诱发引起的聚合物的断链反应和分解生成的过氧化氢。 受阻酚类化合物是最常用的聚氨酯材料的抗氧剂。例如:1,3,5―三甲基―2,4,6―三(3’,5’―二叔丁基)―4―羟基苄基苯、2―(2‘―羟基―3’―叔烷基苄基)苯甲醚、 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |