PMC-780是一种高性能聚氨酯橡胶,具有优异的强度、耐用性和耐磨性。PMC-780不含MOCA——一种已知的致癌剂和危害。以重量计,将两份A至一份B混合,PMC-780易于浇注,在室温下固化,收缩率可忽略不计,可制成固体肖氏80A橡胶。选择一个最适合您的应用:原始的PMC-780干燥不渗出油。新的PMC-780湿含有一个内置的释放剂,以帮助拆模混凝土。(注:“湿”橡胶与“干”橡胶相比,随着时间的推移,其净收缩值更高。)这两种橡胶都在世界各地用于铸造磨料材料,如混凝土(预制混凝土、制作混凝土冲压垫等)和石膏灰泥,具有较高的放热性。PMC-780干燥也常用于制造各种配置的橡胶机械零件(垫圈、车轮和拉力),以及球磨机衬板和振动/冲击垫。 PMC-780 is a premium performance urethane rubber that offers exceptional strength, durability and abrasion resistance. PMC-780 DOES NOT CONTAIN MOCA - a known cancer causing agent and hazard. Mixed two parts A to one part B by weight, PMC-780 pours easily and cures at room temperature with negligible shrinkage to a solid Shore 80A rubber. Pick The One Best Suited For Your Application: Original PMC-780 Dry does not exude oil. New PMC-780 Wet contains a built-in release agent to aid in demolding concrete. (Note: "wet" rubber has a higher net shrinkage value over time vs. "dry " rubber.) Both are used around the world for casting abrasive materials such as concrete (pre-cast concrete, making concrete stamping pads, etc.) and gypsum plasters with high exotherms. PMC-780 Dry is also commonly used to make rubber mechanical parts of varying configurations (gaskets, wheels, and pullies) as well as ball mill liners and vibration/shock pads. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.02 | g/cm³ | ASTM D1475 |
特定体积 Specific volume |
0.983 | cm³/g | |
收缩率 Shrinkage rate |
|||
MD MD |
< 0.10 | % | ASTM D2566 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 A Shaw's A |
80 | ASTM D2240 | |
弹性体 elastic body |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
|||
断裂 fracture |
6.21 | MPa | ASTM D412 |
100% 应变 100% strain |
MPa | ASTM D412 | |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ASTM D412 | |
撕裂强度 tear strength 2 |
kN/m | ASTM D624 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
储存稳定性 storage stability |
|||
23℃ 23℃ |
min | ASTM D2471 | |
热固性混合粘度 Thermosetting mixed viscosity |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
脱模时间 stripping time |
|||
23℃ 23℃ |
min | ||
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
混合比 Mixing ratio |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 C 模具 |
【新闻资讯】查看全部
橡塑机械行业进出口数据汇总
2018-01-02 截止12月30日,橡塑机械行业部分进出口数据已经出炉。数据显示,2017年前11个月,我国外贸进出口达到了25.14万亿元人民币,同比增长15.6%。 据报道,12月28日,商务部召开例行新闻发布会,新闻发言人高峰表示,我国今年前11个月进出口贸易表现良好,增长呈双位数,按照这个速度,如果不出现特殊的情况,预计今年我国的外贸进出口将再次突破4万亿美元。那么,中国橡塑机械行业进出口情况如何呢? |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |