牌号简介 About |
---|
Noryl NH6010B树脂NORYL™ NH6010B resin是一种高性能的改性PPE-PS混合物,具有燃烧时低烟产生、无卤阻燃和低比重的良好平衡。这一等级可以通过挤压或注射成型加工。Noryl NH6010B可定制颜色,可能是建筑、建筑和电气市场中使用的理想材料。 NORYL NH6010B resin is a high performance, modified PPE-PS blend that exhibits an excellent balance of lower smoke production upon burning, nonhalogenated flame retardance and low specific gravity. This grade can be processed via extrusion or injection molding. NORYL NH6010B is available in custom colors and may be an excellent material candidate for use in building and construction and electrical markets. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.11 | g/cm³ | ASTM D792 |
密度 Density |
1.12 | g/cm³ | ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
|||
280℃,5.0kg 280℃,5.0kg |
5.7 | g/10min | ASTM D1238 |
熔体体积流动速率 Melt Volume Rate |
|||
280℃,5 kg 280℃,5 kg |
5.70 | cm³/10min | ISO 1133 |
收缩率 Shrinkage rate |
|||
MD:3.2 mm MD:3.2 mm |
0.50 to 0.80 | % | 内部方法 |
吸水率 Water absorption rate |
|||
饱和,23℃ Saturation, 23 ℃ |
% | ISO 62 | |
平衡,23℃,50% RH Equilibrium, 23 ℃, 50% RH |
% | ISO 62 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus 2 |
MPa | ASTM D638 | |
拉伸模量 Tensile modulus |
MPa | ISO 527-1-2 | |
拉伸强度 tensile strength |
|||
断裂 fracture 3 |
MPa | ASTM D638 | |
断裂 fracture |
MPa | ISO 527-2/50 | |
屈服 yield 3 |
MPa | ASTM D638 | |
屈服 yield |
MPa | ISO 527-2/50 | |
拉伸应变 Tensile strain 3 |
|||
断裂 fracture 4 |
% | ASTM D638 | |
断裂 fracture |
% | ISO 527-2/50 | |
屈服 yield |
% | ISO 527-2/50 | |
屈服 yield 3 |
% | ASTM D638 | |
弯曲模量 Bending modulus 5 |
MPa | ISO 178 | |
50 mm跨距 50 mm span 4 |
MPa | ASTM D790 | |
弯曲强度 bending strength 5 , 6 |
MPa | ISO 178 | |
弯曲强度 bending strength 4 |
|||
屈服,50 mm跨度 Yield, 50 mm span 4 |
MPa | ASTM D790 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength 7 |
|||
23℃ 23℃ 7 |
kJ/m² | ISO 179/1eA | |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
ASTM D256 | ||
-30℃ -30℃ |
J/m | ASTM D256 | |
23℃ 23℃ |
J/m | ASTM D256 | |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch 8 |
ISO 180/1A | ||
-30℃ -30℃ |
kJ/m² | ISO 180-1A | |
23℃ 23℃ |
kJ/m² | ISO 180-1A | |
装有测量仪表的落镖冲击 Dart impact equipped with measuring instruments |
|||
23℃,Total Energy 23℃,Total Energy |
J | ASTM D3763 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火,64 mm跨距 1.8 MPa, unannealed, 64 mm span 9 |
℃ | ISO 75-2/Af | |
1.8 MPa,未退火,3.2 mm 1.8 MPa, unannealed, 3.2 mm |
℃ | ASTM D648 | |
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 10 | |
维卡软化温度 Vicat Softening Temp |
|||
B50 B50 |
℃ | ISO 306 | |
B120 B120 |
℃ | ISO 306/B120 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
TD:-40~40℃ TD:-40~40℃ |
1/℃ | ISO 11359-2 | |
TD:-40~40℃ TD:-40~40℃ |
1/℃ | ASTM E831 | |
MD:-40~40℃ MD:-40~40℃ |
1/℃ | ASTM E831 | |
MD:-40~40℃ MD:-40~40℃ |
1/℃ | ISO 11359-2 | |
相对温度指数 Relative temperature index |
|||
电气性能 Electrical performance |
℃ | UL 746 | |
强度机械性能 Strength mechanical performance |
℃ | UL 746 | |
冲击机械性能 Impact mechanical performance |
℃ | UL 746 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
表面电阻率 Surface resistivity |
ohms | ASTM D257 | |
表面电阻率 Surface resistivity |
ohms | IEC 60093 | |
体积电阻率 Volume resistivity |
ohms·cm | ASTM D257 | |
体积电阻率 Volume resistivity |
ohms·cm | IEC 60093 | |
介电强度 Dielectric strength |
|||
3.2 mm,在油中 3.2 mm in oil |
kV/mm | IEC 60243-1 | |
3.2 mm,在油中 3.2 mm in oil |
kV/mm | ASTM D149 | |
介电常数 Dielectric constant |
|||
1 MHz 1 MHz |
ASTM D150 | ||
相对电容率 Relative permittivity |
|||
1 MHz 1 MHz |
IEC 60250 | ||
耗散因数 Dissipation factor |
|||
1 MHz 1 MHz |
IEC 60250 | ||
1 MHz 1 MHz |
ASTM D150 | ||
相比漏电起痕指数 Compared to the leakage tracing index |
V | IEC 60112 | |
高电弧燃烧指数(HAI) High Arc Burning Index (HAI) |
UL 746 | ||
热丝引燃 Hot wire ignition |
|||
HWI HWI |
UL 746 | ||
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
|||
1.50 mm 1.50 mm |
UL 94 | ||
灼热丝可燃性指数 Glowing wire flammability index |
|||
1.6 mm 1.6 mm |
℃ | IEC 60695-2-12 | |
灼热丝起燃温度 Igniting temperature of the hot wire |
IEC 60695-2-13 | ||
1 mm 1 mm |
℃ | IEC 60695-2-13 | |
2 mm 2 mm |
℃ | IEC 60695-2-13 | |
3 mm 3 mm |
℃ | IEC 60695-2-13 | |
极限氧指数 Extreme oxygen index |
% | ISO 4589-2 | |
Ds_4min Ds_4min |
ISO 5659-2 | ||
F1 Class Smoke and Toxicity Rating F1 Class Smoke and Toxicity Rating |
mm | NF F16-101 | |
Flame Spread Index(1.52 mm) Flame Spread Index(1.52 mm) |
ASTM E162 | ||
散热量 Heat dissipation |
|||
MAHRE MAHRE |
kW/m² | ISO 5660-1 | |
Lateral Flame Spread(CFE) Lateral Flame Spread(CFE) |
kW/m² | ISO 5658-2 | |
M1 Flame Class Rating M1 Flame Class Rating |
mm | NF P 92501 | |
NBS烟雾密度 NBS smoke density |
ASTM E662 | ||
Flaming,20 min:3.20 mm Flaming,20 min:3.20 mm |
ASTM E662 | ||
Flaming,4 min:1.52 mm Flaming,4 min:1.52 mm |
ASTM E662 | ||
Flaming,4 min:3.20 mm Flaming,4 min:3.20 mm |
ASTM E662 | ||
Non-Flaming,4 min:1.52 mm Non-Flaming,4 min:1.52 mm |
ASTM E662 | ||
毒性 toxicity |
|||
-- -- |
ISO 5659-2 | ||
3.00 mm 3.00 mm |
NF X70-100 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 0,20 in/min |
3 类型 1, 2,0 in/min |
4 0,051 in/min |
5 0,079 in/min |
6 Yield |
7 80*10*4 sp=62mm |
8 80*10*4 |
9 80*10*4 mm |
10 标准 B (120°C/h), 载荷2 (50N) |
【新闻资讯】查看全部
打印人体部位,3D系统公司(DDD)股价飙升28%
2021-06-23 搜料网资讯: 3D Systems (DDD)和以色列再生医药公司生物技术公司CollPlant Biotechnologies (CLGN)宣布他们已经签署了一项联合开发协议,将3D生物打印再生软组织基质用于乳房重建手术,并结合 |
打印人体部位,3D系统公司(DDD)股价飙升28% 搜料网资讯:3D Systems (DDD)和以色列再生医药公司生物技术公司CollPlant Biotechnologies (CLGN)宣布他们已经签署了一项联合开发协议,将3D生物打印再生软组织基质用于乳房重建手术,并结合植入物。DDD今日大涨了28%,CLGN大涨13%。 根据世界卫生组织的数据,到2020年,全球共有230万女性被诊断出患有乳腺癌,其中绝大多数需要摘除部分或全部乳房组织。 3D Systems和CollPlant使用rhCollagen开发3D生物打印软组织基质。正在开发的3D生物打印软组织基质产品旨在满足所需的物理和机械性能,同时通过使用基于rhCollagen促进组织再生的生物墨水配方促进细胞浸润和增殖。 具体来说,这对合作伙伴将用3D打印技术打印出一种“软组织基质”,在这种基质上,人体可以生长新的皮肤,在接受乳房切除术后的重建手术的患者中,这种基质将起到“支持乳房下部”的作用。 研究中的基质将使用基于植物的重组人胶原蛋白(rhCollagen)作为其“生物墨水”,而不是其他3D打印产品中用作“墨水”的金属或塑料或类似原材料。 使用3D Systems和CollPlant的专业知识和解决方案设计并生产了具有红墨水灌注血管化通道的3D生物打印软组织支架。
CollPlant是一家再生和美学医学公司,专注于组织和器官的3D生物打印和医学美学。CollPlant最近与艾伯维公司Allergan签订了皮肤和软组织填充剂的开发和全球商业化协议。Allergan是皮肤填充剂市场的全球领导者。 据两家公司介绍,rhCollagen“不会引起人体的不良免疫反应”,因为他们的植物起源和相同的天然人体胶原蛋白,不会引起人体的不良免疫反应。而且“具有卓越的性能、一致性和安全性”,使其成为此类重建手术的理想选择。 虽然这两家公司没有强调这一点,但似乎同样的rhCollagen也可以在其他重建和整形手术中使用。投资者在这里看到的是一个潜在的突破和一个通过3D打印机制造人体部件的全新行业。 现在,3D Systems正在这样做,它的同行们可能很快就会跟进。
交易员们今天交易了85164份DDD的看涨期权,比17,786平均日交易量增加了约379%。 几家机构投资者和对冲基金最近改变了他们在该公司的头寸。 第一季度,PNC金融服务集团(PNC Financial Services Group Inc.)增持了3D Systems的8.5%。PNC金融服务集团在上个季度购买了648股3D打印公司股票后,现在拥有8271股股票,价值22.7万美元。 第一季度,亚利桑那州退休系统公司购买了1,009股3D打印公司股票后,现在拥有36,138股3D打印公司股票,价值992,000美元。 Prudential Financial在3D Systems的份额上升了0.7%。目前持有该3D打印公司142,397股股票,价值3,907,000美元,此前该公司在此期间购买了另外1,010股股票。 另外,执行副总裁Andrew Martin Johnson在5月26日周三的一笔交易中出售了4000股3D Systems股票。该股以27.29美元的平均价格出售,总成交价为109,160美元。 执行副总裁Menno Ellis在5月17日周一的一笔交易中出售了10573股3D Systems股票。该股以22.49美元的平均价格出售,总成交价为237,786.77美元。 在过去的90天里,内部人士已经卖出了24573股公司股票,价值565,947美元。内部人士持有公司3.60%的股份。 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |
价格走势图
抱歉!该牌号暂无认证数据。
- NORYL树脂光伏接线盒
- 2022-10-18 0
- NORYL树脂具有优秀的尺寸稳定性、电气和热性能,能耐受-40°C至140°C的温度,长期在户外的湿热环境使用后,还可保持85%以上的性能,且具有低翘曲特性,满足对接线盒材料的高要求