| 牌号简介 About |
|---|
| SABIC® HDPE F0863树脂是气相技术生产的一种高密度均聚物。该级具有高刚度、耐高温、低水蒸气透过率和非常低的凝胶水平。由于线性特性，建议将该材料与挤出涂层LDPE等级（如SABIC LDPE 2005EC）结合使用，以提高挤出涂层的可加工性（机动载荷和缩颈）。应用SABIC® HDPE F0863通常用于食品包装、离型纸和相纸。本产品不适用于任何医药/医疗应用，也不得用于任何医药/医疗应用。 SABIC® HDPE F0863 resin is a homopolymer with a very high density manufactured by gas phase technology. The grade offers high stiffness, high temperature resistance, low water vapour transmission and a very low gel level. Because of the linear character it is advisable to use the material in combination with extrusion coating LDPE grades like SABIC® LDPE 2005EC in order to improve extrusion coating processability (motorload and Neck In). Application SABIC® HDPE F0863 is typically used for food packaging, release paper and photographic paper. This product is not intended for and must not be used in any pharmaceutical/medical applications. |
产品描述 Product Description
用途：母料;离型纸;食品包装;复合;涂层应用;
加工条件：挤出涂层
性能特点： 机械强度好; 低速凝固晶点; 高密度; 抗氧化; 均聚物; 耐高温; Good Rigidity,Low speed solidification point,High Heat Resistance,Inoxidizability,High density,Homopolymer
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
0.964 | g/cm³ | ISO 1183 |
|
熔体质量流动速率 Melt Flow Rate |
|||
|
190℃，2.16kg 190℃，2.16kg |
8.0 | g/10min | ISO 1133 |
|
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
薄膜厚度 film thickness |
|||
|
测试 test |
25 | µm | |
|
拉伸模量 Tensile modulus |
ISO 527-3 | ||
|
MD，25 µm，铸造薄膜 MD, 25 µ m, cast thin film |
580 | MPa | |
|
TD，25 µm，铸造薄膜 TD, 25 µ m, cast thin film |
580 | MPa | |
|
拉伸强度 tensile strength |
ISO 527-3 | ||
|
MD，屈服，25 µm，吹塑薄膜 MD, yield, 25 µ m, blow molded film |
MPa | ||
|
TD，屈服，25 µm，吹塑薄膜 TD, yield, 25 µ m, blow molded film |
MPa | ||
|
MD，断裂，25 µm，吹塑薄膜 MD, fracture, 25 µ m, blow molded film |
MPa | ||
|
TD，断裂，25 µm，吹塑薄膜 TD, fracture, 25 µ m, blow molded film |
MPa | ||
|
拉伸应变 Tensile strain |
ISO 527-3 | ||
|
MD，断裂，25 µm，铸造薄膜 MD, fracture, 25 µ m, cast thin film |
% | ||
|
TD，断裂，25 µm，铸造薄膜 TD, fracture, 25 µ m, cast thin film |
% | ||
|
透氧率 Oxygen permeability |
|||
|
23℃，25 µm，铸造薄膜 23 ℃, 25 µ m, cast thin film |
cm³/m²/24 hr | 内部方法 | |
|
水气透过率 Water vapor transmittance |
|||
|
38℃，100% RH，25 µm，铸造薄膜 38 ℃, 100% RH, 25 µ m, cast thin film |
g/m²/24 hr | 内部方法 | |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
维卡软化温度 Vicat Softening Temp |
℃ | ISO 306/A | |
|
熔融温度 Melting temperature |
|||
|
DSC DSC |
℃ | DIN 53765 | |
|
Enthalpy Change Enthalpy Change |
J/g | DIN 53765 | |
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
| 2 Measured on pilot line at 200 m/min, 300°C, 10 g/m², airgap 300 mm |
| 3 Measured on pilot line at 400 m/min, 300°C, airgap 300 mm |
|
【新闻资讯】查看全部
巴菲特收购德国管道供应商Wilhelm Schulz GmbH
2017-01-24 据德媒23日报道，美国亿万富翁巴菲特将通过旗下精密铸件公司(Precision Castparts)收购德国管道组成件生产商Wilhelm Schulz GmbH。 精密铸件公司两年前被巴菲特旗下的伯克希尔哈撒伟公司以370亿美元的价格收购。该公司首席执行官Mark Donegan向德媒证实了这一交易，但拒绝透露交易价格。 德国反垄断监管机构目前正在评估这项交易，如果获得批准，这将是巴菲特在德国进行的第二起收购。两年前，伯克希尔哈撒伟以4亿欧元的价格收购了总 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付