| 牌号简介 About |
|---|
| PRE-ELEC® PC 1431是一种基于聚碳酸酯的导电热塑性化合物。导电性是通过使用特殊的导电炭黑来实现的。除了低电阻率。PRE-ELEC® PC 1431具有优良的机械性能，易于注射成型。典型应用包括需要良好冲击强度、较高刚性和很好的耐温性的技术部件。 PRE-ELEC® PC 1431 is a conductive thermoplastic compound based on polycarbonate. Conductivity is achieved by using special conductive carbon black. In addition to a low electrical resistivity. PRE-ELEC® PC 1431 has excellent mechanical properties and is easy to injection mould. Typical applications include technical parts requiring good impact strength, higher rigidity and very good temperature resistance. |
产品描述 Product Description
加工条件：注射成型 Injection Molding
性能特点： 热稳定性好; 机械强度好; 导电; 冲击性能好; 易加工; Good Rigidity,Excellent Processability,High impact resistance,Conductive,Heat Stabilized
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
1.25 | g/cm³ | ASTM D792 |
|
密度 Density |
1.24 | g/cm³ | ISO 1183 |
|
熔体质量流动速率 Melt Flow Rate |
ISO 1133 | ||
|
300℃，1.20kg 300℃，1.20kg |
4.0 | g/10min | ISO 1133 |
|
300℃，2.16kg 300℃，2.16kg |
10 | g/10min | ISO 1133 |
|
收缩率 Shrinkage rate |
|||
|
MD MD |
0.60 | % | ASTM D955 |
|
MD MD |
% | ISO 294-4 | |
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
邵氏硬度 Shore hardness |
|||
|
邵氏 D Shaw's D |
ISO 868 | ||
|
拉伸强度 tensile strength |
ASTM D638 | ||
|
TD TD |
MPa | ASTM D638 | |
|
MD MD |
MPa | ASTM D638 | |
|
拉伸强度 tensile strength |
ASTM D638 | ||
|
TD，屈服 TD, yield |
MPa | ASTM D638 | |
|
MD，屈服 MD, yield |
MPa | ASTM D638 | |
|
拉伸强度 tensile strength |
ISO 527-2 | ||
|
TD，屈服 TD, yield |
MPa | ISO 527-2 | |
|
MD，屈服 MD, yield |
MPa | ISO 527-2 | |
|
拉伸强度 tensile strength |
ISO 527-2 | ||
|
-- -- 2 |
MPa | ISO 527-2 | |
|
0.40 mm 0.40 mm 3 |
MPa | ISO 527-2 | |
|
拉伸应变 Tensile strain |
ISO 527-2 | ||
|
TD，屈服 TD, yield |
% | ISO 527-2 | |
|
流量，屈服 Flow rate, yield |
% | ISO 527-2 | |
|
拉伸应变 Tensile strain |
ISO 527-2 | ||
|
断裂，0.400 mm Fracture, 0.400 mm 4 |
% | ISO 527-2 | |
|
断裂，0.400 mm Fracture, 0.400 mm 3 |
% | ISO 527-2 | |
|
弯曲模量 Bending modulus |
|||
|
4 mm 4 mm |
MPa | ISO 178 | |
|
4 mm 4 mm |
MPa | ASTM D790 | |
|
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
简支梁缺口冲击强度 Charpy Notched Impact Strength 5 |
|||
|
-20℃ -20℃ |
kJ/m² | ASTM D256 | |
|
-20℃ -20℃ |
kJ/m² | ISO 179 | |
|
23℃ 23℃ |
kJ/m² | ISO 179 | |
|
23℃ 23℃ |
kJ/m² | ASTM D256 | |
|
简支梁无缺口冲击强度 Charpy Unnotch Impact strength 5 |
|||
|
-20℃ -20℃ |
ASTM D256 | ||
|
-20℃ -20℃ |
ISO 179 | ||
|
23℃ 23℃ |
ISO 179 | ||
|
23℃ 23℃ |
ASTM D256 | ||
|
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch 5 |
ISO 180 | ||
|
Area Area |
ASTM D256 | ||
|
-20℃，4.00 mm -20℃，4.00 mm |
kJ/m² | ASTM D256 | |
|
23℃，4.00 mm 23℃，4.00 mm |
kJ/m² | ASTM D256 | |
|
-20℃ -20℃ |
kJ/m² | ISO 180 | |
|
23℃ 23℃ |
kJ/m² | ISO 180 | |
|
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam |
ASTM D256 | ||
|
-20℃，4 mm -20℃，4 mm |
ASTM D256 | ||
|
23℃，4 mm 23℃，4 mm |
ASTM D256 | ||
|
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam 5 |
ISO 180 | ||
|
-20℃ -20℃ |
ISO 180 | ||
|
23℃ 23℃ |
ISO 180 | ||
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
热变形温度 Hot deformation temperature |
|||
|
1.8 MPa，未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/Af | |
|
1.8 MPa，未退火 1.8 MPa, unannealed |
℃ | ASTM D648-A | |
|
0.45 MPa，未退火 0.45 MPa, unannealed |
℃ | ASTM D648-B | |
|
0.45 MPa，未退火 0.45 MPa, unannealed |
℃ | ISO 75-2/Bf | |
|
维卡软化温度 Vicat Softening Temp |
|||
|
-- -- |
℃ | ASTM D1525 6 | |
|
-- -- |
℃ | ASTM D1525 7 | |
|
维卡软化温度 Vicat Softening Temp |
|||
|
A50 A50 |
℃ | ISO 306/A50 | |
|
B50 B50 |
℃ | ISO 306 | |
|
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
表面电阻率 Surface resistivity |
ohms | IEC 61340-2-3 | |
|
体积电阻率 Volume resistivity |
ohms·cm | 内部方法 | |
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
| 2 .4 mm Thickness, Across Flow |
| 3 Flow |
| 4 Across Flow |
| 5 4 mm thickness |
| 6 标准 B (120°C/h), 载荷2 (50N) |
| 7 速率 A (50°C/h), 载荷2 (50N) |
|
【新闻资讯】查看全部 
【锂电池需求增长】塞拉尼斯超高分子量聚乙烯装置扩产
2020-10-28 搜料网资讯： 全球知名的技术与特种材料公司塞拉尼斯宣布其美国德克萨斯州Bishop工厂将新增一条GUR超高分子量聚乙烯(UHMW-PE)生产线，以支持和满足其高价值GUR工程材料产品组合的巨大 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |