牌号简介 About |
---|
赢创生产一系列聚对苯二甲酸丁二醇酯化合物,这些化合物以注册商标Vestodur提供。表征维托化合物的材料性能为:高耐热性、高刚度、低吸水性,导致高尺寸稳定性、高硬度、高强度、良好的滑动摩擦性能、低磨损、良好的蠕变性能、良好的电气性能、良好的耐化学性、良好的耐候性、良好的加工性能、良好的机械性能、良好的机械性能、良好的机械性能、良好的机械性能、良好的机械性能、良好的机械性能、良好的机械o形成应力裂纹的倾向 Evonik manufactures a range of polybutylene terephthalate (PBT) compounds and supplies it under the registered trademark VESTODUR®. Material properties characterizing VESTODUR® compounds are: high thermostability high stiffness low water absorption resulting in high dimensional stability high hardness good strength good sliding friction behavior, low abrasion good creep behavior good electrical properties good chemical resistance good weathering resistance good processability no tendency to form stress cracks Applications VESTODUR® compounds can be used for a wide range of applications, for example, for thin-walled injection-molded parts in electrical engineering applications, for especially dimensionally stable components of high surface quality in the automotive industry, as a barrier layer in multilayer fuel lines, for laser-markable components, and in the cable industry. High-molecular extrudable VESTODUR® specialty products have come to occupy a leading position as materials for secondary fiber optic jacketing, because they fulfill the requirements perfectly. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.31 | g/cm³ | ISO 1183 |
收缩率 Shrinkage rate |
|||
MD色素可以改变模具收缩 MD pigment can change mold shrinkage |
1.6 | % | ISO 294-4 |
TD色素可以改变模具收缩 TD pigment can change mold shrinkage |
1.6 | % | ISO 294-4 |
吸水率 Water absorption rate |
|||
|
0.45 | % | ISO 62 |
熔体质量流动速率 Melt Flow Rate |
|||
250℃,2.16kg 250℃,2.16kg |
18.34 | g/10min | ISO 1133 |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ISO 75-2/Bf | |
1.8 MPa,退火 1.8 MPa, annealed |
℃ | ISO 75-2/Af | |
熔融温度 Melting temperature |
℃ | ISO 11357-3 | |
维卡软化温度 Vicat Softening Temp |
|||
B50 B50 |
℃ | ISO 306/A50 | |
A50 A50 |
℃ | ISO 306 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD MD |
1/℃ | ISO 11359-2 | |
TD TD |
1/℃ | ISO 11359-2 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
体积电阻 Volumetric resistance |
Ω.cm | IEC 60093 | |
表面电阻 Surface resistance |
Ω.cm | IEC 60093 | |
绝缘强度 Insulation strength |
|||
|
KV/mm | IEC 60243-1 | |
介电常数 Dielectric constant |
|||
|
1 MHz | IEC 60250 | |
|
100 Hz | IEC 60250 | |
耗散因数 Dissipation factor |
|||
|
IEC 60250 | ||
|
100 Hz | IEC 60250 | |
相比漏电起痕指数 Compared to the leakage tracing index |
V | IEC 60112 | |
相比漏电起痕指数 Compared to the leakage tracing index |
V | IEC 60112 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
|||
1.50mm 1.50mm |
UL-94 | ||
其他性能 Other performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
电解腐蚀 Electrolytic corrosion |
IEC 60426 | ||
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
|||
23℃ 23℃ |
kJ/m² | ISO 179/1eU | |
-30℃ -30℃ |
kJ/m² | ISO 179/1eU | |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
|||
23℃ 23℃ |
kJ/m² | ISO 179/1eA | |
-30℃ -30℃ |
kJ/m² | ISO 179/1eA | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 D Shaw's D |
ISO 868 | ||
球压硬度 Ball hardness |
MPa | ISO 2039-1 | |
拉伸强度 tensile strength |
|||
屈服,23℃ Yield, 23 ℃ |
MPa | ISO 527-2 | |
拉伸应变 Tensile strain |
|||
屈服,23℃ Yield, 23 ℃ |
% | ISO 527-2 | |
断裂,23℃ Fracture, 23 ℃ |
% | ISO 527-2 | |
拉伸模量 Tensile modulus |
|||
23℃ 23℃ |
MPa | ISO 527-2 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 H 30 |
3 K 20/P 50 |
4 100 Drops value |